Mechanical activation and liquid phase sintering were used to manufacture high performance Mo-Cu alloy and develop new processes. The microstructures and properties of the alloy were investigated. The experimental res...Mechanical activation and liquid phase sintering were used to manufacture high performance Mo-Cu alloy and develop new processes. The microstructures and properties of the alloy were investigated. The experimental results showed that: (1) the ball milled Mo/Cu powder has lamellar structure, (2) the microstructures of the sintered Mo-Cu alloy were homogenous compound structures of adhesive phase Cu linking Mo grains, (3) Mo grains frequently strung or gathered in Cu phase, and (4) the full densities of Mo-Cu alloy was achieved through sintering and special densification process. As a result, the properties of the alloy are good enough to satisfy various requirements.展开更多
Mo-Cu composites were fabricated by powder metallurgy with addition of various Ni contents.The effect of Ni contents on mechanical and thermal properties of Mo-Cu composites was investigated.The results show that mech...Mo-Cu composites were fabricated by powder metallurgy with addition of various Ni contents.The effect of Ni contents on mechanical and thermal properties of Mo-Cu composites was investigated.The results show that mechanical and thermal properties of Mo-Cu composites are greatly affected by the addition of Ni contents.The composite powders with Ni addition exhibits high sinterability.The sintering temperature is greatly decreased and the comprehensive properties of Mo-Cu composites are obviously improved.Mo-Cu composites with a content of 1.5 wt.% Ni have relative density 99.2%,bending strength 1057.9 MPa,hardness 72.5 HRA,electronic resistivity 1.28×10^(-7)Ω·m^(-1),thermal conductivity 139 W.m^(-1).K^(-1),and lower coefficient of thermal expansion 7.4×10^(-6)K^(-1).Mo-Cu composites have homogeneous and fine microstructure.The fracture mechanism is ductile fracture.展开更多
文摘Mechanical activation and liquid phase sintering were used to manufacture high performance Mo-Cu alloy and develop new processes. The microstructures and properties of the alloy were investigated. The experimental results showed that: (1) the ball milled Mo/Cu powder has lamellar structure, (2) the microstructures of the sintered Mo-Cu alloy were homogenous compound structures of adhesive phase Cu linking Mo grains, (3) Mo grains frequently strung or gathered in Cu phase, and (4) the full densities of Mo-Cu alloy was achieved through sintering and special densification process. As a result, the properties of the alloy are good enough to satisfy various requirements.
基金supported by the Program of the Department of Education of Hunan Province,China (No.08C331)
文摘Mo-Cu composites were fabricated by powder metallurgy with addition of various Ni contents.The effect of Ni contents on mechanical and thermal properties of Mo-Cu composites was investigated.The results show that mechanical and thermal properties of Mo-Cu composites are greatly affected by the addition of Ni contents.The composite powders with Ni addition exhibits high sinterability.The sintering temperature is greatly decreased and the comprehensive properties of Mo-Cu composites are obviously improved.Mo-Cu composites with a content of 1.5 wt.% Ni have relative density 99.2%,bending strength 1057.9 MPa,hardness 72.5 HRA,electronic resistivity 1.28×10^(-7)Ω·m^(-1),thermal conductivity 139 W.m^(-1).K^(-1),and lower coefficient of thermal expansion 7.4×10^(-6)K^(-1).Mo-Cu composites have homogeneous and fine microstructure.The fracture mechanism is ductile fracture.