Eu 3+ ions were incorporated in sol and gel by a sol gel processing using 3 glycidoxypropyltrimethoxysilane (CH 2OCHCH 2O(CH 2) 3Si(OCH 3) 3, GPTMS) and ethyl silicate (TEOS) as precursors. The basic chem...Eu 3+ ions were incorporated in sol and gel by a sol gel processing using 3 glycidoxypropyltrimethoxysilane (CH 2OCHCH 2O(CH 2) 3Si(OCH 3) 3, GPTMS) and ethyl silicate (TEOS) as precursors. The basic chemical physical properties such as DTA curve, FT IR spectra and specific surface area were recorded. The characteristics of their optical spectra were measured and investigated. The results indicate that the emission intensity of Eu 3+ ion in ormocer is much higher and the global line width is wider than those in SiO 2 gel. The relationship between the composition and structure of gels and the fluorescence intensity and width were discussed. The obtained ormocer shows good mechanical strength, which can be cut and polished in machine without broken.展开更多
The sorption of Eu species onto nano-size silica-water interfaces was investigated using fluorescence spectroscopy for pH ranges of 1-8.5 and an initial Eu concentration (C Eu) of 2×10 -4 M. The sorption rate...The sorption of Eu species onto nano-size silica-water interfaces was investigated using fluorescence spectroscopy for pH ranges of 1-8.5 and an initial Eu concentration (C Eu) of 2×10 -4 M. The sorption rate of Eu was initially low, but significantly increased at pH>4. The sorption density of Eu species on a silica surface was ～1.58×10 -7 mol/m2 when the dissolved Eu species were completely sorbed onto silica-water interfaces at pH=～5.8. The sorbed Eu species at pH<6 is aquo Eu 3+, which is sorbed onto silica-water interfaces as an outer-sphere complex at pH<5, but may be sorbed as an inner-sphere bidentate complex at 5<pH<6, due to the decrease of N H 2O to ～6 at pH=6. At pH=6-8.5, Eu(OH)+ 2, Eu(CO 3)+ and Eu(CO 3)- 2 formed in the solutions, and Eu(CO 3)+ is dominant at pH=～7.5. These ions may be sorbed onto silica-water interfaces as inner-sphere bidentate complexes.展开更多
In this paper, using calcium chloride and sodium molybdate as raw material, polyethylene glycol (PEG2000) as surfactant, the nanocomposites of CaMoO4: Eu3+ were prepared by a direct feeding microwave synthesis method....In this paper, using calcium chloride and sodium molybdate as raw material, polyethylene glycol (PEG2000) as surfactant, the nanocomposites of CaMoO4: Eu3+ were prepared by a direct feeding microwave synthesis method. The as-prepared sample was characterized by X-ray diffraction (XRD), scanning electron micrograph (SEM) and photoluminescence spectrum (PL). The XRD Pattern showed that the samples are scheelite structure of CaMoO4. The SEM image showed that the majority of as-prepared sample is a relatively flake structure, and some fine particles attached to it. PL spectra showed that as-prepared samples have strong luminescence properties;it had purity red emission at 615 nm. The effects of different Eu3+ ions doping amount and surface active agent on the photoluminescence properties were studied. The results showed that when the molar ratio of Eu3+ was 0.10, PEG2000 as surfactant, the luminescence intensity of as-prepared sample was maximum.展开更多
By using an Ar+ ion laser, a tunable Rh 6G dye laser(Linewidth: 0.5 cm -1) and a Coherent 899-21 dye laser as light sources and using a monochromator and a phase-locking amplifier, the optical properties of Eu 3+∶Y_2...By using an Ar+ ion laser, a tunable Rh 6G dye laser(Linewidth: 0.5 cm -1) and a Coherent 899-21 dye laser as light sources and using a monochromator and a phase-locking amplifier, the optical properties of Eu 3+∶Y_2SiO_5 crystal were detected. Persistent spectral hole burning (PSHB) were also observed in 5D_0-7F_0 transition in the crystal at the temperature of 16 K. For 15 mW dye laser (Wavelength: 579.62 nm) burning the crystal for 0.1 s a spectral hole with about 80 MHz hole width were detected and the hole can been keep for longer than 10 h.展开更多
A series of novel luminescent materials, SrZnO2:M (M=Eu3+, or Eu3+ + Li+) have been synthesized by high-temperature solid-state reaction. The structure and luminescence properties of SrZnO2:Eu3+ phosphor were studied ...A series of novel luminescent materials, SrZnO2:M (M=Eu3+, or Eu3+ + Li+) have been synthesized by high-temperature solid-state reaction. The structure and luminescence properties of SrZnO2:Eu3+ phosphor were studied through XRD, photoluminescence and Raman spectroscopy. The excitation spectra show a broad intense band and a number of small peaks corresponding to the inner 4f-shell excitations of Eu3+ (the strongest one is at 395 nm for 7F0-5L6). After SrZnO2:Eu3+ phosphor was co-doped with Li+ ions, its charge transfer band extended to longer wavelengths. This resulted in increase of luminescent quantum efficiency of the sample. SrZnO2:Eu3+,Li+ phosphor can be efficiently excited by longer UV. From the fluorescence spectrum of SrZnO2:Eu3+ phosphor, apart from transition emissions of 5D0 → 7FJ (J=0~4), the transition emissions from 5D1 → 7FJ (J=0~2) have been observed. For the SrZnO2:Eu3+ phosphor, under excitation of UV, the dominant emission is at about 612 nm, due to the 5D0 → 7F2 hypersensitive transition. The incorporation of Li+ ions greatly enhanced the luminescence intensity and made emission peak from 5D0 → 7F2 transition red-shifted.展开更多
文摘Eu 3+ ions were incorporated in sol and gel by a sol gel processing using 3 glycidoxypropyltrimethoxysilane (CH 2OCHCH 2O(CH 2) 3Si(OCH 3) 3, GPTMS) and ethyl silicate (TEOS) as precursors. The basic chemical physical properties such as DTA curve, FT IR spectra and specific surface area were recorded. The characteristics of their optical spectra were measured and investigated. The results indicate that the emission intensity of Eu 3+ ion in ormocer is much higher and the global line width is wider than those in SiO 2 gel. The relationship between the composition and structure of gels and the fluorescence intensity and width were discussed. The obtained ormocer shows good mechanical strength, which can be cut and polished in machine without broken.
文摘The sorption of Eu species onto nano-size silica-water interfaces was investigated using fluorescence spectroscopy for pH ranges of 1-8.5 and an initial Eu concentration (C Eu) of 2×10 -4 M. The sorption rate of Eu was initially low, but significantly increased at pH>4. The sorption density of Eu species on a silica surface was ～1.58×10 -7 mol/m2 when the dissolved Eu species were completely sorbed onto silica-water interfaces at pH=～5.8. The sorbed Eu species at pH<6 is aquo Eu 3+, which is sorbed onto silica-water interfaces as an outer-sphere complex at pH<5, but may be sorbed as an inner-sphere bidentate complex at 5<pH<6, due to the decrease of N H 2O to ～6 at pH=6. At pH=6-8.5, Eu(OH)+ 2, Eu(CO 3)+ and Eu(CO 3)- 2 formed in the solutions, and Eu(CO 3)+ is dominant at pH=～7.5. These ions may be sorbed onto silica-water interfaces as inner-sphere bidentate complexes.
文摘In this paper, using calcium chloride and sodium molybdate as raw material, polyethylene glycol (PEG2000) as surfactant, the nanocomposites of CaMoO4: Eu3+ were prepared by a direct feeding microwave synthesis method. The as-prepared sample was characterized by X-ray diffraction (XRD), scanning electron micrograph (SEM) and photoluminescence spectrum (PL). The XRD Pattern showed that the samples are scheelite structure of CaMoO4. The SEM image showed that the majority of as-prepared sample is a relatively flake structure, and some fine particles attached to it. PL spectra showed that as-prepared samples have strong luminescence properties;it had purity red emission at 615 nm. The effects of different Eu3+ ions doping amount and surface active agent on the photoluminescence properties were studied. The results showed that when the molar ratio of Eu3+ was 0.10, PEG2000 as surfactant, the luminescence intensity of as-prepared sample was maximum.
文摘By using an Ar+ ion laser, a tunable Rh 6G dye laser(Linewidth: 0.5 cm -1) and a Coherent 899-21 dye laser as light sources and using a monochromator and a phase-locking amplifier, the optical properties of Eu 3+∶Y_2SiO_5 crystal were detected. Persistent spectral hole burning (PSHB) were also observed in 5D_0-7F_0 transition in the crystal at the temperature of 16 K. For 15 mW dye laser (Wavelength: 579.62 nm) burning the crystal for 0.1 s a spectral hole with about 80 MHz hole width were detected and the hole can been keep for longer than 10 h.
文摘A series of novel luminescent materials, SrZnO2:M (M=Eu3+, or Eu3+ + Li+) have been synthesized by high-temperature solid-state reaction. The structure and luminescence properties of SrZnO2:Eu3+ phosphor were studied through XRD, photoluminescence and Raman spectroscopy. The excitation spectra show a broad intense band and a number of small peaks corresponding to the inner 4f-shell excitations of Eu3+ (the strongest one is at 395 nm for 7F0-5L6). After SrZnO2:Eu3+ phosphor was co-doped with Li+ ions, its charge transfer band extended to longer wavelengths. This resulted in increase of luminescent quantum efficiency of the sample. SrZnO2:Eu3+,Li+ phosphor can be efficiently excited by longer UV. From the fluorescence spectrum of SrZnO2:Eu3+ phosphor, apart from transition emissions of 5D0 → 7FJ (J=0~4), the transition emissions from 5D1 → 7FJ (J=0~2) have been observed. For the SrZnO2:Eu3+ phosphor, under excitation of UV, the dominant emission is at about 612 nm, due to the 5D0 → 7F2 hypersensitive transition. The incorporation of Li+ ions greatly enhanced the luminescence intensity and made emission peak from 5D0 → 7F2 transition red-shifted.