目的针对装备向高温高速发展的需求,开展NiCr-Cr3C2、CoMoCr及NiCr Al Y涂层的高温摩擦磨损性能对比研究。方法针对上述三种涂层,通过超级爆炸喷涂工艺进行涂层制备,并测试涂层孔隙率、显微硬度、结合强度等基本性能,开展650℃/260 h的...目的针对装备向高温高速发展的需求,开展NiCr-Cr3C2、CoMoCr及NiCr Al Y涂层的高温摩擦磨损性能对比研究。方法针对上述三种涂层,通过超级爆炸喷涂工艺进行涂层制备,并测试涂层孔隙率、显微硬度、结合强度等基本性能,开展650℃/260 h的抗氧化试验和400、650℃的销盘式摩擦磨损试验,对比涂层的各项性能和在高温条件下的氧化质量增量、摩擦系数、磨损质量损失。结果抗氧化试验后,NiCr-Cr3C2、CoMoCrSi及NiCrAlY涂层氧化增重0.18、0.1、0.005 mg/(cm^2·h)。650℃时,摩擦系数分别为0.5、1.0、0.6。结论超级爆炸喷涂工艺制备的涂层组织、结合强度均优于等离子喷涂等常规喷涂工艺。高温下的氧化产物Co3O4与Cr2O3对高温摩擦系数有不同的影响。NiCr-75Cr3C2和NiCrAlY涂层在400、650℃可作为与SG37A材料的对磨副材料。展开更多
The objective of the present work was to determine the influence of the neutral salt spray corrosion on the wear resistance of HVOF sprayed NiCr-Cr3C2 coating with intermediate layer. Ni-Zn-Al2O3 coatings as interlaye...The objective of the present work was to determine the influence of the neutral salt spray corrosion on the wear resistance of HVOF sprayed NiCr-Cr3C2 coating with intermediate layer. Ni-Zn-Al2O3 coatings as interlayers were prepared by low pressure cold spray（LPCS） between NiCr-Cr3C2 cermet coatings to form a sandwich structure to enhance the corrosion resistance properties. The tribological properties were examined using the UMT-3 fricition and wear tester by line-contact reciprocating sliding under dry and salt spray one week corrosion. The morphology, element distribution, and phase compositions of the coating and worn sufaces were analyzed by using scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction respectively. The corrosion behavior of the coating was studied by the open-circuit potential, the electrochemical impedance spectroscopy, potentiodynamic polarization, and salt spray corrosion methods. It is found that the sandwich structured coating has better corrosion resistance than the single layer coating. The results show that under dry wear conditions, the wear mechanism is abrasive and adhesive wear, whereas under salt spray corrosion conditions it becomes corrosion wear. The friction coefficient of the sandwich structured coating after salt spray corrosion is slightly lower than the dry friction coefficient, but the weight of the wear loss is lower than that under dry condition.展开更多
文摘目的针对装备向高温高速发展的需求,开展NiCr-Cr3C2、CoMoCr及NiCr Al Y涂层的高温摩擦磨损性能对比研究。方法针对上述三种涂层,通过超级爆炸喷涂工艺进行涂层制备,并测试涂层孔隙率、显微硬度、结合强度等基本性能,开展650℃/260 h的抗氧化试验和400、650℃的销盘式摩擦磨损试验,对比涂层的各项性能和在高温条件下的氧化质量增量、摩擦系数、磨损质量损失。结果抗氧化试验后,NiCr-Cr3C2、CoMoCrSi及NiCrAlY涂层氧化增重0.18、0.1、0.005 mg/(cm^2·h)。650℃时,摩擦系数分别为0.5、1.0、0.6。结论超级爆炸喷涂工艺制备的涂层组织、结合强度均优于等离子喷涂等常规喷涂工艺。高温下的氧化产物Co3O4与Cr2O3对高温摩擦系数有不同的影响。NiCr-75Cr3C2和NiCrAlY涂层在400、650℃可作为与SG37A材料的对磨副材料。
基金Funded by the High-Tech Research and Development Program of China(No.2012AA09A203)the Fundmental Research Funds for the Central Universities(No.15CX06061A)the Postgraduate Innovation Project of China University of Petroleum(East China)(No.YCXJ2016059)
文摘The objective of the present work was to determine the influence of the neutral salt spray corrosion on the wear resistance of HVOF sprayed NiCr-Cr3C2 coating with intermediate layer. Ni-Zn-Al2O3 coatings as interlayers were prepared by low pressure cold spray（LPCS） between NiCr-Cr3C2 cermet coatings to form a sandwich structure to enhance the corrosion resistance properties. The tribological properties were examined using the UMT-3 fricition and wear tester by line-contact reciprocating sliding under dry and salt spray one week corrosion. The morphology, element distribution, and phase compositions of the coating and worn sufaces were analyzed by using scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction respectively. The corrosion behavior of the coating was studied by the open-circuit potential, the electrochemical impedance spectroscopy, potentiodynamic polarization, and salt spray corrosion methods. It is found that the sandwich structured coating has better corrosion resistance than the single layer coating. The results show that under dry wear conditions, the wear mechanism is abrasive and adhesive wear, whereas under salt spray corrosion conditions it becomes corrosion wear. The friction coefficient of the sandwich structured coating after salt spray corrosion is slightly lower than the dry friction coefficient, but the weight of the wear loss is lower than that under dry condition.