The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The r...The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The results indicate that the Cu-P master alloy possesses not only obvious modification effect,but also longevity effect with more than 8 h on the hypereutectic Al-Si alloy.It is shown from thermal calculation,scanning electron microscope（SEM）,and energy dispersive analysis of X-rays（EDAX） that the modification mechanism of Cu-P on primary silicon in the castings is heterogeneous nucleation around AlP particles.The Cu-P master alloy has no or little modifying effect on eutectic silicon,even though it has obvious modification on primary silicon in the castings.This may be because of the fast transformation of eutectic silicon at a very narrow temperature,which will notably weaken the role of AlP particles as heterogeneous nuclei for eutectic silicon.展开更多
The effect of the rare earth cerium （Ce） on the hypereutectic Al-Si alloy under different casting states have been studied by optical microscope and quantitative image analysis. It is found that the size and the qua...The effect of the rare earth cerium （Ce） on the hypereutectic Al-Si alloy under different casting states have been studied by optical microscope and quantitative image analysis. It is found that the size and the quantity of primary silicon in castings decrease with the increase of added Ce in the melt. Meanwhile primary silicon changes from branched shape to fine facetted shape. Although the modification on eutectic silicon in castings also improves with the increase of added Ce in the melt, the effect of modification on eutectic silicon away from primary silicon is more obvious than that on eutectic silicon close to primary silicon. The modification mechanism was analyzed in detail by means of scanning electron microscope equipped with energy dispersive analysis of X-ray and thermodynamics analysis, which included the analysis on the change in standard Gibbs energy of reaction and reaction equilibrium.展开更多
Microstructural evolution and phase transformation induced by different heat treatments of the hypereutectic aluminium-silicon alloy, Al-25Si-5Fe-3Cu （wt%, signed as 3C）, fabricated by traditional cast （TC） and sp...Microstructural evolution and phase transformation induced by different heat treatments of the hypereutectic aluminium-silicon alloy, Al-25Si-5Fe-3Cu （wt%, signed as 3C）, fabricated by traditional cast （TC） and spray forming （SF） processes, were investigated by differential scanning calorimetry （DSC） and scanning electron microscopy （SEM） combined with energy dispersive X-ray spectroscopy and X-ray diffraction techniques. The results show that A17Cu2Fe phase can be formed and transformed in TC- and SF-3C alloys between 802-813 K and 800-815 K, respectively. The transformation from β-Al5FeSi to δ-Al4FeSi2 phase via peritectic reaction can occur at around 858-870 K and 876-890 K in TC- and SF-3C alloys, respectively. The starting precipitation temperature of δ-Al4FeSi2 phase as the dominant Fe-bearing phase in the TC-3C alloy is 997 K and the exothermic peak about the peritectic transformation of δ-Al4FeSi2→β-Al5FeSi is not detected in the present DSC experiments. Also, the mechanisms of the microstructural evolution and phase transformation are discussed.展开更多
The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing...The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing compounds in the alloys produced by conventional casting process are detrimental to the strength of matrix. The effect of ultrasonic vibration （USV） on the morphology change of Fe-containing intermetallic compounds in the hypereutectic Al-17Si-xFe （x=2, 3, 4, 5） alloys was systematically studied. The results show that, the Fe-containing intermetallic compounds are mainly composed of long needle-like β-Al5FeSi phase with a small amount of plate-like δ-Al4FeSi2 phase in Al-17Si-2Fe alloy produced by conventional casting process. With the increase of Fe content from 2% to 5% in the alloys, the amount of plate-like or coarse needle-like δ-Al4FeSi2 phase increases while the amount of long needle-like β-Al5FeSi phases decreases. In Al-17Si-5Fe alloy, the Fe-containing intermetallic compounds exist mainly as coarse needle-like δ-Al4FeSi2 phase. After USV treatment, the Fe-containing compounds in the Al-17Si-xFe alloys are refined and exist mainly as δ-Al4FeSi2 particles, with average grain size ranging from 26 μm to 37 μm, and only a small amount of β-Al5FeSi phases remain. The mechanism of USV on the morphology of Fe-containing intermetallic compounds was also discussed.展开更多
The influence of high pressure and manganese addition on Fe-rich phases(FRPs)and mechanical properties of Al-14Si-2Fe alloy with rheo-squeeze casting(RSC)was investigated.The semi-solid alloy melt was treated by ultra...The influence of high pressure and manganese addition on Fe-rich phases(FRPs)and mechanical properties of Al-14Si-2Fe alloy with rheo-squeeze casting(RSC)was investigated.The semi-solid alloy melt was treated by ultrasonic vibration(UV)firstly,and then formed by squeeze casting(SC).Results show that the FRPs in as-cast SC alloys are composed of coarseβ-Al5(Fe,Mn)Si,δ-Al4(Fe,Mn)Si2 and bone-shapedα-Al15(Fe,Mn)3Si2 phases when the pressure is 0 MPa.With RSC process,the FRPs are first refined by UV,and then the solidification under pressure further causes the grains to become smaller.The peritectic transformation occurs during the formation ofαphase.For the alloy with the same composition,the ultimate tensile strength(UTS)of RSC sample is higher than that of the SC sample.With the same forming process,the UTS of Al-14Si-2Fe-0.8Mn alloy is higher than that of Al-14Si-2Fe-0.4Mn alloy.展开更多
The effects of mixed rare earth oxides and CaCO3 on the microstructure of an in-situ Mg2Si/Al-Si hypereutectic alloy composite were investigated by optical microscope,scanning electron microscope,and energy dispersive...The effects of mixed rare earth oxides and CaCO3 on the microstructure of an in-situ Mg2Si/Al-Si hypereutectic alloy composite were investigated by optical microscope,scanning electron microscope,and energy dispersive spectrum analysis. The results showed that the morphol-ogy of the primary Mg2Si phase particles changed from irregular or crosses to polygonal shape,their sizes decreased from 75 μm to about 25 μm,and the compound of both the oxide and CaCO3 was better than either the single mixed rare earth o...展开更多
The effect of squeeze casting on microstructure and mechanical properties of hypereutectic Al-xS i alloys（x = 15, 17.5, 22 wt%） was investigated in this study. Results show that microstructure of the hypereutectic A...The effect of squeeze casting on microstructure and mechanical properties of hypereutectic Al-xS i alloys（x = 15, 17.5, 22 wt%） was investigated in this study. Results show that microstructure of the hypereutectic Al-x Si alloys was obviously improved by squeeze casting. The amount of coarse primary Si phase decreased, while that of fine primary α-Al dendrites increased with the increase of squeeze casting pressure. Due to the decrease of coarse primary Si particles, cracking of the matrix was reduced, whilst the fine microstructure, and mechanical properties of the squeeze casting alloys were improved. Compared with gravity casting alloys, mechanical properties of the hypereutectic Al-xS i alloys solidified at 600 MPa were improved significantly. Hardness of the squeeze casting hypereutectic Al-（15, 17.5, 22 wt%） Si alloys was improved by 15.91%, 12.23%, 17.48%, ultimate tensile strength was improved by 37.85%, 32.27%, 22.74%,and elongation was improved by 55.83%, 167.86%, 126.76%, respectively. Due to the uniform distribution of Si phases in squeeze casting Al-x Si alloys, their wear resistance was markedly enhanced.展开更多
The feasibility of semi solid processing of hypereutectic A390 alloys using a novel rheoforming process was investigated. A combination of the swirl enthalpy equilibration device （SEED） process, isothermal holding u...The feasibility of semi solid processing of hypereutectic A390 alloys using a novel rheoforming process was investigated. A combination of the swirl enthalpy equilibration device （SEED） process, isothermal holding using insulation and addition of solid alloy during swirling was introduced as a novel method to improve the processability of semi solid slurry. The effects of isothermal holding and the addition of solid alloy on the temperature gradient between the centre and the wall and on the formation of a（Al） particles were examined. In additional tests, phosphorus and strontium were added to the molten metal to refine the primary and eutectic silicon structure to facilitate semi solid processing. The results show that the combination of the SEED process with two additional processing steps can produce semi-solid A390 alloys that can be rheoprocessed. The microstructure reveals an adequate amount of non-dendritic a（Al） globules surrounded by liquid, which greatly improves the processability of semi-solid slurry.展开更多
Hypereutectic aluminum-silicon alloy powder of Al-20Si-0.35RE was synthesized by using the inert gas atomization technique. This powder was ball milled for different time and hot extruded subsequently. The microstruct...Hypereutectic aluminum-silicon alloy powder of Al-20Si-0.35RE was synthesized by using the inert gas atomization technique. This powder was ball milled for different time and hot extruded subsequently. The microstructure and electrical conductivity of alloy were studied by powder particle size analyzer, scanning electron microscope, X-ray diffraction and bridge resistance instrument respectively. It is indicated that the powder got by spray method have a better homogeneous distribution. The proper RE amount and milling time improved the conductivity due to either microstructural refining or decreasing of Si solid solubility in Al matrix. The conductivity changed with ball milling time, while unique high conductivity (75%IACS) could be achieved after milling for 12 h and hot-extruded 3 times. This kind of high conductivity aluminum-silicon alloy will be a potential conductor material which could be extensively used in the electrical engineering field.展开更多
文摘The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The results indicate that the Cu-P master alloy possesses not only obvious modification effect,but also longevity effect with more than 8 h on the hypereutectic Al-Si alloy.It is shown from thermal calculation,scanning electron microscope（SEM）,and energy dispersive analysis of X-rays（EDAX） that the modification mechanism of Cu-P on primary silicon in the castings is heterogeneous nucleation around AlP particles.The Cu-P master alloy has no or little modifying effect on eutectic silicon,even though it has obvious modification on primary silicon in the castings.This may be because of the fast transformation of eutectic silicon at a very narrow temperature,which will notably weaken the role of AlP particles as heterogeneous nuclei for eutectic silicon.
基金The work is financially supported by Shanghai Leading Academic Discipline Project (No. T0101)the Open Funds of Shanghai Key Laboratory of Metal Function Materials Research and Application.
文摘The effect of the rare earth cerium （Ce） on the hypereutectic Al-Si alloy under different casting states have been studied by optical microscope and quantitative image analysis. It is found that the size and the quantity of primary silicon in castings decrease with the increase of added Ce in the melt. Meanwhile primary silicon changes from branched shape to fine facetted shape. Although the modification on eutectic silicon in castings also improves with the increase of added Ce in the melt, the effect of modification on eutectic silicon away from primary silicon is more obvious than that on eutectic silicon close to primary silicon. The modification mechanism was analyzed in detail by means of scanning electron microscope equipped with energy dispersive analysis of X-ray and thermodynamics analysis, which included the analysis on the change in standard Gibbs energy of reaction and reaction equilibrium.
基金supported by the Major State Basic Research & Development Program of China (No2006CB605204)
文摘Microstructural evolution and phase transformation induced by different heat treatments of the hypereutectic aluminium-silicon alloy, Al-25Si-5Fe-3Cu （wt%, signed as 3C）, fabricated by traditional cast （TC） and spray forming （SF） processes, were investigated by differential scanning calorimetry （DSC） and scanning electron microscopy （SEM） combined with energy dispersive X-ray spectroscopy and X-ray diffraction techniques. The results show that A17Cu2Fe phase can be formed and transformed in TC- and SF-3C alloys between 802-813 K and 800-815 K, respectively. The transformation from β-Al5FeSi to δ-Al4FeSi2 phase via peritectic reaction can occur at around 858-870 K and 876-890 K in TC- and SF-3C alloys, respectively. The starting precipitation temperature of δ-Al4FeSi2 phase as the dominant Fe-bearing phase in the TC-3C alloy is 997 K and the exothermic peak about the peritectic transformation of δ-Al4FeSi2→β-Al5FeSi is not detected in the present DSC experiments. Also, the mechanisms of the microstructural evolution and phase transformation are discussed.
基金Project(2012CB619600)supported by the National Basic Research Program of ChinaProject(50775086)supported by the National Natural Science Foundation of China
文摘The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing compounds in the alloys produced by conventional casting process are detrimental to the strength of matrix. The effect of ultrasonic vibration （USV） on the morphology change of Fe-containing intermetallic compounds in the hypereutectic Al-17Si-xFe （x=2, 3, 4, 5） alloys was systematically studied. The results show that, the Fe-containing intermetallic compounds are mainly composed of long needle-like β-Al5FeSi phase with a small amount of plate-like δ-Al4FeSi2 phase in Al-17Si-2Fe alloy produced by conventional casting process. With the increase of Fe content from 2% to 5% in the alloys, the amount of plate-like or coarse needle-like δ-Al4FeSi2 phase increases while the amount of long needle-like β-Al5FeSi phases decreases. In Al-17Si-5Fe alloy, the Fe-containing intermetallic compounds exist mainly as coarse needle-like δ-Al4FeSi2 phase. After USV treatment, the Fe-containing compounds in the Al-17Si-xFe alloys are refined and exist mainly as δ-Al4FeSi2 particles, with average grain size ranging from 26 μm to 37 μm, and only a small amount of β-Al5FeSi phases remain. The mechanism of USV on the morphology of Fe-containing intermetallic compounds was also discussed.
基金Project(51605342) supported by the National Natural Science Foundation of ChinaProject(2015CFB431) supported by the Natural Science Foundation of Hubei Province,China+1 种基金Project(K201520) supported by the Science Research Foundation of Wuhan Institute of Technology,ChinaProject(2016KA01) supported by the Open Research Fund Program of Hubei Provincial Key Laboratory of Chemical Equipment Intensification and Intrinsic Safety,China
文摘The influence of high pressure and manganese addition on Fe-rich phases(FRPs)and mechanical properties of Al-14Si-2Fe alloy with rheo-squeeze casting(RSC)was investigated.The semi-solid alloy melt was treated by ultrasonic vibration(UV)firstly,and then formed by squeeze casting(SC).Results show that the FRPs in as-cast SC alloys are composed of coarseβ-Al5(Fe,Mn)Si,δ-Al4(Fe,Mn)Si2 and bone-shapedα-Al15(Fe,Mn)3Si2 phases when the pressure is 0 MPa.With RSC process,the FRPs are first refined by UV,and then the solidification under pressure further causes the grains to become smaller.The peritectic transformation occurs during the formation ofαphase.For the alloy with the same composition,the ultimate tensile strength(UTS)of RSC sample is higher than that of the SC sample.With the same forming process,the UTS of Al-14Si-2Fe-0.8Mn alloy is higher than that of Al-14Si-2Fe-0.4Mn alloy.
基金the Natural Science Foundation of Jiangxi Province (No. 0650047)the Science and Technology Program of the Education Department of Jiangxi Province,China(No.GJJ08268).
文摘The effects of mixed rare earth oxides and CaCO3 on the microstructure of an in-situ Mg2Si/Al-Si hypereutectic alloy composite were investigated by optical microscope,scanning electron microscope,and energy dispersive spectrum analysis. The results showed that the morphol-ogy of the primary Mg2Si phase particles changed from irregular or crosses to polygonal shape,their sizes decreased from 75 μm to about 25 μm,and the compound of both the oxide and CaCO3 was better than either the single mixed rare earth o...
基金support from the National Natural Science Foundation of China(Grant No.51674168)Shenyang Application Basic Research Fund(Grant No.F14-231-1-23)
文摘The effect of squeeze casting on microstructure and mechanical properties of hypereutectic Al-xS i alloys（x = 15, 17.5, 22 wt%） was investigated in this study. Results show that microstructure of the hypereutectic Al-x Si alloys was obviously improved by squeeze casting. The amount of coarse primary Si phase decreased, while that of fine primary α-Al dendrites increased with the increase of squeeze casting pressure. Due to the decrease of coarse primary Si particles, cracking of the matrix was reduced, whilst the fine microstructure, and mechanical properties of the squeeze casting alloys were improved. Compared with gravity casting alloys, mechanical properties of the hypereutectic Al-xS i alloys solidified at 600 MPa were improved significantly. Hardness of the squeeze casting hypereutectic Al-（15, 17.5, 22 wt%） Si alloys was improved by 15.91%, 12.23%, 17.48%, ultimate tensile strength was improved by 37.85%, 32.27%, 22.74%,and elongation was improved by 55.83%, 167.86%, 126.76%, respectively. Due to the uniform distribution of Si phases in squeeze casting Al-x Si alloys, their wear resistance was markedly enhanced.
基金the financial support provided by the Natural Sciences and Engineering Research Council of Canada (NSERC) and Rio Tinto Alcan through the NSERC Industrial Research Chair in Metallurgy of Aluminum Transformation at Université du Québec à Chicoutimi
文摘The feasibility of semi solid processing of hypereutectic A390 alloys using a novel rheoforming process was investigated. A combination of the swirl enthalpy equilibration device （SEED） process, isothermal holding using insulation and addition of solid alloy during swirling was introduced as a novel method to improve the processability of semi solid slurry. The effects of isothermal holding and the addition of solid alloy on the temperature gradient between the centre and the wall and on the formation of a（Al） particles were examined. In additional tests, phosphorus and strontium were added to the molten metal to refine the primary and eutectic silicon structure to facilitate semi solid processing. The results show that the combination of the SEED process with two additional processing steps can produce semi-solid A390 alloys that can be rheoprocessed. The microstructure reveals an adequate amount of non-dendritic a（Al） globules surrounded by liquid, which greatly improves the processability of semi-solid slurry.
基金Shanghai Science and Technology Expertise Program (10QB1400800)Shanghai Science and Technology Committee Foundation (08DZ2201300)National Natural Science Foundation of China (50901052)
文摘Hypereutectic aluminum-silicon alloy powder of Al-20Si-0.35RE was synthesized by using the inert gas atomization technique. This powder was ball milled for different time and hot extruded subsequently. The microstructure and electrical conductivity of alloy were studied by powder particle size analyzer, scanning electron microscope, X-ray diffraction and bridge resistance instrument respectively. It is indicated that the powder got by spray method have a better homogeneous distribution. The proper RE amount and milling time improved the conductivity due to either microstructural refining or decreasing of Si solid solubility in Al matrix. The conductivity changed with ball milling time, while unique high conductivity (75%IACS) could be achieved after milling for 12 h and hot-extruded 3 times. This kind of high conductivity aluminum-silicon alloy will be a potential conductor material which could be extensively used in the electrical engineering field.