The lanthanum molybdovanadophosphoric tetrabasic heteropoly complex was synthesized.Catalytic properties of the title heteropoly complex for selective oxidation of ethylbezene to acetonphenone was investigated.The sui...The lanthanum molybdovanadophosphoric tetrabasic heteropoly complex was synthesized.Catalytic properties of the title heteropoly complex for selective oxidation of ethylbezene to acetonphenone was investigated.The suitable reaction conditions was discussed.展开更多
合成了未见报道的标题配合物。通过化学分析、ICP和TG曲线确定了其化学式为K_8H_3[Y(PW_(11)O_(39))_2]·25H_2O;利用IR、UV、XRD、^(183)W-NMR、循环伏安等手段对其结构进行了表征,结果表明杂多阴离子为β_2型Keggin结构。采用稀...合成了未见报道的标题配合物。通过化学分析、ICP和TG曲线确定了其化学式为K_8H_3[Y(PW_(11)O_(39))_2]·25H_2O;利用IR、UV、XRD、^(183)W-NMR、循环伏安等手段对其结构进行了表征,结果表明杂多阴离子为β_2型Keggin结构。采用稀土多元渗的方法对配合物进行了气相热扩渗,经ICP和XPS测试表明:微量的稀土元素La和Ce可以渗入到配合物的体相,并与组份元素存在键合作用。扩渗后化合物的化学式为K_8H_6YLa_(0.11)Ce_(0.18)P_2W_4~ⅤW_(18)~ⅥO_(78)·15H_2O,其晶体属单斜晶系,晶胞参数:a=6.3775nm,b=3.6771nm,c=3.7727nm,β=90.192°,V=88.47326nm^3;导电性的测试结果表明:室温时,扩渗后试样的电导率提高了约10~3倍,且热稳定范围变宽,523K时的电导率为1.33×10^(-2)S·cm^(-1),有望成为实用化的导电材料;~1H MAS NMR测试结果表明其存在三种质子,其导电机理可能是质子导电。展开更多
利用水热合成法合成了分子组成为(C6H11NH3)5H(P2Mo5O23)4H2O的杂多化合物, 用单晶X-ray衍射方法测定了它的结构,该晶体属于单斜晶系,空间群P21/c, a = 12.830(3), b = 14.848(3), c = 25.258(5) ? b = 92.95(3), Mr = 1483.62, V = 48...利用水热合成法合成了分子组成为(C6H11NH3)5H(P2Mo5O23)4H2O的杂多化合物, 用单晶X-ray衍射方法测定了它的结构,该晶体属于单斜晶系,空间群P21/c, a = 12.830(3), b = 14.848(3), c = 25.258(5) ? b = 92.95(3), Mr = 1483.62, V = 4805.1(17) 3, Z = 4, Dc = 2.051 g/cm3, m = 1.431 mm-1, F(000) = 3000, I >2s(I) 的可观察衍射点4426个, 最终结构偏差因子R = 0.0464, wR = 0.0801, S = 0.731。在[P2Mo5O23]6-杂多阴离子中5个MoO6八面体通过共边和共角相连, 形成1个近似的五角平面骨架, 2个PO4四面体加在五角平面的两侧。热性质研究表明杂多阴离子骨架在547.4 ℃左右分解。展开更多
文摘The lanthanum molybdovanadophosphoric tetrabasic heteropoly complex was synthesized.Catalytic properties of the title heteropoly complex for selective oxidation of ethylbezene to acetonphenone was investigated.The suitable reaction conditions was discussed.
文摘合成了未见报道的标题配合物。通过化学分析、ICP和TG曲线确定了其化学式为K_8H_3[Y(PW_(11)O_(39))_2]·25H_2O;利用IR、UV、XRD、^(183)W-NMR、循环伏安等手段对其结构进行了表征,结果表明杂多阴离子为β_2型Keggin结构。采用稀土多元渗的方法对配合物进行了气相热扩渗,经ICP和XPS测试表明:微量的稀土元素La和Ce可以渗入到配合物的体相,并与组份元素存在键合作用。扩渗后化合物的化学式为K_8H_6YLa_(0.11)Ce_(0.18)P_2W_4~ⅤW_(18)~ⅥO_(78)·15H_2O,其晶体属单斜晶系,晶胞参数:a=6.3775nm,b=3.6771nm,c=3.7727nm,β=90.192°,V=88.47326nm^3;导电性的测试结果表明:室温时,扩渗后试样的电导率提高了约10~3倍,且热稳定范围变宽,523K时的电导率为1.33×10^(-2)S·cm^(-1),有望成为实用化的导电材料;~1H MAS NMR测试结果表明其存在三种质子,其导电机理可能是质子导电。