The effect of Nd addition on the structure, phase transformation and magnetic properties of FePt based alloys was investigated. The results indicated that the transition temperature from ordered FCT to disordered FCC ...The effect of Nd addition on the structure, phase transformation and magnetic properties of FePt based alloys was investigated. The results indicated that the transition temperature from ordered FCT to disordered FCC phase decreased with increasing Nd concentration, but for alloys quenched rapidly from the γ phase region into ice-water, it increased with increasing Nd. The Nd element not only effectively reduced the grain size of the ordered phase but also decreased the degree of the ordered phase and refined the grains of the FCC matrix phase. The remanence ratio and coereivity of the FePt based alloy as a function of the Nd content had maximum values, respectively.展开更多
The structure and disorder-order transformation of NdxFe60.5-x Pt39.5（x = 0, 0.5, 1.0, 1.5） alloys were investigated in situ by high temperature X-ray diffraction. The results show that the lattice parameter a of di...The structure and disorder-order transformation of NdxFe60.5-x Pt39.5（x = 0, 0.5, 1.0, 1.5） alloys were investigated in situ by high temperature X-ray diffraction. The results show that the lattice parameter a of disordered γ phase （FCC, Al structure type） and the lattice parameter ratio c/a of ordered γ1 phase （FCT, L10 structure type） increase linearly with increasing Nd concentration, whereas the c/a ratio decreases with increasing temperature. The transition temperature from ordered FCT to disordered FCC decreases with increasing Nd concentration, but for alloys quenched rapidly from γ phase region into ice-water it increases with increasing Nd.展开更多
The effects of Pr on the structure and magnetic properties of PrxFe60.5-xPt39.5 alloys （x = 0, 0.5, 1.0, and 1.5） were investigated. X-ray diffraction data indicated that the phase transition temperature of FePt bas...The effects of Pr on the structure and magnetic properties of PrxFe60.5-xPt39.5 alloys （x = 0, 0.5, 1.0, and 1.5） were investigated. X-ray diffraction data indicated that the phase transition temperature of FePt based alloys from disordered face-centered-cubic to ordered face-centered-tetragonal cubic decreases with the increase in Pr concentration. Pr plays the role of a grain refiner and it can enhance the exchange coupling between soft magnetic phase and hard magnetic phase. The results indicate that the replacement of Fe by Pr can significantly improve the remanence and coercivity of the Fe60.5Pt39.5 alloy. These results can be explained on the basis of phase transformation and microstructure. Both the remanence ratio and coercivity of the FePt based alloy as a function of the Pr content are increased by the optimum addition of 0.5 at.% Pr.展开更多
基金Project supported by the National Natural Science Foundation of China (50261002 ,10574049)
文摘The effect of Nd addition on the structure, phase transformation and magnetic properties of FePt based alloys was investigated. The results indicated that the transition temperature from ordered FCT to disordered FCC phase decreased with increasing Nd concentration, but for alloys quenched rapidly from the γ phase region into ice-water, it increased with increasing Nd. The Nd element not only effectively reduced the grain size of the ordered phase but also decreased the degree of the ordered phase and refined the grains of the FCC matrix phase. The remanence ratio and coereivity of the FePt based alloy as a function of the Nd content had maximum values, respectively.
文摘The structure and disorder-order transformation of NdxFe60.5-x Pt39.5（x = 0, 0.5, 1.0, 1.5） alloys were investigated in situ by high temperature X-ray diffraction. The results show that the lattice parameter a of disordered γ phase （FCC, Al structure type） and the lattice parameter ratio c/a of ordered γ1 phase （FCT, L10 structure type） increase linearly with increasing Nd concentration, whereas the c/a ratio decreases with increasing temperature. The transition temperature from ordered FCT to disordered FCC decreases with increasing Nd concentration, but for alloys quenched rapidly from γ phase region into ice-water it increases with increasing Nd.
基金This work is financially supported by the National Natural Science Foundation of China (Nos.50261002 and 10574049).
文摘The effects of Pr on the structure and magnetic properties of PrxFe60.5-xPt39.5 alloys （x = 0, 0.5, 1.0, and 1.5） were investigated. X-ray diffraction data indicated that the phase transition temperature of FePt based alloys from disordered face-centered-cubic to ordered face-centered-tetragonal cubic decreases with the increase in Pr concentration. Pr plays the role of a grain refiner and it can enhance the exchange coupling between soft magnetic phase and hard magnetic phase. The results indicate that the replacement of Fe by Pr can significantly improve the remanence and coercivity of the Fe60.5Pt39.5 alloy. These results can be explained on the basis of phase transformation and microstructure. Both the remanence ratio and coercivity of the FePt based alloy as a function of the Pr content are increased by the optimum addition of 0.5 at.% Pr.