Organo-fly ash （OFA） was prepared with pretreated fly ash （FA） and hexadecyltrimethyl ammonium bromide （HDTMAB）, and the composites composed of OFA and polyaniline were obtained by emulsion polymerization at dif...Organo-fly ash （OFA） was prepared with pretreated fly ash （FA） and hexadecyltrimethyl ammonium bromide （HDTMAB）, and the composites composed of OFA and polyaniline were obtained by emulsion polymerization at different OFA weight ratios （2.0 wt%, 5.0 wt%, 10.0 wt%, 15.0 wt% and 20.0 wt%） in the presence of dodecylbenzenesulfonic acid as dopant and emulsifier. A polymerization procedure was supposed. The electrical conductivities of the composites were tested by the four-probe technique. The chemical structure and crystallinity of the composites were confirmed by FT-IR and X-ray diffraction, respectively. Morphologies of FA, OFA and the composites were observed by SEM. The element analysis was performed by energy dispersive spectrometry. The thermal stability of the composites was analyzed by TGA. The results showed that the electrical conductivity of the composites decreased with increasing the feed weight ratio of OFA, and the lowest value was 0.62 S/cm. HDTMAB and PAn were just adsorbed on the surface of FA and OFA, respectively according to the physical adsorption without destroying the crystalline structure of FA or OFA. The surface became smoother after organification of FA by using HDTMAB, and its content on FA surfaces was about 26.9 wt%. The core/shell structure of the composite was observed by SEM analysis. The composites showed a higher thermal stability than pure PAn by introduction of OFA into this polymerization system, the heat stability of PAn was increased by decreasing 31.8 wt% of weight loss after introducing 20 wt% of OFA.展开更多
Plasma-induced surface graft copolymerization of acrylic acid on polypropylene non-woven fabric(PP-g-AA)andpolypropylene membrane were reported.The extents of grafting were controlled by the plasma and polymerizationc...Plasma-induced surface graft copolymerization of acrylic acid on polypropylene non-woven fabric(PP-g-AA)andpolypropylene membrane were reported.The extents of grafting were controlled by the plasma and polymerizationcondition.Hexadecyltrimethyl ammonium bromide was then coupled with the carboxyl group of PP-g-AA to obtain apolyion complex(PIC).At last,CF_4 plasma was used to give PICs hydrophobic property.The moisture regain and water-repellency of the processed PICs was investigated.The surfaces were characterized using ATR FT-IR and XPS.The resultindicates that the products have very high ability to adsorb moisture,even better than cotton fiber.At the same time,theproducts show excellent hydrophobic property,which can't be wetted by those reagents whose surface tensions were higherthan 327 mN/m.展开更多
Surfactant-modified natural zeolites(SMNZ)with different coverage types were prepared by loading hexadecyltrimethyl ammonium bromide(HTAB)onto the surface of a natural zeolite.The adsorption behavior of humic acid(HA)...Surfactant-modified natural zeolites(SMNZ)with different coverage types were prepared by loading hexadecyltrimethyl ammonium bromide(HTAB)onto the surface of a natural zeolite.The adsorption behavior of humic acid(HA)on SMNZ was investigated.Results indicate that the adsorbent SMNZ exhibited a higher affinity toward HA than the natural zeolite.HA removal efficiency by SMNZ increased with HTAB loading.Coexisting Ca2+in solution favored HA adsorption onto SMNZ.Adsorption capacity decreased with an increasing solution pH.For typical SMNZ with bilayer HTAB coverage,HA adsorption process is well described by a pseudo-second-order kinetic model.The experimental isotherm data fitted well with the Langmuir model.Calculated maximum HA adsorption capacities for SMNZ with bilayer HTAB coverage at pH 5.5 and 7.5 were 63 and 41 mg·g^(-1),respectively.E2/E3(absorbance at 250 nm to that at 365 nm)and E4/E6(absorbance at 465 nm to that at 665 nm)ratios of the residual HA in solution were lower than that of the original HA solution.This indicates that the HA fractions with high polar functional groups,low molecular weight(MW),and aromaticity had a stronger tendency for adsorption onto SMNZ with bilayer HTAB coverage.Results show that HTABmodified natural zeolite is a promising adsorbent for removal of HA from aqueous solution.展开更多
基金supported by the Shaanxi Provincial Education Department(No.09JK528) and Program of Shaanxi Key Subject
文摘Organo-fly ash （OFA） was prepared with pretreated fly ash （FA） and hexadecyltrimethyl ammonium bromide （HDTMAB）, and the composites composed of OFA and polyaniline were obtained by emulsion polymerization at different OFA weight ratios （2.0 wt%, 5.0 wt%, 10.0 wt%, 15.0 wt% and 20.0 wt%） in the presence of dodecylbenzenesulfonic acid as dopant and emulsifier. A polymerization procedure was supposed. The electrical conductivities of the composites were tested by the four-probe technique. The chemical structure and crystallinity of the composites were confirmed by FT-IR and X-ray diffraction, respectively. Morphologies of FA, OFA and the composites were observed by SEM. The element analysis was performed by energy dispersive spectrometry. The thermal stability of the composites was analyzed by TGA. The results showed that the electrical conductivity of the composites decreased with increasing the feed weight ratio of OFA, and the lowest value was 0.62 S/cm. HDTMAB and PAn were just adsorbed on the surface of FA and OFA, respectively according to the physical adsorption without destroying the crystalline structure of FA or OFA. The surface became smoother after organification of FA by using HDTMAB, and its content on FA surfaces was about 26.9 wt%. The core/shell structure of the composite was observed by SEM analysis. The composites showed a higher thermal stability than pure PAn by introduction of OFA into this polymerization system, the heat stability of PAn was increased by decreasing 31.8 wt% of weight loss after introducing 20 wt% of OFA.
文摘Plasma-induced surface graft copolymerization of acrylic acid on polypropylene non-woven fabric(PP-g-AA)andpolypropylene membrane were reported.The extents of grafting were controlled by the plasma and polymerizationcondition.Hexadecyltrimethyl ammonium bromide was then coupled with the carboxyl group of PP-g-AA to obtain apolyion complex(PIC).At last,CF_4 plasma was used to give PICs hydrophobic property.The moisture regain and water-repellency of the processed PICs was investigated.The surfaces were characterized using ATR FT-IR and XPS.The resultindicates that the products have very high ability to adsorb moisture,even better than cotton fiber.At the same time,theproducts show excellent hydrophobic property,which can't be wetted by those reagents whose surface tensions were higherthan 327 mN/m.
基金This work was supported by the National Major Project of Science and Technology Ministry of China(Grant No.2008ZX07421-002)the National Natural Science Foundation of China(Grant No.50908142)the National Science and Technology Infrastructure Program of China(Grant No.2006BAJ08B02).
文摘Surfactant-modified natural zeolites(SMNZ)with different coverage types were prepared by loading hexadecyltrimethyl ammonium bromide(HTAB)onto the surface of a natural zeolite.The adsorption behavior of humic acid(HA)on SMNZ was investigated.Results indicate that the adsorbent SMNZ exhibited a higher affinity toward HA than the natural zeolite.HA removal efficiency by SMNZ increased with HTAB loading.Coexisting Ca2+in solution favored HA adsorption onto SMNZ.Adsorption capacity decreased with an increasing solution pH.For typical SMNZ with bilayer HTAB coverage,HA adsorption process is well described by a pseudo-second-order kinetic model.The experimental isotherm data fitted well with the Langmuir model.Calculated maximum HA adsorption capacities for SMNZ with bilayer HTAB coverage at pH 5.5 and 7.5 were 63 and 41 mg·g^(-1),respectively.E2/E3(absorbance at 250 nm to that at 365 nm)and E4/E6(absorbance at 465 nm to that at 665 nm)ratios of the residual HA in solution were lower than that of the original HA solution.This indicates that the HA fractions with high polar functional groups,low molecular weight(MW),and aromaticity had a stronger tendency for adsorption onto SMNZ with bilayer HTAB coverage.Results show that HTABmodified natural zeolite is a promising adsorbent for removal of HA from aqueous solution.