The microstructure of a composite coating system, which was composed of an inner layer of Fe-Cr-Al and an outer layer of aluminum, was studied after it was respectively oxidized and sulfurdized at elevated temperature...The microstructure of a composite coating system, which was composed of an inner layer of Fe-Cr-Al and an outer layer of aluminum, was studied after it was respectively oxidized and sulfurdized at elevated temperatures. Apart from the Al2O3 scale formed on the surface, the microstructure of the composite coatings exposed at 900℃ in air for 4h was a three-layer structure. The first layer consisted of a solid solution of Cr and Fe in α aluminum and an intermetallic compound FeAl3 while the second layer was a single phase of the aluminide and the third layer still remained the same appearance as the original Fe-Cr-Al coating. The microstructural observation of the specimen tested at 850-900℃ at low oxygen pressure and high sulfur pressure for 576h revealed that the surface coatings of the specimen had transformed into a duplex structure containing an outer layer and a thicker aluminide layer beneath. X-ray diffraction results showed that the out layer was composed of Al2S3 and Al2O3 and that AlCrFee was the main phase composition of the aluminide layer, with a few of Al2S3 and Al2O3 accompanied.展开更多
A certain amount of Ti was added to the plasma cladding Fe-Cr-C coating in the early stage in order to improve the quality and properties of the coating.Ti-Fe-Cr-C composite powder was prepared by precursor carbonizat...A certain amount of Ti was added to the plasma cladding Fe-Cr-C coating in the early stage in order to improve the quality and properties of the coating.Ti-Fe-Cr-C composite powder was prepared by precursor carbonization-composition process.In situ synthesized TiC-Fe-Cr coatings were fabricated on substrate of Q235 steel by plasma cladding process with the composite powder.Microstructures of the coatings with different process parameters,including cladding current,cladding speed,number of overlapping cladding layers,were analyzed by scanning electron microscope.The results show that the structure of the TiC-Fe-Cr coating is greatly affected by the cladding current,the cladding speed and the overlapping cladding process.In this test,when the cladding current of 300 A and the cladding process parameter of the cladding speed of 50 mm/min are clad with three layers,a well-formed and well-structured TiC-Fe-Cr coating can be obtained in this test.TiC-Fe-Cr coating has good wear resistance and good load characteristics under dry sliding wear test conditions.展开更多
Anti-coking oxide films were prepared on a 25Cr35Ni and 35Cr45Ni alloy surface under the low oxygen partialpressure atmosphere of a H2-H2O mixture. The composition and phase structure of the oxide films were analyzed ...Anti-coking oxide films were prepared on a 25Cr35Ni and 35Cr45Ni alloy surface under the low oxygen partialpressure atmosphere of a H2-H2O mixture. The composition and phase structure of the oxide films were analyzed by energydispersive spectroscopy (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The anti-cokingperformance of a mini tube made of a HP40 (25Cr35Ni) alloy was evaluated on a bench scale pyrolysis and coking test unit.The results showed that the surface Fe and Ni content decreased after the oxidation of the two alloys in a low oxygen partialpressure atmosphere. The oxide films were mainly composed of MnCr_(2)O_(4) and Cr_(2)O_(3). The average mass of coke in the minitube with oxide film decreased by 87% relative to that of a tube without an oxide film when the cracking temperature was 900℃. The ethylene, propylene, and butadiene yields in the pyrolysis tests were almost the same for the mini tubes withand without an oxide film. The oxide film on the alloy surface effectively inhibited catalytic filamentous coke formation.An industrial test showed that the run length of the cracking furnace with the in-situ coating technology was significantlyextended.展开更多
文摘The microstructure of a composite coating system, which was composed of an inner layer of Fe-Cr-Al and an outer layer of aluminum, was studied after it was respectively oxidized and sulfurdized at elevated temperatures. Apart from the Al2O3 scale formed on the surface, the microstructure of the composite coatings exposed at 900℃ in air for 4h was a three-layer structure. The first layer consisted of a solid solution of Cr and Fe in α aluminum and an intermetallic compound FeAl3 while the second layer was a single phase of the aluminide and the third layer still remained the same appearance as the original Fe-Cr-Al coating. The microstructural observation of the specimen tested at 850-900℃ at low oxygen pressure and high sulfur pressure for 576h revealed that the surface coatings of the specimen had transformed into a duplex structure containing an outer layer and a thicker aluminide layer beneath. X-ray diffraction results showed that the out layer was composed of Al2S3 and Al2O3 and that AlCrFee was the main phase composition of the aluminide layer, with a few of Al2S3 and Al2O3 accompanied.
基金National Natural Science Foundation of China (Grant No. 51905382)the Cooperation in Production and Education by Ministry of Education (Grant No. 201802252016)Weifang University Distinguished Professor Support Programme
文摘A certain amount of Ti was added to the plasma cladding Fe-Cr-C coating in the early stage in order to improve the quality and properties of the coating.Ti-Fe-Cr-C composite powder was prepared by precursor carbonization-composition process.In situ synthesized TiC-Fe-Cr coatings were fabricated on substrate of Q235 steel by plasma cladding process with the composite powder.Microstructures of the coatings with different process parameters,including cladding current,cladding speed,number of overlapping cladding layers,were analyzed by scanning electron microscope.The results show that the structure of the TiC-Fe-Cr coating is greatly affected by the cladding current,the cladding speed and the overlapping cladding process.In this test,when the cladding current of 300 A and the cladding process parameter of the cladding speed of 50 mm/min are clad with three layers,a well-formed and well-structured TiC-Fe-Cr coating can be obtained in this test.TiC-Fe-Cr coating has good wear resistance and good load characteristics under dry sliding wear test conditions.
基金the scientific research project of China Petroleum&Chemical Corporation(Grant No.411048).
文摘Anti-coking oxide films were prepared on a 25Cr35Ni and 35Cr45Ni alloy surface under the low oxygen partialpressure atmosphere of a H2-H2O mixture. The composition and phase structure of the oxide films were analyzed by energydispersive spectroscopy (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The anti-cokingperformance of a mini tube made of a HP40 (25Cr35Ni) alloy was evaluated on a bench scale pyrolysis and coking test unit.The results showed that the surface Fe and Ni content decreased after the oxidation of the two alloys in a low oxygen partialpressure atmosphere. The oxide films were mainly composed of MnCr_(2)O_(4) and Cr_(2)O_(3). The average mass of coke in the minitube with oxide film decreased by 87% relative to that of a tube without an oxide film when the cracking temperature was 900℃. The ethylene, propylene, and butadiene yields in the pyrolysis tests were almost the same for the mini tubes withand without an oxide film. The oxide film on the alloy surface effectively inhibited catalytic filamentous coke formation.An industrial test showed that the run length of the cracking furnace with the in-situ coating technology was significantlyextended.
基金"863"Project(2012AA09A203)Nature Science Founding of Shandong Province(Q2008F12)Fundamental Research Funds for the Central Universities(11CX04032A,11CX06069A)