The performance of Mn-W/TiO2 for selective catalytic reduction（SCR） of NOx with NH3 and its resistance to different concentrations of SO2 at various temperatures were investigated. The results show that WO3 increase...The performance of Mn-W/TiO2 for selective catalytic reduction（SCR） of NOx with NH3 and its resistance to different concentrations of SO2 at various temperatures were investigated. The results show that WO3 increased the active sites and enhanced the strength of acid, so it was an effective promoter of MnOJTiO2. The NOx conversion on Mn-W/TiO2 ranges from 80.3% to 99.6% between 100 ℃to 350℃ at GHSV=18900 h 1, while N2 product selectivity changes from 100% to 98.7%. In the presence of 0.01% SO2 and 6% H20, NOx conversion maintained 98.5% at 120℃. The influence of more than 0.01% SO2 on the activity of MnOx-WO3/TiO2 will disappear if the temperature rises above 250℃. By means of heating and sweeping with He, the activity of the catalysts can be recovered. At 300℃, NOx conversion yielded 99% with 0.07% SO2 and reached the level of commercial V-W/TiO2 catalysts. The Mn-W/TiO2 catalyst showed excellent performance for SCR of NOx with NH3 in a wider range of temperature with strong tolerance to SO2.展开更多
The catalytic activities of MnOx-WO3/TiO2 for selective catalytic reduction（SCR） of NO with NH3 were investigated in a wide range of temperature and reaction condition.It yielded a NOx conversion of 80.3%—99.6% and...The catalytic activities of MnOx-WO3/TiO2 for selective catalytic reduction（SCR） of NO with NH3 were investigated in a wide range of temperature and reaction condition.It yielded a NOx conversion of 80.3%—99.6% and a N2 product selectivity of 100%—98.7% during 100 °C to 350 °C at gas hourly space velocity（GHSV）=18900 h-1.In the presence of 0.01% SO2 and 6% H2O at 120 °C,the NOx conversion can maintain 98.5%.At 300 °C and with 0.07% SO2 in reactant stream,the NOx conversion stabilized at 99% as high as the commercial V-W/TiO2 catalyst＇s level.The steady-state kinetics study shows that O2 played a promoting role.In the presence of less than 1.5% O2,NOx conversion can increase sharply with the increase of O2 concentration.The reaction order was zero with respect to NH3 and first with respect to NO with excess O2 and H2O.The kinetics active energy（Ea） of Mn-W/TiO2 was calculated to be 6.24 kJ/mol according to the kinetic experiment at various temperatures,much lower than those of other catalysts reported in the literature.Mn-W/TiO2 is an excellent catalyst for SCR of NO with NH3 by now.展开更多
文摘研究了Mn-W/TiO2用于NH3选择性催化还原NOx体系的催化反应性能,探索了不同温度条件下该催化剂对抗不同SO2浓度的抗毒性能。结果显示WO3能够增加活性酸中心的数量和酸性,是MnOx/TiO2非常有效的助催化剂。在气体体积空速(gaseous hourly space velocity,GHSV)为18900h-1时100～350℃范围内,Mn-W/TiO2催化剂还原NOx的转化率高达80.3%～99.6%,N2选择性达100%～98.7%。当反应气中有0.01%SO2和6%H2O时,120℃NOx转化率可维持在98.5%,当SO2浓度超过0.01%时,则需将反应温度升高到250℃以上才可消除其干扰,而当SO2浓度高达0.07%时,300℃下转化率可长期维持在99%,达到了商用V-W/TiO2催化剂的水平。对于NH3选择性还原NOx体系Mn-W/TiO2显示了极好的催化性能,是目前抗SO2毒性最强的催化剂之一。试验发现,低温条件下,SO2对Mn-W/TiO2催化剂的影响是可逆的,随着反应温度的提高,活性将自然恢复。
文摘The performance of Mn-W/TiO2 for selective catalytic reduction（SCR） of NOx with NH3 and its resistance to different concentrations of SO2 at various temperatures were investigated. The results show that WO3 increased the active sites and enhanced the strength of acid, so it was an effective promoter of MnOJTiO2. The NOx conversion on Mn-W/TiO2 ranges from 80.3% to 99.6% between 100 ℃to 350℃ at GHSV=18900 h 1, while N2 product selectivity changes from 100% to 98.7%. In the presence of 0.01% SO2 and 6% H20, NOx conversion maintained 98.5% at 120℃. The influence of more than 0.01% SO2 on the activity of MnOx-WO3/TiO2 will disappear if the temperature rises above 250℃. By means of heating and sweeping with He, the activity of the catalysts can be recovered. At 300℃, NOx conversion yielded 99% with 0.07% SO2 and reached the level of commercial V-W/TiO2 catalysts. The Mn-W/TiO2 catalyst showed excellent performance for SCR of NOx with NH3 in a wider range of temperature with strong tolerance to SO2.
文摘The catalytic activities of MnOx-WO3/TiO2 for selective catalytic reduction（SCR） of NO with NH3 were investigated in a wide range of temperature and reaction condition.It yielded a NOx conversion of 80.3%—99.6% and a N2 product selectivity of 100%—98.7% during 100 °C to 350 °C at gas hourly space velocity（GHSV）=18900 h-1.In the presence of 0.01% SO2 and 6% H2O at 120 °C,the NOx conversion can maintain 98.5%.At 300 °C and with 0.07% SO2 in reactant stream,the NOx conversion stabilized at 99% as high as the commercial V-W/TiO2 catalyst＇s level.The steady-state kinetics study shows that O2 played a promoting role.In the presence of less than 1.5% O2,NOx conversion can increase sharply with the increase of O2 concentration.The reaction order was zero with respect to NH3 and first with respect to NO with excess O2 and H2O.The kinetics active energy（Ea） of Mn-W/TiO2 was calculated to be 6.24 kJ/mol according to the kinetic experiment at various temperatures,much lower than those of other catalysts reported in the literature.Mn-W/TiO2 is an excellent catalyst for SCR of NO with NH3 by now.