A high performance Ni-Al-Mo-B system cast Ni_3Al base alloy, named Alloy IC6, has been developed for advanced gas turbine blades and vanes. The alloy has high strength and ductility from room temperature to 1100℃ as...A high performance Ni-Al-Mo-B system cast Ni_3Al base alloy, named Alloy IC6, has been developed for advanced gas turbine blades and vanes. The alloy has high strength and ductility from room temperature to 1100℃ as well as excellent creep resistance over a wide temperature range of 760℃ to 1100℃ . The superior mechanical properties of this alloy.may be attributed to (1) solid solution hardening by the large amount of Mo addition , (2)second phase strengthening by γ-phase and other minor phases that precipitate in various temperature ranges, (3) rearrangement of γ-phase in the form of raft structure during creep deformation , (4) high-density misfit dislocation networks at the γ /γ' interfaces that form due to a high value ofγ /γ ' misfit .展开更多
The oridation resistance at 1100°C of a dirationally solidified Ni3Al base alloy IC6is substantially improved by the addition of yttriurn or yttrium and silicon. The stress rupture property under 1100°C/80MP...The oridation resistance at 1100°C of a dirationally solidified Ni3Al base alloy IC6is substantially improved by the addition of yttriurn or yttrium and silicon. The stress rupture property under 1100°C/80MPa is increased by adding proper amounts of yttrium, howevef it decreases bg adding 0.3wt% silicon and 0. 1wt% yttrium at the same time, which may be attributed to the formation of a needle like phase rich in nickel and molybdenum.展开更多
The effect of recycle proportion on the composition,microstructure and mechanical prop- erites of recycled Ni_3Al basealloy IC6 was examined by scanning electron microscopy with X-ray en-ergy-dispersive spectrometer (...The effect of recycle proportion on the composition,microstructure and mechanical prop- erites of recycled Ni_3Al basealloy IC6 was examined by scanning electron microscopy with X-ray en-ergy-dispersive spectrometer (SEM/ES) and transmission electronmicroscopy (TEM). The results indicate that the addition of recycledscraps has no obvious effect on the chemical composition, except thecontent of C and N increases with the addition proportion of recycledscraps. The microstructure of IC6 recycled alloys has no obviousdifference compared with the fresh alloy, except some M_6C car- bidesprecipitate in the interdendritic area.展开更多
The HAZ cracking test in EB welding condition and hot ductility test show that the cracking mechanism is the formation of Ni - Ni5Zr eutectic which is resulting from the enrichment of Zr in grain boundaries during ...The HAZ cracking test in EB welding condition and hot ductility test show that the cracking mechanism is the formation of Ni - Ni5Zr eutectic which is resulting from the enrichment of Zr in grain boundaries during welding.In order to eliminate HAZ cracks the diffusion and recrystalization anealing treatment after cast and during cold rolling should be conducted in vacuum or protecting atmosphere and at the same time a slow welding speed is necessary.展开更多
文摘A high performance Ni-Al-Mo-B system cast Ni_3Al base alloy, named Alloy IC6, has been developed for advanced gas turbine blades and vanes. The alloy has high strength and ductility from room temperature to 1100℃ as well as excellent creep resistance over a wide temperature range of 760℃ to 1100℃ . The superior mechanical properties of this alloy.may be attributed to (1) solid solution hardening by the large amount of Mo addition , (2)second phase strengthening by γ-phase and other minor phases that precipitate in various temperature ranges, (3) rearrangement of γ-phase in the form of raft structure during creep deformation , (4) high-density misfit dislocation networks at the γ /γ' interfaces that form due to a high value ofγ /γ ' misfit .
文摘The oridation resistance at 1100°C of a dirationally solidified Ni3Al base alloy IC6is substantially improved by the addition of yttriurn or yttrium and silicon. The stress rupture property under 1100°C/80MPa is increased by adding proper amounts of yttrium, howevef it decreases bg adding 0.3wt% silicon and 0. 1wt% yttrium at the same time, which may be attributed to the formation of a needle like phase rich in nickel and molybdenum.
文摘The effect of recycle proportion on the composition,microstructure and mechanical prop- erites of recycled Ni_3Al basealloy IC6 was examined by scanning electron microscopy with X-ray en-ergy-dispersive spectrometer (SEM/ES) and transmission electronmicroscopy (TEM). The results indicate that the addition of recycledscraps has no obvious effect on the chemical composition, except thecontent of C and N increases with the addition proportion of recycledscraps. The microstructure of IC6 recycled alloys has no obviousdifference compared with the fresh alloy, except some M_6C car- bidesprecipitate in the interdendritic area.
文摘The HAZ cracking test in EB welding condition and hot ductility test show that the cracking mechanism is the formation of Ni - Ni5Zr eutectic which is resulting from the enrichment of Zr in grain boundaries during welding.In order to eliminate HAZ cracks the diffusion and recrystalization anealing treatment after cast and during cold rolling should be conducted in vacuum or protecting atmosphere and at the same time a slow welding speed is necessary.