Spalling and mechanical properties of FRHPC subjected to fire were tested on notched beams. The results confirm that the internal vapor pressure is the leading reason for spalling of high-performance concrete （HPC）....Spalling and mechanical properties of FRHPC subjected to fire were tested on notched beams. The results confirm that the internal vapor pressure is the leading reason for spalling of high-performance concrete （HPC）. At the same time, the temperature-increasing velocity and constrained conditions of concrete element also play significant roles in spalling. Steel fibers cannot reduce the risk of spalling, although they have obvious beneficial effects on the mechanical properties of concrete before and after exposure to fire. Polypropylene （PP） fibers are very useful in preventing HPC from spalling, however, they have negative effects on the strengths. By using hybrid fibers （steel fibers＋PP fibers）, both good anti-spalling performance and improved mechanical properties come true, which may provide necessary safe guarantee for the rescue work and structure repair after fire disaster.展开更多
The objective of this study is to increase the insight into the mechanical behaviors of steel fiber reinforced high-performance concrete （SFHPC） after exposure to high temperatures. Three types of steel fibers were ...The objective of this study is to increase the insight into the mechanical behaviors of steel fiber reinforced high-performance concrete （SFHPC） after exposure to high temperatures. Three types of steel fibers were used and three-point bending tests on notched beams of SFHPC were carried out. The results showed that the flexural toughness and fracture energy of SFHPC increased evidently with the fiber content. The hooked steel fibers with higher strength possess higher flexural toughness and fracture energy than the marked steel fibers with lower strength. After exposure to high temperatures of 300, 600 and 900 ℃ in an electrical furnace, the compressive strength, flexural toughness and fracture energy of SFHPC decreased less than that of HPC without fibers, Both steel fiber content and type had strong influences on the flexural toughness and fracture energy. In addition, the failure patterns of SFHPC beams changed from pull-out of steel fibers at lower temperatures to tensile failure of steel fibers at 900 ℃.展开更多
基金the National Natural Science Foundation of China (No. 50278013)
文摘Spalling and mechanical properties of FRHPC subjected to fire were tested on notched beams. The results confirm that the internal vapor pressure is the leading reason for spalling of high-performance concrete （HPC）. At the same time, the temperature-increasing velocity and constrained conditions of concrete element also play significant roles in spalling. Steel fibers cannot reduce the risk of spalling, although they have obvious beneficial effects on the mechanical properties of concrete before and after exposure to fire. Polypropylene （PP） fibers are very useful in preventing HPC from spalling, however, they have negative effects on the strengths. By using hybrid fibers （steel fibers＋PP fibers）, both good anti-spalling performance and improved mechanical properties come true, which may provide necessary safe guarantee for the rescue work and structure repair after fire disaster.
基金The National Natural Science Foundation of China (No.50278013)
文摘The objective of this study is to increase the insight into the mechanical behaviors of steel fiber reinforced high-performance concrete （SFHPC） after exposure to high temperatures. Three types of steel fibers were used and three-point bending tests on notched beams of SFHPC were carried out. The results showed that the flexural toughness and fracture energy of SFHPC increased evidently with the fiber content. The hooked steel fibers with higher strength possess higher flexural toughness and fracture energy than the marked steel fibers with lower strength. After exposure to high temperatures of 300, 600 and 900 ℃ in an electrical furnace, the compressive strength, flexural toughness and fracture energy of SFHPC decreased less than that of HPC without fibers, Both steel fiber content and type had strong influences on the flexural toughness and fracture energy. In addition, the failure patterns of SFHPC beams changed from pull-out of steel fibers at lower temperatures to tensile failure of steel fibers at 900 ℃.