An organo-montmorillonite-supported nanoscale zero-valent iron material （M-NZVI） was synthesized to degrade decabromodiphenyl ether （BDE-209）. The results showed that nanoscale zero-valent iron had good dispersion...An organo-montmorillonite-supported nanoscale zero-valent iron material （M-NZVI） was synthesized to degrade decabromodiphenyl ether （BDE-209）. The results showed that nanoscale zero-valent iron had good dispersion on organo-montmoriUonite and was present as a core-shell structure with a particle size range of nanoscale iron between 30-90 nm, characterized by XRD, SEM, TEM, XRF, ICP-AES, and XPS. The results of the degradation of BDE-209 by M-NZVI showed that the efficiency of M-NZVI in removing BDE-209 was much higher than that of NZVI. The efficiency of M-NZVI in removing BDE-209 decreased as the pH and the initial dissolved oxygen content of the reaction solution increased, but increased as the proportion of water in the reaction solution increased.展开更多
Three organo-montmorillonites were prepared using surfactants, and their adsorption behaviors toward sulfamethoxazole（SMX） were investigated. The surfactants used were cetyltrimethyl ammonium bromide（CTMAB）, 3-（N...Three organo-montmorillonites were prepared using surfactants, and their adsorption behaviors toward sulfamethoxazole（SMX） were investigated. The surfactants used were cetyltrimethyl ammonium bromide（CTMAB）, 3-（N,N-dimethylhexadecylammonio） propane sulfonate（HDAPS） and 1,3-bis（hexadecyldimethylammonio）-propane dibromide（BHDAP）. The properties of the organo-montmorillonites were characterized by X-ray diffraction, scanning electron microscopy and N2adsorption–desorption isotherm measurements. Results showed that the interlayer spacing of montmorillonite was increased and the surface area as well as the morphology were changed. Batch adsorption experiments showed that the surfactant loading amount had a great effect on the adsorption of SMX. The adsorption process was p H dependent and the maximum adsorption capacity was obtained at p H 3 for HDAPS-Mt, while CTMAB-Mt and BHDAP-Mt showed a high removal efficiency at 3–11. The adsorption capacity increased with the initial SMX concentration and contact time but decreased with increasing solution ionic strength.Kinetic data were best described by the pseudo second-order model. Equilibrium data were best represented by the Langmuir model, and the Freundlich constant（n） indicated a favorable adsorption process. The maximum adsorption capacity of SMX was 235.29 mg/g for CTMAB-Mt, 155.28 mg/g for HDAPS-Mt and 242.72 mg/g for BHDAP-Mt. Thermodynamic parameters were calculated to evaluate the spontaneity and endothermic or exothermic nature. The adsorption mechanism was found to be dominated by electrostatic interaction,while hydrophobic interaction played a secondary role.展开更多
基金supported by the National Science and Technology Major Projects of Water Pollution Control andManagement of China (No. 2012ZX07206002)
文摘An organo-montmorillonite-supported nanoscale zero-valent iron material （M-NZVI） was synthesized to degrade decabromodiphenyl ether （BDE-209）. The results showed that nanoscale zero-valent iron had good dispersion on organo-montmoriUonite and was present as a core-shell structure with a particle size range of nanoscale iron between 30-90 nm, characterized by XRD, SEM, TEM, XRF, ICP-AES, and XPS. The results of the degradation of BDE-209 by M-NZVI showed that the efficiency of M-NZVI in removing BDE-209 was much higher than that of NZVI. The efficiency of M-NZVI in removing BDE-209 decreased as the pH and the initial dissolved oxygen content of the reaction solution increased, but increased as the proportion of water in the reaction solution increased.
文摘Three organo-montmorillonites were prepared using surfactants, and their adsorption behaviors toward sulfamethoxazole（SMX） were investigated. The surfactants used were cetyltrimethyl ammonium bromide（CTMAB）, 3-（N,N-dimethylhexadecylammonio） propane sulfonate（HDAPS） and 1,3-bis（hexadecyldimethylammonio）-propane dibromide（BHDAP）. The properties of the organo-montmorillonites were characterized by X-ray diffraction, scanning electron microscopy and N2adsorption–desorption isotherm measurements. Results showed that the interlayer spacing of montmorillonite was increased and the surface area as well as the morphology were changed. Batch adsorption experiments showed that the surfactant loading amount had a great effect on the adsorption of SMX. The adsorption process was p H dependent and the maximum adsorption capacity was obtained at p H 3 for HDAPS-Mt, while CTMAB-Mt and BHDAP-Mt showed a high removal efficiency at 3–11. The adsorption capacity increased with the initial SMX concentration and contact time but decreased with increasing solution ionic strength.Kinetic data were best described by the pseudo second-order model. Equilibrium data were best represented by the Langmuir model, and the Freundlich constant（n） indicated a favorable adsorption process. The maximum adsorption capacity of SMX was 235.29 mg/g for CTMAB-Mt, 155.28 mg/g for HDAPS-Mt and 242.72 mg/g for BHDAP-Mt. Thermodynamic parameters were calculated to evaluate the spontaneity and endothermic or exothermic nature. The adsorption mechanism was found to be dominated by electrostatic interaction,while hydrophobic interaction played a secondary role.