Laser surface melting（LSM） is a high-energy surface treatment that allows modification of the microstructure and surface properties of Mg alloys. In the present work, an attempt of LSM on magnesium alloy with liquid...Laser surface melting（LSM） is a high-energy surface treatment that allows modification of the microstructure and surface properties of Mg alloys. In the present work, an attempt of LSM on magnesium alloy with liquid nitrogen-assisted cooling（LNSC） was carried out to get the higher cooling rate and improve the surface properties. The experimental results were compared with those of Ar gas protection at room temperature. The samples after LSM with LNSC resulted in a thinner melted layer, a highly homogeneous, refined melted microstructure and formed a lot of worm-like nanocrystals and local amorphous structures. Microhardness of the melted layer with LNAC was improved to HV 90-148 as compared to HV 65-105 of the samples with Ar gas protection. The corrosion resistance of the melted layer in a 3.5% Na Cl solution（mass fraction） was improved because of the grain refinement and redistribution of β-Mg17Al12 phases following rapid quenching associated with the process.展开更多
Based on volume of fluid(VoF)interface capturing method and shear-stress transport(SST)k-ω turbulence model,numerical simulation was performed to reveal the flow mechanism of metal melts in melt delivery nozzle(MDN)d...Based on volume of fluid(VoF)interface capturing method and shear-stress transport(SST)k-ω turbulence model,numerical simulation was performed to reveal the flow mechanism of metal melts in melt delivery nozzle(MDN)during gas atomization(GA)process.The experimental validation indicated that the numerical models could give a reasonable prediction on the melt flow process in the MDN.With the decrease of the MDN inner-diameter,the melt flow resistance increased for both molten aluminum and iron,especially achieving an order of 10^(2) kPa in the case of the MDN inner-diameter≤1 mm.Based on the conventional GA process,the positive pressure was imposed on the viscous aluminum alloy melt to overcome its flow resistance in the MDN,thus producing powders under different MDN inner-diameters.When the MDN inner-diameter was reduced from 4 to 2 mm,the yield of fine powder(<150μm)soared from 54.7%to 94.2%.The surface quality of powders has also been improved when using a smaller inner-diameter MDN.展开更多
A low-energy plasma electrolytic oxidation(LePEO)technique is developed to simultaneously improve energy efficiency and anti-corrosion.Ionic liquids(1-butyl-3-methylimidazole tetrafluoroborate(BmimBF_(4)))as sustainab...A low-energy plasma electrolytic oxidation(LePEO)technique is developed to simultaneously improve energy efficiency and anti-corrosion.Ionic liquids(1-butyl-3-methylimidazole tetrafluoroborate(BmimBF_(4)))as sustainable corrosion inhibitors are chosen to investigate the corrosion inhibition behavior of ionic liquid(ILs)during the LePEO process for LA91 magnesium-lithium(Mg-Li)alloy.Results show that the ionic liquid BmimBF_(4)participates in the LePEO coating formation process,causing an increment in coating thickness and surface roughness.The low conductivity of the ionic liquid is responsible for the voltage and breakdown voltage increases during the LePEO with IL process(LePEO-IL).After adding BmimBF_(4),corrosion current density decreases from 1.159×10^(−4)A·cm^(−2)to 8.143×10^(−6)A·cm^(−2).The impedance modulus increases to 1.048×10^(4)Ω·cm^(−2)and neutral salt spray remains intact for 24 h.The superior corrosion resistance of the LePEO coating assisted by ionic liquid could be mainly attributed to its compact and thick barrier layer and physical absorption of ionic liquid.The ionic liquid-assisted LePEO technique provides a promising approach to reducing energy consumption and improving film performance.展开更多
基金Project(51305292)supported by the National Natural Science Foundation of ChinaProject(2014-024)supported by Shanxi Scholarship Council of China
文摘Laser surface melting（LSM） is a high-energy surface treatment that allows modification of the microstructure and surface properties of Mg alloys. In the present work, an attempt of LSM on magnesium alloy with liquid nitrogen-assisted cooling（LNSC） was carried out to get the higher cooling rate and improve the surface properties. The experimental results were compared with those of Ar gas protection at room temperature. The samples after LSM with LNSC resulted in a thinner melted layer, a highly homogeneous, refined melted microstructure and formed a lot of worm-like nanocrystals and local amorphous structures. Microhardness of the melted layer with LNAC was improved to HV 90-148 as compared to HV 65-105 of the samples with Ar gas protection. The corrosion resistance of the melted layer in a 3.5% Na Cl solution（mass fraction） was improved because of the grain refinement and redistribution of β-Mg17Al12 phases following rapid quenching associated with the process.
基金the National Natural Science Foundation of China(No.52074157)Shenzhen Science and Technology Innovation Com-mission,China(Nos.JSGG20180508152608855,KQTD20170328154443162)Shenzhen Key Laboratory for Additive Manufacturing of High-performance Materials,China(No.ZDSYS201703031748354).
文摘Based on volume of fluid(VoF)interface capturing method and shear-stress transport(SST)k-ω turbulence model,numerical simulation was performed to reveal the flow mechanism of metal melts in melt delivery nozzle(MDN)during gas atomization(GA)process.The experimental validation indicated that the numerical models could give a reasonable prediction on the melt flow process in the MDN.With the decrease of the MDN inner-diameter,the melt flow resistance increased for both molten aluminum and iron,especially achieving an order of 10^(2) kPa in the case of the MDN inner-diameter≤1 mm.Based on the conventional GA process,the positive pressure was imposed on the viscous aluminum alloy melt to overcome its flow resistance in the MDN,thus producing powders under different MDN inner-diameters.When the MDN inner-diameter was reduced from 4 to 2 mm,the yield of fine powder(<150μm)soared from 54.7%to 94.2%.The surface quality of powders has also been improved when using a smaller inner-diameter MDN.
基金supported by the Natural Science Founda-tion of Beijing(Grant No.2182017,2202017).
文摘A low-energy plasma electrolytic oxidation(LePEO)technique is developed to simultaneously improve energy efficiency and anti-corrosion.Ionic liquids(1-butyl-3-methylimidazole tetrafluoroborate(BmimBF_(4)))as sustainable corrosion inhibitors are chosen to investigate the corrosion inhibition behavior of ionic liquid(ILs)during the LePEO process for LA91 magnesium-lithium(Mg-Li)alloy.Results show that the ionic liquid BmimBF_(4)participates in the LePEO coating formation process,causing an increment in coating thickness and surface roughness.The low conductivity of the ionic liquid is responsible for the voltage and breakdown voltage increases during the LePEO with IL process(LePEO-IL).After adding BmimBF_(4),corrosion current density decreases from 1.159×10^(−4)A·cm^(−2)to 8.143×10^(−6)A·cm^(−2).The impedance modulus increases to 1.048×10^(4)Ω·cm^(−2)and neutral salt spray remains intact for 24 h.The superior corrosion resistance of the LePEO coating assisted by ionic liquid could be mainly attributed to its compact and thick barrier layer and physical absorption of ionic liquid.The ionic liquid-assisted LePEO technique provides a promising approach to reducing energy consumption and improving film performance.