A new approach of ball-milled Mg_2Ni in tetrahydrofuran (THF) to improve thehydriding kinetics of Mg_2Ni alloy is suggested and studied. It is found that the modified alloydisplayed the improved activity for hydriding...A new approach of ball-milled Mg_2Ni in tetrahydrofuran (THF) to improve thehydriding kinetics of Mg_2Ni alloy is suggested and studied. It is found that the modified alloydisplayed the improved activity for hydriding even at relatively low temperature (e.g., 323-373 K).In the case of the sample milled in THF for 20 h, the hydrogen content (mass fraction) reaches 1.6 %at 323 K, 2.1% at 348 K and 3.4% at 448 K, respectively. The use of THF during grinding led to thechange of the structure, which is reflected by the broadening and weakening of the diffraction peaksin the XRD spectra. The XPS analysis shows that Mg (2s) binding energy peak of Mg_2Ni aftermodification shifted from a lower binding energy to a higher one, indicating the charge transferencebetween Mg and THF and the formation of catalytically active electron donor-acceptor (EDA)complexes on the surface of modified Mg_2Ni alloy.展开更多
The nanocrystalline and amorphous Mg2Ni-type Mg2Ni1-xCox （x = 0, 0.1, 0.2, 0.3, 0.4） alloys were synthesized by melt quenching technology. The structures of the as-cast and quenched alloys were characterized by XRD,...The nanocrystalline and amorphous Mg2Ni-type Mg2Ni1-xCox （x = 0, 0.1, 0.2, 0.3, 0.4） alloys were synthesized by melt quenching technology. The structures of the as-cast and quenched alloys were characterized by XRD, SEM and HRTEM. The gaseous hydrogen storage kinetics of the alloys was measured using an automatically controlled Sieverts apparatus. The alloy electrodes were charged and discharged with a constant current density in order to investigate the electrochemical hydrogen storage kinetics of the alloys. The results demonstrate that the substitution of Co for Ni results in the formation of secondary phases MgCo2 and Mg instead of altering the major phase Mg2Ni. No amorphous phase is detected in the as-quenched Co- ffee alloy, however, a certain amount of amorphous phase is clearly found in the as-quenched alloys substituted by Co. Furthermore, both the rapid quenching and the Co substitution significantly improve the gaseous and electrochemical hydrogen storage kinetics of the alloys, for which the notable increase of the hydrogen diffusion coefficient （D） along with the limiting current density （IL） and the obvious decline of the electrochemical impedance generated by both the Co substitution and the rapid quenching are basically responsible.展开更多
基金This work is supported by the State Key Project for Fundamental Research (TG2000026406) and the National Natural Science Foundation of China (No. 50071053).
文摘A new approach of ball-milled Mg_2Ni in tetrahydrofuran (THF) to improve thehydriding kinetics of Mg_2Ni alloy is suggested and studied. It is found that the modified alloydisplayed the improved activity for hydriding even at relatively low temperature (e.g., 323-373 K).In the case of the sample milled in THF for 20 h, the hydrogen content (mass fraction) reaches 1.6 %at 323 K, 2.1% at 348 K and 3.4% at 448 K, respectively. The use of THF during grinding led to thechange of the structure, which is reflected by the broadening and weakening of the diffraction peaksin the XRD spectra. The XPS analysis shows that Mg (2s) binding energy peak of Mg_2Ni aftermodification shifted from a lower binding energy to a higher one, indicating the charge transferencebetween Mg and THF and the formation of catalytically active electron donor-acceptor (EDA)complexes on the surface of modified Mg_2Ni alloy.
基金Funded by National Natural Science Foundations of China(Nos.51161015 and 50961009)Natural Science Foundation of Inner Mongolia,China(Nos.2011ZD10 and 2010ZD05)Higher Education Science Research Project of Inner Mongolia,China(No.NJzy08071)
文摘The nanocrystalline and amorphous Mg2Ni-type Mg2Ni1-xCox （x = 0, 0.1, 0.2, 0.3, 0.4） alloys were synthesized by melt quenching technology. The structures of the as-cast and quenched alloys were characterized by XRD, SEM and HRTEM. The gaseous hydrogen storage kinetics of the alloys was measured using an automatically controlled Sieverts apparatus. The alloy electrodes were charged and discharged with a constant current density in order to investigate the electrochemical hydrogen storage kinetics of the alloys. The results demonstrate that the substitution of Co for Ni results in the formation of secondary phases MgCo2 and Mg instead of altering the major phase Mg2Ni. No amorphous phase is detected in the as-quenched Co- ffee alloy, however, a certain amount of amorphous phase is clearly found in the as-quenched alloys substituted by Co. Furthermore, both the rapid quenching and the Co substitution significantly improve the gaseous and electrochemical hydrogen storage kinetics of the alloys, for which the notable increase of the hydrogen diffusion coefficient （D） along with the limiting current density （IL） and the obvious decline of the electrochemical impedance generated by both the Co substitution and the rapid quenching are basically responsible.