AZ31 alloy sheet fabricated by rolling was processed by friction stir processing(FSP) with different passes. The effect of FSP on the microstructure and damping capacity of AZ31 alloy sheet was discussed. The fine and...AZ31 alloy sheet fabricated by rolling was processed by friction stir processing(FSP) with different passes. The effect of FSP on the microstructure and damping capacity of AZ31 alloy sheet was discussed. The fine and equiaxed grains were obtained in the stirred zone(SZ) for FSPed samples from 1 pass to 3 passes with the average grain size of 10.6, 10.4 and 13.6 μm, respectively. The damping peak P_1 was presented on the curves of temperature-dependent damping capacity for FSPed samples. The damping peak P_2 was restrained after FSP and the damping peak P_1 was a relaxation process. The FSPed samples(2-pass FSP and 3-pass FSP) obtained high damping capacity. The best damping valuesQ_0^(-1)(ε=10_(-4)) and damping values Q_H^(-1)(ε=10^(-3)) of the sample subjected to 3-pass FSP(0.0131 and 0.0496) increased by 33.7% and 157.0%, respectively.展开更多
基金Project(51301077)supported by the National Natural Science Foundation,ChinaProject(BK20130470)supported by the Natural Science Foundation of Jiangsu Province,ChinaProject supported by Priority Academic Program Development of Jiangsu Higher Education Institutions,China
文摘AZ31 alloy sheet fabricated by rolling was processed by friction stir processing(FSP) with different passes. The effect of FSP on the microstructure and damping capacity of AZ31 alloy sheet was discussed. The fine and equiaxed grains were obtained in the stirred zone(SZ) for FSPed samples from 1 pass to 3 passes with the average grain size of 10.6, 10.4 and 13.6 μm, respectively. The damping peak P_1 was presented on the curves of temperature-dependent damping capacity for FSPed samples. The damping peak P_2 was restrained after FSP and the damping peak P_1 was a relaxation process. The FSPed samples(2-pass FSP and 3-pass FSP) obtained high damping capacity. The best damping valuesQ_0^(-1)(ε=10_(-4)) and damping values Q_H^(-1)(ε=10^(-3)) of the sample subjected to 3-pass FSP(0.0131 and 0.0496) increased by 33.7% and 157.0%, respectively.