In the present study, by adding SiC particles into AI-Si-Mg melt, Mg2Si and SiC particles hybrid reinforced AI matrix composites were fabricated through the Mg2Si in situ synthesis in melt combined with the SiC ex sit...In the present study, by adding SiC particles into AI-Si-Mg melt, Mg2Si and SiC particles hybrid reinforced AI matrix composites were fabricated through the Mg2Si in situ synthesis in melt combined with the SiC ex situ stir casting. The as-cast microstructure containing primary Mg2Si and SiC particles that distribute homogenously in AI matrix was successfully achieved. The effects of SiC particle addition on the microstructure of Mg2Si/AI composites were investigated by using scanning electron microscopy （SEM） and XRD. The results show that, with increasing the fraction of the SiC particles from 5wt.% to 10wt.%, the morphologies of the primary Mg2Si particulates in the prepared samples remain polygonal, but the size of the primary phase decreases slightly. However, when the SiC particle addition reaches 15wt.%, the morphologies of the primary Mg2Si particulates change partially from polygonal to quadrangular with a decrease in size from 50 pm to 30 μm. The size of primary AI dendrites decreases with increasing fraction of the SiC particles from 0wt.% to 15wt.%. The morphology of the eutectic Mg2Si phase changes from a fiber-form to a short fiber-form and/or a dot-like shape with increasing fraction of the SiC particles. Furthermore, no significant change in dendrite arm spacing （DAS） was observed in the presence of SiC particles.展开更多
The effect of Sb on the microstructure and mechanical properties of Mg2Si/Al-Si composites was investigated.The results show that Sb can improve the microstructure and mechanical properties of Mg2Si/Al-Si composites.W...The effect of Sb on the microstructure and mechanical properties of Mg2Si/Al-Si composites was investigated.The results show that Sb can improve the microstructure and mechanical properties of Mg2Si/Al-Si composites.When the content of Sb is 0.4%,the morphology of primary Mg2Si changes from dendrites to fine particles,the average size of Mg2Si particles is refined from 52 to 25μm,and the ultimate tensile strength and elongation of the composites increase from 102.1 MPa and 0.26% to 138.6 MPa and 0.36%,respectively.The strengthening mechanism can be attributed to the fine-grain strengthening.However,excessive Sb is disadvantageous to the modification of the composites.展开更多
基金supported by the National Natural Science Foundation of China(No.50671044)the Sci-tech Development Project of Jilin Province of China(No.20070506)
文摘In the present study, by adding SiC particles into AI-Si-Mg melt, Mg2Si and SiC particles hybrid reinforced AI matrix composites were fabricated through the Mg2Si in situ synthesis in melt combined with the SiC ex situ stir casting. The as-cast microstructure containing primary Mg2Si and SiC particles that distribute homogenously in AI matrix was successfully achieved. The effects of SiC particle addition on the microstructure of Mg2Si/AI composites were investigated by using scanning electron microscopy （SEM） and XRD. The results show that, with increasing the fraction of the SiC particles from 5wt.% to 10wt.%, the morphologies of the primary Mg2Si particulates in the prepared samples remain polygonal, but the size of the primary phase decreases slightly. However, when the SiC particle addition reaches 15wt.%, the morphologies of the primary Mg2Si particulates change partially from polygonal to quadrangular with a decrease in size from 50 pm to 30 μm. The size of primary AI dendrites decreases with increasing fraction of the SiC particles from 0wt.% to 15wt.%. The morphology of the eutectic Mg2Si phase changes from a fiber-form to a short fiber-form and/or a dot-like shape with increasing fraction of the SiC particles. Furthermore, no significant change in dendrite arm spacing （DAS） was observed in the presence of SiC particles.
文摘The effect of Sb on the microstructure and mechanical properties of Mg2Si/Al-Si composites was investigated.The results show that Sb can improve the microstructure and mechanical properties of Mg2Si/Al-Si composites.When the content of Sb is 0.4%,the morphology of primary Mg2Si changes from dendrites to fine particles,the average size of Mg2Si particles is refined from 52 to 25μm,and the ultimate tensile strength and elongation of the composites increase from 102.1 MPa and 0.26% to 138.6 MPa and 0.36%,respectively.The strengthening mechanism can be attributed to the fine-grain strengthening.However,excessive Sb is disadvantageous to the modification of the composites.
基金国家自然科学基金项目50671044吉林省科技发展计划项目20070506资助+1 种基金Supported by National Natural Science Foundation of China(No.50671044)Science and Technology Development Project of Jilin Province of China(No.20070506)