Morphology controlled synthesis of nanoparticles of powerful high energetic compounds(HECs) such as l,3,5-trinitro-l,3,5-triazinane(RDX) and 1,3,5,7-tetranitro-l,3,5,7-tetrazocane(HMX) were achieved by a simple solven...Morphology controlled synthesis of nanoparticles of powerful high energetic compounds(HECs) such as l,3,5-trinitro-l,3,5-triazinane(RDX) and 1,3,5,7-tetranitro-l,3,5,7-tetrazocane(HMX) were achieved by a simple solvent—antisolvent interaction(SAI) method at 70 ℃.The effects of different solvents on particle size and morphology of the prepared nano-HECs were studied systematically.Particle size and morphology of the nano-HECs was characterized using field emission scanning electron microscopy(FE-SEM) imaging.X-ray diffraction(XRD) and Fourier transform infrared(FTIR) spectroscopy studies revealed that RDX and HMX were precipitated in their most stable polymorphic forms,i.e.a and P,respectively.Thermogravimetric analysis coupled with differential scanning calorimetry(TGA-DSC) studies showed that the thermal response of the nanoparticles was similar to the respective raw-HECs.HEC nanoparticles with spherical and rod shaped morphology were observed under different solvent conditions.The mean particle size also varied considerably with the use of different solvents.展开更多
Nano hexahydro-1,3,5-trinitro-1,3,5-triazine(RDX) was prepared using a bi-directional rotation mill and dried under different conditions(liquid, temperature and drying). It shows that the samples cake seriously and th...Nano hexahydro-1,3,5-trinitro-1,3,5-triazine(RDX) was prepared using a bi-directional rotation mill and dried under different conditions(liquid, temperature and drying). It shows that the samples cake seriously and the particles grow up obviously by ordinary drying in different liquids at 70 C, which occurs again after vacuum drying. With the increase of temperature, the degrees of caking and aggregation are enhanced.Well dispersed sample maintaining constant particle size is extracted by supercritical drying, especially freeze drying. Furthermore, the mechanical sensitivities of I-RDX, O-RDX and F-RDX, of which the average sizes are 88.03 mm, 15.32 mm and 0.16 mm, respectively, are evaluated. Compared with I-RDX, the friction, impact and shock sensitivities of O-RDX are slightly lower. However, the friction, impact and shock sensitivities of F-RDX are reduced by 30%, 99.0% and 59.9%, respectively.展开更多
基金Financial assistance from ARMREB(DRDO) under grant No.ARMREB/CDSW/2012/149
文摘Morphology controlled synthesis of nanoparticles of powerful high energetic compounds(HECs) such as l,3,5-trinitro-l,3,5-triazinane(RDX) and 1,3,5,7-tetranitro-l,3,5,7-tetrazocane(HMX) were achieved by a simple solvent—antisolvent interaction(SAI) method at 70 ℃.The effects of different solvents on particle size and morphology of the prepared nano-HECs were studied systematically.Particle size and morphology of the nano-HECs was characterized using field emission scanning electron microscopy(FE-SEM) imaging.X-ray diffraction(XRD) and Fourier transform infrared(FTIR) spectroscopy studies revealed that RDX and HMX were precipitated in their most stable polymorphic forms,i.e.a and P,respectively.Thermogravimetric analysis coupled with differential scanning calorimetry(TGA-DSC) studies showed that the thermal response of the nanoparticles was similar to the respective raw-HECs.HEC nanoparticles with spherical and rod shaped morphology were observed under different solvent conditions.The mean particle size also varied considerably with the use of different solvents.
文摘Nano hexahydro-1,3,5-trinitro-1,3,5-triazine(RDX) was prepared using a bi-directional rotation mill and dried under different conditions(liquid, temperature and drying). It shows that the samples cake seriously and the particles grow up obviously by ordinary drying in different liquids at 70 C, which occurs again after vacuum drying. With the increase of temperature, the degrees of caking and aggregation are enhanced.Well dispersed sample maintaining constant particle size is extracted by supercritical drying, especially freeze drying. Furthermore, the mechanical sensitivities of I-RDX, O-RDX and F-RDX, of which the average sizes are 88.03 mm, 15.32 mm and 0.16 mm, respectively, are evaluated. Compared with I-RDX, the friction, impact and shock sensitivities of O-RDX are slightly lower. However, the friction, impact and shock sensitivities of F-RDX are reduced by 30%, 99.0% and 59.9%, respectively.