In the present paper, the behavior of a single polymer chain under various solvent conditions was modeled by self-avoiding walks (SAW) with nearest neighbors attraction Ae on a simple cubic lattice. Determination of t...In the present paper, the behavior of a single polymer chain under various solvent conditions was modeled by self-avoiding walks (SAW) with nearest neighbors attraction Ae on a simple cubic lattice. Determination of the 0-condition was based on the numerical results of the mean square radius of gyration and end-to-end distance. It was found that at the 0 temperature Delta epsilon /kT equals -0.27. The exponents a in the Mark-Houwink equation with different interaction parameters are consistent with the results of experiments: under 0-condition, alpha= 0.5, and for a good solvent alpha =0.74-0.84, respectively.展开更多
The polymerization of 1-octene initiated by methylalmnoxane （MAO）-activated Ni（II）-based-a-diimine complexes [（2,6-i-Pr）2C6H3-DAB（An）]NiBr2 was investigated. Using this catalyst, poly（1-octene）s with molecul...The polymerization of 1-octene initiated by methylalmnoxane （MAO）-activated Ni（II）-based-a-diimine complexes [（2,6-i-Pr）2C6H3-DAB（An）]NiBr2 was investigated. Using this catalyst, poly（1-octene）s with molecular weight between 100 × 10^3 and 400 ×10^3 and polydispersity （Mw/Mn） between 1.3 and 1.5 were synthesized successfully by varying reaction time at room temperature. The poly（1-octene）s were amorphous polymers and could be well soluble in tetrahydrofuran （THF）. After fractional precipitation, poly（1-octene）s with narrow molecular weight distributions （Mw/Mn 〈 1.12） were obtained. Their weight-average molecular weights were measured by gel permeation chromatography （GPC） in conjunction with online model BI-MwA multiangle laser light scattering （MALLS）, and their intrinsic viscosities were measured by Maron＇s single-point method. The k and a values in Mark-Houwink equation [η] = KM^a in THF at 40α were 0.089 mL/g and 0.61 respectively.展开更多
Bulk polymerization of vinylene carbonate using t-butylperoxypivalate at 40℃gave colourless, high molecular weight poly(vinylene carbonate) (PVCA). Solutions of PVCA in acetone and DMF are not stable at 25℃and this... Bulk polymerization of vinylene carbonate using t-butylperoxypivalate at 40℃gave colourless, high molecular weight poly(vinylene carbonate) (PVCA). Solutions of PVCA in acetone and DMF are not stable at 25℃and this degradation was studied. From measurements in DMF with unfractionated PVCA a Mark-Houwink equation was obtained:展开更多
基金This work was supported by the National Natural Science Foundation of China (No. 29974019)
文摘In the present paper, the behavior of a single polymer chain under various solvent conditions was modeled by self-avoiding walks (SAW) with nearest neighbors attraction Ae on a simple cubic lattice. Determination of the 0-condition was based on the numerical results of the mean square radius of gyration and end-to-end distance. It was found that at the 0 temperature Delta epsilon /kT equals -0.27. The exponents a in the Mark-Houwink equation with different interaction parameters are consistent with the results of experiments: under 0-condition, alpha= 0.5, and for a good solvent alpha =0.74-0.84, respectively.
基金supported by the program for new century excellent talents in Chinese universities and Beijing Municipal Education Commission
文摘The polymerization of 1-octene initiated by methylalmnoxane （MAO）-activated Ni（II）-based-a-diimine complexes [（2,6-i-Pr）2C6H3-DAB（An）]NiBr2 was investigated. Using this catalyst, poly（1-octene）s with molecular weight between 100 × 10^3 and 400 ×10^3 and polydispersity （Mw/Mn） between 1.3 and 1.5 were synthesized successfully by varying reaction time at room temperature. The poly（1-octene）s were amorphous polymers and could be well soluble in tetrahydrofuran （THF）. After fractional precipitation, poly（1-octene）s with narrow molecular weight distributions （Mw/Mn 〈 1.12） were obtained. Their weight-average molecular weights were measured by gel permeation chromatography （GPC） in conjunction with online model BI-MwA multiangle laser light scattering （MALLS）, and their intrinsic viscosities were measured by Maron＇s single-point method. The k and a values in Mark-Houwink equation [η] = KM^a in THF at 40α were 0.089 mL/g and 0.61 respectively.
文摘 Bulk polymerization of vinylene carbonate using t-butylperoxypivalate at 40℃gave colourless, high molecular weight poly(vinylene carbonate) (PVCA). Solutions of PVCA in acetone and DMF are not stable at 25℃and this degradation was studied. From measurements in DMF with unfractionated PVCA a Mark-Houwink equation was obtained: