AA2219 aluminium alloy square butt joints without filler metal addition were fabricated using gas tungsten arc welding （GTAW）, electron beam welding （EBW） and friction stir welding （FSW） processes. The effects o...AA2219 aluminium alloy square butt joints without filler metal addition were fabricated using gas tungsten arc welding （GTAW）, electron beam welding （EBW） and friction stir welding （FSW） processes. The effects of three welding processes on the tensile, fatigue and corrosion behaviour were studied. Microstructure analysis was carried out using optical and electron microscopes. The results show that the FSW joints exhibit superior tensile and fatigue properties compared to EBW and GTAW joints. It is also found that the friction stir welds show lower corrosion resistance than EB and GTA welds. This is mainly due to the presence of finer grains and uniform distribution of strengthening precipitates in the weld metal of FSW joints.展开更多
Titanium alloys have been successfully applied for aerospace, ship and chemical industries because they possess many good characteristics such as high specific strength, superior corrosion resistance and excellent hig...Titanium alloys have been successfully applied for aerospace, ship and chemical industries because they possess many good characteristics such as high specific strength, superior corrosion resistance and excellent high temperature resistance. Though these alloys show reasonable weldability characteristics, the joint properties are greatly influenced by the welding processes. Weld thermal cycle of the processes will control the weld metal solidification and subsequent phase transformation and resultant microstructure. The welded joints of Ti-6Al-4V alloy were fabricated by gas tungsten arc welding （GTAW）, laser beam welding （LBW） and electron beam welding （EBW） processes. The joints fabricated by EBW process exhibit higher strength compared with the GTAW and LBW joints; but the joints by GTAW process exhibit higher impact toughness compared with the LBW and EBW joints. The resultant tensile and impact properties of the welded joints were correlated with the weld metal microstructures.展开更多
Microstructure features of 12 MnNiVR pressure vessel steel welded joint deposited by the high heat input electrogas welding have been systematically investigated. It is revealed that the welded joint is featured by a ...Microstructure features of 12 MnNiVR pressure vessel steel welded joint deposited by the high heat input electrogas welding have been systematically investigated. It is revealed that the welded joint is featured by a heterogeneous juxtaposition. The coarse grained heat-affected zone(CGHAZ) primarily consists of lath bainites and minor granular bainites. The fine grained heat-affected zone(FGHAZ) is dominated by polygonal ferrites, pearlites, and fine cementite particles. Moreover, electron backscatter diffraction results further demonstrate that the CGHAZ is populated by coarse prior austenite grains(PAGs) with high frequency(61.3%) of low angle grain boundaries(LAGBs). On the other hand, the FGHAZ is filled with fine PAGs with a lower frequency(19.6%) of LAGBs. Such microstructural differences may likely contribute to differed mechanical properties for samples tested at designed positions.展开更多
NiTi/Stainless Steel(SS) sheets have been welded via a vacuum electron beam welding process, with three methods(offsetting electron beam to SS side without interlayer, adding Ni interlayer and adding Fe Ni interlayer)...NiTi/Stainless Steel(SS) sheets have been welded via a vacuum electron beam welding process, with three methods(offsetting electron beam to SS side without interlayer, adding Ni interlayer and adding Fe Ni interlayer), to promote mechanical properties of the Ni Ti/SS joints. The joints with different interlayers are all fractured in the weld zone near the Ni Ti side, which is attributed to the enrichment of intermetallic compounds including Fe2 Ti and Ni3 Ti. The fracture mechanisms of different joints are strongly dependent on the types of interlayers, and the joints without interlayer, adding Ni interlayer and adding Fe Ni interlayer exhibit cleavage fracture, intergranular fracture and mixed fracture composed of cleavage and tearing ridge, respectively. Compared with the brittle laves phase Fe2 Ti, Ni3 Ti phase can exhibit certain plasticity, block the crack propagation and change the direction of crack propagation. The composite structure of Ni3 Ti and Fe2 Ti will be formed when the Fe Ni alloy is taken as the interlayer, which provides the joint excellent mechanical properties, with rupture strength of 343 MPa.展开更多
Electron beam welding of Ti-15-3 alloy to 304 stainless steel （STS） using a copper filler metal was carried out. The temperature fields and stress distributions in the Ti/Fe and Ti/Cu/Fe joint during the welding pro...Electron beam welding of Ti-15-3 alloy to 304 stainless steel （STS） using a copper filler metal was carried out. The temperature fields and stress distributions in the Ti/Fe and Ti/Cu/Fe joint during the welding process were numerically simulated and experimentally measured. The results show that the rotated parabola body heat source is fit for the simulation of the electron beam welding. The temperature distribution is asymmetric along the weld center and the temperature in the titanium alloy plate is higher than that in the 304 STS plate. The thermal stress also appears to be in asymmetric distribution. The residual tensile stress mainly exists in the weld at the 304 STS side. The copper filler metal decreases the peak temperature and temperature grade in the joint as well as the residual stress. The longitudinal and lateral residual tensile strengths reduce by 66 MPa and 31 MPa, respectively. From the temperature and residual stress, it is concluded that copper is a good filler metal candidate for the electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel.展开更多
Electron beam welding experiments of titanium alloy to stainless steel were carried out with different filler metals, such as Ni, V, and Cu. Microstructures of the joints were examined by optical microscopy, scanning ...Electron beam welding experiments of titanium alloy to stainless steel were carried out with different filler metals, such as Ni, V, and Cu. Microstructures of the joints were examined by optical microscopy, scanning electron microscopy and X-ray diffraction analysis. Mechanical properties of the joints were evaluated according to tensile strength and microhardness. As a result, influences of filler metals on microstructures and mechanical properties of electron beam welded titanium-stainless steel joints were discussed. The results showed that all the filler metals were helpful to restrain the Ti-Fe intermetallics. The welds with different filler metals were all characterized by solid solution and interfacial intermetallics. For each type of the filler metal, the type of solid solution and interfacial intermetallics depended on the metallurgical reactions between the filler metals and base metals. The interfacial intermetallics were Fe2Ti＋Ni3Ti＋NiTi2, TiFe, and Cu2Ti＋CuTi＋CuTi2 in the joints welded with Ni, V, and Cu filler metals, respectively. The tensile strengths of the joints were dependent on the hardness of the interfacial intermetallics. The joint welded with Ag filler metal had the highest tensile strength, which is about 310 MPa.展开更多
In order to estimate the residual stresses in Ti2AlNb alloy jointed by electron beam welding (EBW), a computational approach based on finite element method was developed. Meanwhile, experiments were carried out to ver...In order to estimate the residual stresses in Ti2AlNb alloy jointed by electron beam welding (EBW), a computational approach based on finite element method was developed. Meanwhile, experiments were carried out to verify the numerical results. The comparison between the simulation results and measurements suggests that the developed computational approach has sufficient accuracy to predict the welding residual stress distributions. The results show that the central area of the fusion zone suffers tensile stresses in three directions. When the other parameters remain unchanged, the focus current has great impact on the weld shape and size, and then affects the residual stress level significantly. Moreover, the thick plate full-penetrated EBW weld suffers near 1000 MPa tensile stress of Z-direction in the center of the fusion zone. The wider weld has lower tensile stress in Z-direction, resulting in lower risk for cracking.展开更多
In order to clarify the characteristics and formation mechanism of the reheat cracking in Ti2AlNb weldments,a series of heat treatment conditions were performed to the circular joints welded by electron beam,and then ...In order to clarify the characteristics and formation mechanism of the reheat cracking in Ti2AlNb weldments,a series of heat treatment conditions were performed to the circular joints welded by electron beam,and then the macrostructures and microstructures were investigated using optical microscopy,scanning electron microscopy,X-ray diffractometry,and transmission electron microscopy.The results show that the reheat cracking occurs primarily along the grain boundaries in the weld when the Ti2AlNb circular welded joints are heated up to about 700℃.During the heat treatment,an almost complete transformation of B2→O happens while the temperature goes up through the O single-phase region.Then,O→B2+O phase transformation occurs primarily along the grain boundaries as the weld metal continues to heat up to the B2+O dual-phase region.Under the high tension stress consisting of welding residual stress and phase transformation stress,reheat cracking occurs at the interface between the B2+O dual-phase layer and the O-phase matrix.展开更多
Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy...Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy(SEM) and X-ray diffractometry(XRD).In addition,the mechanical properties of the joint were evaluated by tensile test and the microhardness was measured.These two alloys were successfully welded by adding copper transition layer into the weld.Solid solution with a certain thickness was located at the interfaces between weld and base metal in both sides.Regions inside the weld and near the stainless steel were characterized by solid solution of copper with TiFe2 intermetallics dispersedly distributed in it.While weld near titanium alloy contained Ti-Cu and Ti-Fe-Cu intermetallics layer,in which the hardness of weld came to the highest value.Brittle fracture occurred in the intermetallics layer when the joint was stretched.展开更多
The microstructure, phase composition and cold shut defect of thick titanium alloy electron beam welded joint were studied. The results showed that the microstructure of weld zone was composed of α′ phase; the heat ...The microstructure, phase composition and cold shut defect of thick titanium alloy electron beam welded joint were studied. The results showed that the microstructure of weld zone was composed of α′ phase; the heat affected zone was divided into fine-grained zone and coarse-grained zone, the microstructure of fine-grained zone was primary α phase ＋ β phase ＋ equiaxed α phase, and the microstructure of coarse-grained zone was primary α phase ＋ acicular α′ phase; the microstructure of base metal zone basically consisted of primary α phase, and a small amount of residual β phase sprinkled. The forming. reason of cold shut was analyzed, and the precaution of cold shut was proposed.展开更多
Effects of welding parameters on the microstructure and mechanical properties of Ti/Cu/Ni joint welded by electron beam were investigated.High welding heat input increased the melting quantity of Ti60 titanium alloy a...Effects of welding parameters on the microstructure and mechanical properties of Ti/Cu/Ni joint welded by electron beam were investigated.High welding heat input increased the melting quantity of Ti60 titanium alloy and promoted the formation of Ti-Cu intermetallic compounds(IMC)such as Ti_(2)Cu and Ti_(3)Cu_(4),increasing the brittleness of the joints.Low welding heat input was not conducive to the complete melting of the copper interlayer,and the unmelted copper reduced the performance of the joints.Under the optimal welding parameters,Ti-Ni IMCs in the weld would be replaced by(Cu,Ni)solid solutions((Cu,Ni)_(ss)).However,Ti-Cu IMC layers cannot be eliminated entirely by changing the welding parameters.The maximum tensile strength of the joints was 201 MPa.The fracture of the joints occurred at the Ti-Cu IMC layer,which was a typical brittle fracture.展开更多
Based on the binary alloy phase diagram of Re-Ti, the weldability of Re and BT5-1 titanium alloy was analyzed. Using two methods of direct electron beam welding （EBW-D） and intergradafion electron beam welding （EB...Based on the binary alloy phase diagram of Re-Ti, the weldability of Re and BT5-1 titanium alloy was analyzed. Using two methods of direct electron beam welding （EBW-D） and intergradafion electron beam welding （EBW-I）, Re and BT5-1 was welded. Experimental results show that the joint figuration of EBW-D between Re and BT5-1 is not fine, and the joint is inclined to brittleness rupture. The joint figuration of EBW-I between Re and BT5-1 is fine. No cracking and other disfigures occur in the intergradation joint. The element distribution of Re, Me, and Ti in the weld metal is progressional diversification.展开更多
Electron beam welding was carried out between aluminum alloy and steel with Ag interlayer. Seam morphology, structure and mechanical properties of the joints were investigated with different action positions of the el...Electron beam welding was carried out between aluminum alloy and steel with Ag interlayer. Seam morphology, structure and mechanical properties of the joints were investigated with different action positions of the electron beam spot. The results show that with the increment of the beam offset to the silver side from the interface between silver and steel, the seam morphology was improved, and the porosity in the Ag interlayer vanished. A transition layer mainly composed of Ag2Al and Al eutectic was formed at the interface between silver and aluminum, and became thin and spiccato as the beam offset increased. When the beam offset was too large, two IMC layers composed of FeAl and FeAl3 respectively were formed at the interface between steel and Ag interlayer. The optimal beam offset was 0.2 mm, and the maximum tensile strength of the joint was 193 MPa, 88.9% that of the aluminum alloy, and the fracture occurred at the interface between steel and Ag interlayer.展开更多
A two-dimensional mathematical model based on volume-of-fluid method is proposed to investigate the heat transfer,fluidflow and keyhole dynamics during electron beam welding(EBW)on20mm-thick2219aluminum alloy plate.In...A two-dimensional mathematical model based on volume-of-fluid method is proposed to investigate the heat transfer,fluidflow and keyhole dynamics during electron beam welding(EBW)on20mm-thick2219aluminum alloy plate.In the model,anadaptive heat source model tracking keyhole depth is employed to simulate the heating process of electron beam.Heat and masstransport of different vortexes induced by surface tension,thermo-capillary force,recoil pressure,hydrostatic pressure and thermalbuoyancy is coupled with keyhole evolution.A series of physical phenomena involving keyhole drilling,collapse,reopening,quasi-stability,backfilling and the coupled thermal field are analyzed systematically.The results indicate that the decreased heat fluxof beam in depth can decelerate the keyholing velocity of recoil pressure and promote the quasi-steady state.Before and close to thisstate,the keyhole collapses and complicates the fluid transport of vortexes.Finally,all simulation results are validated againstexperiments.展开更多
Electron beam welding （EBW） of 304 stainless steel to QCr0.8 copper alloy with copper filler wire was carried out. Orthogonal experiment was performed to investigate the effects of process parameters on the tensile ...Electron beam welding （EBW） of 304 stainless steel to QCr0.8 copper alloy with copper filler wire was carried out. Orthogonal experiment was performed to investigate the effects of process parameters on the tensile strength of the joints, and the process parameters were optimized. The optimum process parameters are as follows：beam current of 30 mA, welding speed of 100 mm/min, wire feed rate of 1 m/min and beam offset of-0.3 mm. The microstructures of the optimum joint were studied. The results indicate that the weld is mainly composed of dendriticαphase with little globularεphase, and copper inhomogeneity only occurs at the top of the fusion zone. In addition, a melted region without mixing exists near the weld junction of copper side. This region with a coarser grain size is the weakest section of the joints. It is found that the microhardness of the weld decreases with the increase of the copper content in solid solution. The highest tensile strength of the joint is 276 MPa.展开更多
基金Project DRAO/08/1061356/M1 supported by Aeronautical Research & Development Board (ARDB),New Delhi,India
文摘AA2219 aluminium alloy square butt joints without filler metal addition were fabricated using gas tungsten arc welding （GTAW）, electron beam welding （EBW） and friction stir welding （FSW） processes. The effects of three welding processes on the tensile, fatigue and corrosion behaviour were studied. Microstructure analysis was carried out using optical and electron microscopes. The results show that the FSW joints exhibit superior tensile and fatigue properties compared to EBW and GTAW joints. It is also found that the friction stir welds show lower corrosion resistance than EB and GTA welds. This is mainly due to the presence of finer grains and uniform distribution of strengthening precipitates in the weld metal of FSW joints.
基金the Combat Vehicle Research and Development Establishment(CVRDE),Avadi,Chennai,Government of India for providing financial support to carry out this investigation through a Contract Acquisition for Research Services project,No.CVRDE/MMG/09-10/0043/CARS
文摘Titanium alloys have been successfully applied for aerospace, ship and chemical industries because they possess many good characteristics such as high specific strength, superior corrosion resistance and excellent high temperature resistance. Though these alloys show reasonable weldability characteristics, the joint properties are greatly influenced by the welding processes. Weld thermal cycle of the processes will control the weld metal solidification and subsequent phase transformation and resultant microstructure. The welded joints of Ti-6Al-4V alloy were fabricated by gas tungsten arc welding （GTAW）, laser beam welding （LBW） and electron beam welding （EBW） processes. The joints fabricated by EBW process exhibit higher strength compared with the GTAW and LBW joints; but the joints by GTAW process exhibit higher impact toughness compared with the LBW and EBW joints. The resultant tensile and impact properties of the welded joints were correlated with the weld metal microstructures.
基金financially supported by the National Natural Science Foundation of China (Nos. 51622401, 51628402, 51861145312 and 51861130361)the National Key Research and Development Program of China (2016YFB0300602)+3 种基金the Research Fund for Central Universities (No. N172502004)State Key Laboratory of Solidification Processing, Northwestern Polytechnical University (No. SKLSP201805)the Global Talents Recruitment Program endowed by the Chinese Governmentsupport from Jiangyin Xingcheng Special Steel Works Co., Ltd.
文摘Microstructure features of 12 MnNiVR pressure vessel steel welded joint deposited by the high heat input electrogas welding have been systematically investigated. It is revealed that the welded joint is featured by a heterogeneous juxtaposition. The coarse grained heat-affected zone(CGHAZ) primarily consists of lath bainites and minor granular bainites. The fine grained heat-affected zone(FGHAZ) is dominated by polygonal ferrites, pearlites, and fine cementite particles. Moreover, electron backscatter diffraction results further demonstrate that the CGHAZ is populated by coarse prior austenite grains(PAGs) with high frequency(61.3%) of low angle grain boundaries(LAGBs). On the other hand, the FGHAZ is filled with fine PAGs with a lower frequency(19.6%) of LAGBs. Such microstructural differences may likely contribute to differed mechanical properties for samples tested at designed positions.
文摘NiTi/Stainless Steel(SS) sheets have been welded via a vacuum electron beam welding process, with three methods(offsetting electron beam to SS side without interlayer, adding Ni interlayer and adding Fe Ni interlayer), to promote mechanical properties of the Ni Ti/SS joints. The joints with different interlayers are all fractured in the weld zone near the Ni Ti side, which is attributed to the enrichment of intermetallic compounds including Fe2 Ti and Ni3 Ti. The fracture mechanisms of different joints are strongly dependent on the types of interlayers, and the joints without interlayer, adding Ni interlayer and adding Fe Ni interlayer exhibit cleavage fracture, intergranular fracture and mixed fracture composed of cleavage and tearing ridge, respectively. Compared with the brittle laves phase Fe2 Ti, Ni3 Ti phase can exhibit certain plasticity, block the crack propagation and change the direction of crack propagation. The composite structure of Ni3 Ti and Fe2 Ti will be formed when the Fe Ni alloy is taken as the interlayer, which provides the joint excellent mechanical properties, with rupture strength of 343 MPa.
基金Foundation item:Project (2010CB731704) supported by the National Basic Research Program of ChinaProject (51075189) supported by the National Natural Science Foundation of China
文摘Electron beam welding of Ti-15-3 alloy to 304 stainless steel （STS） using a copper filler metal was carried out. The temperature fields and stress distributions in the Ti/Fe and Ti/Cu/Fe joint during the welding process were numerically simulated and experimentally measured. The results show that the rotated parabola body heat source is fit for the simulation of the electron beam welding. The temperature distribution is asymmetric along the weld center and the temperature in the titanium alloy plate is higher than that in the 304 STS plate. The thermal stress also appears to be in asymmetric distribution. The residual tensile stress mainly exists in the weld at the 304 STS side. The copper filler metal decreases the peak temperature and temperature grade in the joint as well as the residual stress. The longitudinal and lateral residual tensile strengths reduce by 66 MPa and 31 MPa, respectively. From the temperature and residual stress, it is concluded that copper is a good filler metal candidate for the electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel.
基金Project(2011DFR50760)supported by International Science&Technology Cooperation Program of China
文摘Electron beam welding experiments of titanium alloy to stainless steel were carried out with different filler metals, such as Ni, V, and Cu. Microstructures of the joints were examined by optical microscopy, scanning electron microscopy and X-ray diffraction analysis. Mechanical properties of the joints were evaluated according to tensile strength and microhardness. As a result, influences of filler metals on microstructures and mechanical properties of electron beam welded titanium-stainless steel joints were discussed. The results showed that all the filler metals were helpful to restrain the Ti-Fe intermetallics. The welds with different filler metals were all characterized by solid solution and interfacial intermetallics. For each type of the filler metal, the type of solid solution and interfacial intermetallics depended on the metallurgical reactions between the filler metals and base metals. The interfacial intermetallics were Fe2Ti＋Ni3Ti＋NiTi2, TiFe, and Cu2Ti＋CuTi＋CuTi2 in the joints welded with Ni, V, and Cu filler metals, respectively. The tensile strengths of the joints were dependent on the hardness of the interfacial intermetallics. The joint welded with Ag filler metal had the highest tensile strength, which is about 310 MPa.
基金Project(CALT201309)supported by Joint Innovation Fund for China Academy of Launch Vehicle Technology and Colleges
文摘In order to estimate the residual stresses in Ti2AlNb alloy jointed by electron beam welding (EBW), a computational approach based on finite element method was developed. Meanwhile, experiments were carried out to verify the numerical results. The comparison between the simulation results and measurements suggests that the developed computational approach has sufficient accuracy to predict the welding residual stress distributions. The results show that the central area of the fusion zone suffers tensile stresses in three directions. When the other parameters remain unchanged, the focus current has great impact on the weld shape and size, and then affects the residual stress level significantly. Moreover, the thick plate full-penetrated EBW weld suffers near 1000 MPa tensile stress of Z-direction in the center of the fusion zone. The wider weld has lower tensile stress in Z-direction, resulting in lower risk for cracking.
基金financially supported by the National Natural Science Foundation of China(No.51365014)the Industrial Support Key Project of Jiangxi Province,China(No.20161BBE50072)
文摘In order to clarify the characteristics and formation mechanism of the reheat cracking in Ti2AlNb weldments,a series of heat treatment conditions were performed to the circular joints welded by electron beam,and then the macrostructures and microstructures were investigated using optical microscopy,scanning electron microscopy,X-ray diffractometry,and transmission electron microscopy.The results show that the reheat cracking occurs primarily along the grain boundaries in the weld when the Ti2AlNb circular welded joints are heated up to about 700℃.During the heat treatment,an almost complete transformation of B2→O happens while the temperature goes up through the O single-phase region.Then,O→B2+O phase transformation occurs primarily along the grain boundaries as the weld metal continues to heat up to the B2+O dual-phase region.Under the high tension stress consisting of welding residual stress and phase transformation stress,reheat cracking occurs at the interface between the B2+O dual-phase layer and the O-phase matrix.
文摘Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy(SEM) and X-ray diffractometry(XRD).In addition,the mechanical properties of the joint were evaluated by tensile test and the microhardness was measured.These two alloys were successfully welded by adding copper transition layer into the weld.Solid solution with a certain thickness was located at the interfaces between weld and base metal in both sides.Regions inside the weld and near the stainless steel were characterized by solid solution of copper with TiFe2 intermetallics dispersedly distributed in it.While weld near titanium alloy contained Ti-Cu and Ti-Fe-Cu intermetallics layer,in which the hardness of weld came to the highest value.Brittle fracture occurred in the intermetallics layer when the joint was stretched.
基金Project (2010CB731704) supported by the National Basic Research Program of China
文摘The microstructure, phase composition and cold shut defect of thick titanium alloy electron beam welded joint were studied. The results showed that the microstructure of weld zone was composed of α′ phase; the heat affected zone was divided into fine-grained zone and coarse-grained zone, the microstructure of fine-grained zone was primary α phase ＋ β phase ＋ equiaxed α phase, and the microstructure of coarse-grained zone was primary α phase ＋ acicular α′ phase; the microstructure of base metal zone basically consisted of primary α phase, and a small amount of residual β phase sprinkled. The forming. reason of cold shut was analyzed, and the precaution of cold shut was proposed.
基金supported by Shandong Provincial Key Research and Development Program of China(2019JZZY010439)。
文摘Effects of welding parameters on the microstructure and mechanical properties of Ti/Cu/Ni joint welded by electron beam were investigated.High welding heat input increased the melting quantity of Ti60 titanium alloy and promoted the formation of Ti-Cu intermetallic compounds(IMC)such as Ti_(2)Cu and Ti_(3)Cu_(4),increasing the brittleness of the joints.Low welding heat input was not conducive to the complete melting of the copper interlayer,and the unmelted copper reduced the performance of the joints.Under the optimal welding parameters,Ti-Ni IMCs in the weld would be replaced by(Cu,Ni)solid solutions((Cu,Ni)_(ss)).However,Ti-Cu IMC layers cannot be eliminated entirely by changing the welding parameters.The maximum tensile strength of the joints was 201 MPa.The fracture of the joints occurred at the Ti-Cu IMC layer,which was a typical brittle fracture.
文摘Based on the binary alloy phase diagram of Re-Ti, the weldability of Re and BT5-1 titanium alloy was analyzed. Using two methods of direct electron beam welding （EBW-D） and intergradafion electron beam welding （EBW-I）, Re and BT5-1 was welded. Experimental results show that the joint figuration of EBW-D between Re and BT5-1 is not fine, and the joint is inclined to brittleness rupture. The joint figuration of EBW-I between Re and BT5-1 is fine. No cracking and other disfigures occur in the intergradation joint. The element distribution of Re, Me, and Ti in the weld metal is progressional diversification.
基金Project (2010CB731704) supported by the National Basic Research Program of ChinaProject (51075089) supported by the National Natural Science Foundation of china
文摘Electron beam welding was carried out between aluminum alloy and steel with Ag interlayer. Seam morphology, structure and mechanical properties of the joints were investigated with different action positions of the electron beam spot. The results show that with the increment of the beam offset to the silver side from the interface between silver and steel, the seam morphology was improved, and the porosity in the Ag interlayer vanished. A transition layer mainly composed of Ag2Al and Al eutectic was formed at the interface between silver and aluminum, and became thin and spiccato as the beam offset increased. When the beam offset was too large, two IMC layers composed of FeAl and FeAl3 respectively were formed at the interface between steel and Ag interlayer. The optimal beam offset was 0.2 mm, and the maximum tensile strength of the joint was 193 MPa, 88.9% that of the aluminum alloy, and the fracture occurred at the interface between steel and Ag interlayer.
文摘A two-dimensional mathematical model based on volume-of-fluid method is proposed to investigate the heat transfer,fluidflow and keyhole dynamics during electron beam welding(EBW)on20mm-thick2219aluminum alloy plate.In the model,anadaptive heat source model tracking keyhole depth is employed to simulate the heating process of electron beam.Heat and masstransport of different vortexes induced by surface tension,thermo-capillary force,recoil pressure,hydrostatic pressure and thermalbuoyancy is coupled with keyhole evolution.A series of physical phenomena involving keyhole drilling,collapse,reopening,quasi-stability,backfilling and the coupled thermal field are analyzed systematically.The results indicate that the decreased heat fluxof beam in depth can decelerate the keyholing velocity of recoil pressure and promote the quasi-steady state.Before and close to thisstate,the keyhole collapses and complicates the fluid transport of vortexes.Finally,all simulation results are validated againstexperiments.
基金Project(2010CB731704)supported by the National Basic Research Program of ChinaProject(2011DFR50760)supported by International Science&Technology Cooperation Program of China
文摘Electron beam welding （EBW） of 304 stainless steel to QCr0.8 copper alloy with copper filler wire was carried out. Orthogonal experiment was performed to investigate the effects of process parameters on the tensile strength of the joints, and the process parameters were optimized. The optimum process parameters are as follows：beam current of 30 mA, welding speed of 100 mm/min, wire feed rate of 1 m/min and beam offset of-0.3 mm. The microstructures of the optimum joint were studied. The results indicate that the weld is mainly composed of dendriticαphase with little globularεphase, and copper inhomogeneity only occurs at the top of the fusion zone. In addition, a melted region without mixing exists near the weld junction of copper side. This region with a coarser grain size is the weakest section of the joints. It is found that the microhardness of the weld decreases with the increase of the copper content in solid solution. The highest tensile strength of the joint is 276 MPa.