A series of（SiO2/MgO/ID/MgCl2）·TiClx Ziegler-Natta catalysts for propylene polymerization has been prepared with a new method. These catalysts were synthesized using soluble Mg-compounds as the Mg-source and th...A series of（SiO2/MgO/ID/MgCl2）·TiClx Ziegler-Natta catalysts for propylene polymerization has been prepared with a new method. These catalysts were synthesized using soluble Mg-compounds as the Mg-source and the preparation progress was relatively simple. The catalyst could copy the spherical shape of the carrier very well. The propylene polymerization results showed that the catalyst revealed the best activity with 9,9-di（methoxymethyl）fluorene（BMMF） as internal donor at 50 °C with the optimal molar ratio Al/Ti = 5, which was much lower than what the industrial polypropylene catalyst used（at least molar ratio Al/Ti = 100）, resulting in great cost saving. Additionally, the polymerization kinetics of the catalyst exhibited very stable property after achieving a relatively high value. These catalysts possessed rather high activity and good hydrogen response. The isotactic index（Ⅱ.） value of the PP products could be higher than 98% in the presence of both internal and external electron donors. Moreover, temperature rising elution fractionation method was used to understand the influence of donors and H2 on the properties of the PP products.展开更多
The composition distribution (CD) and microisotacticity distribution (ID) of propene/1-hexene copolymer synthesized by MgCl2/DIBP/TiCl4 (DIBP: diisobutyl phthalate) were determined by fractionating the copolymers acco...The composition distribution (CD) and microisotacticity distribution (ID) of propene/1-hexene copolymer synthesized by MgCl2/DIBP/TiCl4 (DIBP: diisobutyl phthalate) were determined by fractionating the copolymers according to crystallinity and characterizing the fractions by (CNMR)-C-13. The effects of two alkoxysilane donors, triethoxyphenylsilane (PTES) and dimethoxydi-tert-butylsilane (TBMS), on CD and ID of the copolymers were compared. Three main parts in the CD diagram of each copolymer were distinguished, which were correlated to active center distribution (ACD) based on three groups of different active centers. By studying the changes in l-hexene content, microisotacticity and reactivity ratio product of three typical fractions, the effects of external donor on ACD were better elucidated. It was found that TBMS shows much stronger effects on ACD than PTES. In the former system, most fractions were produced on active centers with relatively lower r(1)r(2), higher reactivity to I-hexene, and higher stereospecificity as compared to the system without external donor. It is concluded that the observed very extensive changes in ACD are mainly resulted by the formation of new types of active centers, possibly by coordination of external donor to certain positions on the catalyst.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.21406061 and 21674036)the Major State Basic Research Development Program of China(No.2014CB239503)the Fundamental Research Funds for the Central Universities
文摘A series of（SiO2/MgO/ID/MgCl2）·TiClx Ziegler-Natta catalysts for propylene polymerization has been prepared with a new method. These catalysts were synthesized using soluble Mg-compounds as the Mg-source and the preparation progress was relatively simple. The catalyst could copy the spherical shape of the carrier very well. The propylene polymerization results showed that the catalyst revealed the best activity with 9,9-di（methoxymethyl）fluorene（BMMF） as internal donor at 50 °C with the optimal molar ratio Al/Ti = 5, which was much lower than what the industrial polypropylene catalyst used（at least molar ratio Al/Ti = 100）, resulting in great cost saving. Additionally, the polymerization kinetics of the catalyst exhibited very stable property after achieving a relatively high value. These catalysts possessed rather high activity and good hydrogen response. The isotactic index（Ⅱ.） value of the PP products could be higher than 98% in the presence of both internal and external electron donors. Moreover, temperature rising elution fractionation method was used to understand the influence of donors and H2 on the properties of the PP products.
文摘The composition distribution (CD) and microisotacticity distribution (ID) of propene/1-hexene copolymer synthesized by MgCl2/DIBP/TiCl4 (DIBP: diisobutyl phthalate) were determined by fractionating the copolymers according to crystallinity and characterizing the fractions by (CNMR)-C-13. The effects of two alkoxysilane donors, triethoxyphenylsilane (PTES) and dimethoxydi-tert-butylsilane (TBMS), on CD and ID of the copolymers were compared. Three main parts in the CD diagram of each copolymer were distinguished, which were correlated to active center distribution (ACD) based on three groups of different active centers. By studying the changes in l-hexene content, microisotacticity and reactivity ratio product of three typical fractions, the effects of external donor on ACD were better elucidated. It was found that TBMS shows much stronger effects on ACD than PTES. In the former system, most fractions were produced on active centers with relatively lower r(1)r(2), higher reactivity to I-hexene, and higher stereospecificity as compared to the system without external donor. It is concluded that the observed very extensive changes in ACD are mainly resulted by the formation of new types of active centers, possibly by coordination of external donor to certain positions on the catalyst.