The microstructure of Mg-8Zn-1Y alloy solidified under super-high pressure was analyzed through X-ray diffraction（XRD）, scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS）. And, compression...The microstructure of Mg-8Zn-1Y alloy solidified under super-high pressure was analyzed through X-ray diffraction（XRD）, scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS）. And, compression deformation behavior at room-temperature was studied. The results showed that the microstructure of Mg-8Zn-1Y alloy solidified under ambient pressure and super-high pressure was both mainly composed of ■-Mg and quasicrystal I-Mg3Zn6 Y. Solidification under super-high pressure contributed to refining solidified microstructure and changing morphology of the intergranular second phase. The morphology of intergranular second phase（quasicrystal I-Mg3Zn6Y） was transformed from continuous network（ambient pressure） to long island（high pressure） and finally to granular（super-high pressure） with the increase in pressure. The compressive strength, yield strength and rupture strain of the samples solidified under ambient pressure were significantly improved from 262.6 MPa, 244.4 MPa and 13.3% to 437.3 MPa, 368.9 MPa and 24.7% under the pressure of 6 GPa, respectively. Under ambient pressure, cleavage plane on compressive fracture was large and smooth. When it was solidified under the pressure ranging from 4 to 6 GPa, cleavage plane on compressive fracture was small and coarse. In addition, dimple, tear ridge and lobate patterns existed.展开更多
The effect of ultrasonic power and treatment time on degassing of Mg-6Zn-1Ca alloy was studied in this paper. The degassing effect was characterized by measuring densities of ingots. The results show that proper ultra...The effect of ultrasonic power and treatment time on degassing of Mg-6Zn-1Ca alloy was studied in this paper. The degassing effect was characterized by measuring densities of ingots. The results show that proper ultrasonic treatment can remove hydrogen from the melt of the Mg-6Zn-1Ca alloy. The ultrasonic degassing effect is closely related to the ultrasonic power density and treatment time. The degassing efficiency increases with an increase in ultrasonic power density when the melt is treated at 690 °C for 120 s, reaching its highest value at 1.2 W·cm-3. When the power density is 1.2 W·cm-3, with an increase in ultrasonic treatment time, the degassing efficiency increases at first, reaches its peak value at 120 s, then decreases as the ultrasonic treatment is further prolonged. In this experiment, the optimum degassing effect with an efficiency of 67.5 % is obtained by ultrasonic treatment with the power density of 1.2 W·cm-3 for 120 s. The maximum density of ingot can be increased from 1.8069 g·cm-3 to 1.8146 g·cm-3(increased by 0.43%).展开更多
In order to investigate the effect of extrusion on Mg-4Zn-1Y alloy, microstructure and mechanical properties were analyzed by optical microscopy（OM）, scanning electron microscopy（SEM）, transmission electron micros...In order to investigate the effect of extrusion on Mg-4Zn-1Y alloy, microstructure and mechanical properties were analyzed by optical microscopy（OM）, scanning electron microscopy（SEM）, transmission electron microscopy（TEM）, X-ray diffraction（XRD）, energy dispersive spectrum（EDS） and tensile testing.The results indicated that the microstructure was obviously refined by extrusion and dynamic recrystallization.The second phases were dynamic precipitated and distributed more dispersively through extrusion.W-Phases（Mg3Zn3Y2） were twisted and broken, while I-Phases（Mg3Zn6Y） were spheroidized by deformation.Twin bands were formed to achieve the large deformation and hinder the slip of dislocations effectively to improve tensile properties.The tensile strength and elongation of extruded Mg-4Zn-1Y alloy were 254.94 MPa and 17.9% respectively which were improved greatly compared with those of as-cast alloy.The strengthening mechanisms of the extruded alloy were mainly fine-grain strengthening and distortion strengthening.展开更多
基金Project supported by National Natural Science Foundation of China(51475486)Natural Science Foundation of Hebei Province(E2013501096)
文摘The microstructure of Mg-8Zn-1Y alloy solidified under super-high pressure was analyzed through X-ray diffraction（XRD）, scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS）. And, compression deformation behavior at room-temperature was studied. The results showed that the microstructure of Mg-8Zn-1Y alloy solidified under ambient pressure and super-high pressure was both mainly composed of ■-Mg and quasicrystal I-Mg3Zn6 Y. Solidification under super-high pressure contributed to refining solidified microstructure and changing morphology of the intergranular second phase. The morphology of intergranular second phase（quasicrystal I-Mg3Zn6Y） was transformed from continuous network（ambient pressure） to long island（high pressure） and finally to granular（super-high pressure） with the increase in pressure. The compressive strength, yield strength and rupture strain of the samples solidified under ambient pressure were significantly improved from 262.6 MPa, 244.4 MPa and 13.3% to 437.3 MPa, 368.9 MPa and 24.7% under the pressure of 6 GPa, respectively. Under ambient pressure, cleavage plane on compressive fracture was large and smooth. When it was solidified under the pressure ranging from 4 to 6 GPa, cleavage plane on compressive fracture was small and coarse. In addition, dimple, tear ridge and lobate patterns existed.
基金supported by the Major State Basic Research Development Program of China(2013CB632203)the National Key Technology R&D Program of China(2012BAF09B01)+2 种基金the Liaoning Provincial Natural Science Foundation(Grant No.201202072)the Program for Liaoning Excellent Talents in University(Grant No.LJQ2012023)the Fundamental Research Foundation of Central Universities(N120509002 and N120309003)
文摘The effect of ultrasonic power and treatment time on degassing of Mg-6Zn-1Ca alloy was studied in this paper. The degassing effect was characterized by measuring densities of ingots. The results show that proper ultrasonic treatment can remove hydrogen from the melt of the Mg-6Zn-1Ca alloy. The ultrasonic degassing effect is closely related to the ultrasonic power density and treatment time. The degassing efficiency increases with an increase in ultrasonic power density when the melt is treated at 690 °C for 120 s, reaching its highest value at 1.2 W·cm-3. When the power density is 1.2 W·cm-3, with an increase in ultrasonic treatment time, the degassing efficiency increases at first, reaches its peak value at 120 s, then decreases as the ultrasonic treatment is further prolonged. In this experiment, the optimum degassing effect with an efficiency of 67.5 % is obtained by ultrasonic treatment with the power density of 1.2 W·cm-3 for 120 s. The maximum density of ingot can be increased from 1.8069 g·cm-3 to 1.8146 g·cm-3(increased by 0.43%).
基金Project supported by General Program of Liaoning Province Committee of Education(L2012035)Liaoning Province Science and Technology Plan(2013201018)Liaoning Province University Innovation Team Support Plan
文摘In order to investigate the effect of extrusion on Mg-4Zn-1Y alloy, microstructure and mechanical properties were analyzed by optical microscopy（OM）, scanning electron microscopy（SEM）, transmission electron microscopy（TEM）, X-ray diffraction（XRD）, energy dispersive spectrum（EDS） and tensile testing.The results indicated that the microstructure was obviously refined by extrusion and dynamic recrystallization.The second phases were dynamic precipitated and distributed more dispersively through extrusion.W-Phases（Mg3Zn3Y2） were twisted and broken, while I-Phases（Mg3Zn6Y） were spheroidized by deformation.Twin bands were formed to achieve the large deformation and hinder the slip of dislocations effectively to improve tensile properties.The tensile strength and elongation of extruded Mg-4Zn-1Y alloy were 254.94 MPa and 17.9% respectively which were improved greatly compared with those of as-cast alloy.The strengthening mechanisms of the extruded alloy were mainly fine-grain strengthening and distortion strengthening.
基金supported by Chongqing Talent Plan:Leading Talents in Innovation and Entrepreneurship,China(No.CQYC201903051)University Innovation Research Group of Chongqing,China(No.CXQT20023)+4 种基金Qingnian Project of Science and Technology Research Program of Chongqing Municipal Education Commission,China(No.KJQN202001106)China Postdoctoral Science Foundation(No.2021M700556)Natural Science Foundation of Chongqing,China(No.cstc2021jcyj-bsh X0114)Natural Science Foundation of China(Nos.U20A20234,51874062)Chongqing Foundation and Advanced Research Project,China(No.cstc2019jcyj-zdxm X0010)。