The regulation of ceramic coating formed by micro-arc oxidation on Mg-11Gd-1Y-0.5Zn (wt.%) magnesium alloys was investigated by scanning electron microscopy (SEM) and X-ray diffractometer (XRD). The relation of phase ...The regulation of ceramic coating formed by micro-arc oxidation on Mg-11Gd-1Y-0.5Zn (wt.%) magnesium alloys was investigated by scanning electron microscopy (SEM) and X-ray diffractometer (XRD). The relation of phase structure and corrosion resistance of MgO coating formed by micro-arc oxidation in different growth stages was analyzed. The results showed that the growth of coating accorded with linear regularity in the initial stage of micro-arc oxidation, which was the stage of anodic oxidation controlled ...展开更多
Microstructure and mechanical properties of Mg-15wt.%Gd-5 wt.%Y-0.5wt.% Zr alloy were investigated in a series of conditions. The eutectic was dissolved into the matrix and there was no evident grain growth after soln...Microstructure and mechanical properties of Mg-15wt.%Gd-5 wt.%Y-0.5wt.% Zr alloy were investigated in a series of conditions. The eutectic was dissolved into the matrix and there was no evident grain growth after solntionized at 525 ℃ for 12 h. The evolution of the phase constituents from as-cast to cast-T4 was as follows： α-Mg solid solution＋Mg5（Gd,Y） entectic compound→α-Mg solid solution＋ spheroidized Mg5（Gd, Y） phase→α-Mg supersaturated solid solution＋cuboid-shaped compound （Mg2Y3Gd2）. And the precipitation sequences of Mg-15Gd-5Y-0.5Zr alloy were observed, according to the hardness response to isothermal ageing at 225-300 ℃ for 0-128 h.展开更多
基金Project supported by the Natioanl Defence Major Safety Foundation of China (6133002B2008)
文摘The regulation of ceramic coating formed by micro-arc oxidation on Mg-11Gd-1Y-0.5Zn (wt.%) magnesium alloys was investigated by scanning electron microscopy (SEM) and X-ray diffractometer (XRD). The relation of phase structure and corrosion resistance of MgO coating formed by micro-arc oxidation in different growth stages was analyzed. The results showed that the growth of coating accorded with linear regularity in the initial stage of micro-arc oxidation, which was the stage of anodic oxidation controlled ...
基金the Major State Basic Research Development Program of China (973 Program, 5133001E)
文摘Microstructure and mechanical properties of Mg-15wt.%Gd-5 wt.%Y-0.5wt.% Zr alloy were investigated in a series of conditions. The eutectic was dissolved into the matrix and there was no evident grain growth after solntionized at 525 ℃ for 12 h. The evolution of the phase constituents from as-cast to cast-T4 was as follows： α-Mg solid solution＋Mg5（Gd,Y） entectic compound→α-Mg solid solution＋ spheroidized Mg5（Gd, Y） phase→α-Mg supersaturated solid solution＋cuboid-shaped compound （Mg2Y3Gd2）. And the precipitation sequences of Mg-15Gd-5Y-0.5Zr alloy were observed, according to the hardness response to isothermal ageing at 225-300 ℃ for 0-128 h.