Pores,microcracks and density of plasma sprayed Cr2O3 coatings before and after high-intensity pulsed ion beam(HIPIB) irradiation were investigated using the ultrasonic reflection coefficient spectroscopy(URCS).The UR...Pores,microcracks and density of plasma sprayed Cr2O3 coatings before and after high-intensity pulsed ion beam(HIPIB) irradiation were investigated using the ultrasonic reflection coefficient spectroscopy(URCS).The URCS was analyzed based on an acoustic transmission model for the multi-layered structure.The longitudinal velocity in the coatings was calculated from the experimental URCS,and the attenuation coefficient expression was deduced by comparing the experimental and numerical fitting amplitude spectral lines.The longitudinal velocity of as-sprayed Cr2O3 coating is 2 002 m/s,and increases to 2 099 and 2 148 m/s after being irradiated by HIPIB with 1 and 5 shots.Correspondingly,the factor A changes from 0.046 to 0.026 and 0.020 and n from 1.702 to 1.658 and 1.649 in the attenuation coefficient expression of α=Af n.It is observed that the surface morphology of Cr2O3 coatings changes from rough and porous to smooth and uniform with the increase of shot number,which accords with the ultrasonic analyses reasonably.The URCS seems to provide a convenient and nondestructive method to characterize surface modification of the plasma sprayed coatings.展开更多
Two types of commercial WC-Ni samples were irradiated with the High-intensity pulsed ion beam(HIPIB).Both the surface characteristics and tribo-characteristics of the non-irradiated and irradiated WC-Ni samples,slidin...Two types of commercial WC-Ni samples were irradiated with the High-intensity pulsed ion beam(HIPIB).Both the surface characteristics and tribo-characteristics of the non-irradiated and irradiated WC-Ni samples,sliding against graphite under water lubrication,were compared.Quite low steady friction coefficients(approximately of 0.02) of the irradiated WC-Ni were observed.The surface topographies and components were investigated.The quite low friction of the irradiated WC-Ni samples was ascribed to the higher fluid retention capability of the latter and the tribofilm formed during sliding.展开更多
基金Project(KM200710015010) supported by the Scientific Research Program of Beijing Municipal Education Commission,China
文摘Pores,microcracks and density of plasma sprayed Cr2O3 coatings before and after high-intensity pulsed ion beam(HIPIB) irradiation were investigated using the ultrasonic reflection coefficient spectroscopy(URCS).The URCS was analyzed based on an acoustic transmission model for the multi-layered structure.The longitudinal velocity in the coatings was calculated from the experimental URCS,and the attenuation coefficient expression was deduced by comparing the experimental and numerical fitting amplitude spectral lines.The longitudinal velocity of as-sprayed Cr2O3 coating is 2 002 m/s,and increases to 2 099 and 2 148 m/s after being irradiated by HIPIB with 1 and 5 shots.Correspondingly,the factor A changes from 0.046 to 0.026 and 0.020 and n from 1.702 to 1.658 and 1.649 in the attenuation coefficient expression of α=Af n.It is observed that the surface morphology of Cr2O3 coatings changes from rough and porous to smooth and uniform with the increase of shot number,which accords with the ultrasonic analyses reasonably.The URCS seems to provide a convenient and nondestructive method to characterize surface modification of the plasma sprayed coatings.
基金financially supported by both the National Basic Research Program of China(973)(Grant No.2015CB057303)the National Natural Science Foundation of China(Grant No.51275268)
文摘Two types of commercial WC-Ni samples were irradiated with the High-intensity pulsed ion beam(HIPIB).Both the surface characteristics and tribo-characteristics of the non-irradiated and irradiated WC-Ni samples,sliding against graphite under water lubrication,were compared.Quite low steady friction coefficients(approximately of 0.02) of the irradiated WC-Ni were observed.The surface topographies and components were investigated.The quite low friction of the irradiated WC-Ni samples was ascribed to the higher fluid retention capability of the latter and the tribofilm formed during sliding.