The present work aimed at using rare earth lanthanum salt and trimethoxy（viny）silance as chromate substitutes for galvanized steel passivation, in contrast to zinc coating samples treated with chromate.The corrosion...The present work aimed at using rare earth lanthanum salt and trimethoxy（viny）silance as chromate substitutes for galvanized steel passivation, in contrast to zinc coating samples treated with chromate.The corrosion resistance was assessed by electrochemical impedance spectroscopy（EIS） and neutral salt spray tests（NSS）.Scanning electron microscopy（SEM） was used to characterize the sample surfaces.The organic coating adhesion on the panel was also investigated via varnishes-cross cut tests.The results indicated that rare earth and silane two-step treatment gave more effective anticorrosion performance than Cr, which also provided good paint adhesion.The coating formation mechanism was also discussed.展开更多
A complex film on hot-dip galvanized steel sheet（HDG） was prepared by immersing the sheet in 0.1wt.% Ce（NO3）3 solution and 5vol.% silane solution in turn.The corrosion protection of the complex film was evaluated ...A complex film on hot-dip galvanized steel sheet（HDG） was prepared by immersing the sheet in 0.1wt.% Ce（NO3）3 solution and 5vol.% silane solution in turn.The corrosion protection of the complex film was evaluated by potentiodynamic linear polarization（LPR）, electrochemical impendence spectra（EIS） and natural salt spray（NSS） tests and compared with that of single cerium film and silane film.The results showed that, the presence of these films on the zinc coating hindered corrosion reaction by reducing the rate of both anodic and cathodic reaction in the corrosion process, and the corrosion protection of the complex film was much better than that of single cerium film or silane film and closed to that of chromate film, because the polarization resistance Rp and electrochemical impendence were increased markedly.Microstructure and chemical composition of these pretreated films were also investigated by scanning electron microscopy（SEM） and AES.展开更多
文摘The present work aimed at using rare earth lanthanum salt and trimethoxy（viny）silance as chromate substitutes for galvanized steel passivation, in contrast to zinc coating samples treated with chromate.The corrosion resistance was assessed by electrochemical impedance spectroscopy（EIS） and neutral salt spray tests（NSS）.Scanning electron microscopy（SEM） was used to characterize the sample surfaces.The organic coating adhesion on the panel was also investigated via varnishes-cross cut tests.The results indicated that rare earth and silane two-step treatment gave more effective anticorrosion performance than Cr, which also provided good paint adhesion.The coating formation mechanism was also discussed.
基金supported by the United Nations Common Fund for Commodities (CFC/LZSG/12)
文摘A complex film on hot-dip galvanized steel sheet（HDG） was prepared by immersing the sheet in 0.1wt.% Ce（NO3）3 solution and 5vol.% silane solution in turn.The corrosion protection of the complex film was evaluated by potentiodynamic linear polarization（LPR）, electrochemical impendence spectra（EIS） and natural salt spray（NSS） tests and compared with that of single cerium film and silane film.The results showed that, the presence of these films on the zinc coating hindered corrosion reaction by reducing the rate of both anodic and cathodic reaction in the corrosion process, and the corrosion protection of the complex film was much better than that of single cerium film or silane film and closed to that of chromate film, because the polarization resistance Rp and electrochemical impendence were increased markedly.Microstructure and chemical composition of these pretreated films were also investigated by scanning electron microscopy（SEM） and AES.