The electrochemical reduction of Zr^4＋（complex） ions in NaCl-KCl-K2ZrF6 molten salt on Pt electrode was investigated using cyclic voltammetry and square wave voltammetry at 1023 K.Two cathodic reduction peaks relat...The electrochemical reduction of Zr^4＋（complex） ions in NaCl-KCl-K2ZrF6 molten salt on Pt electrode was investigated using cyclic voltammetry and square wave voltammetry at 1023 K.Two cathodic reduction peaks related to Zr^4＋/Zr^2＋ and Zr^2＋/Zr steps were observed in the cyclic voltammograms.The result was also confirmed by square wave voltammetry.The diffusion coefficient of Zr^4＋（complex） ions at 1023 K in NaCl-KCl-K2ZrF6 melt,measured by cyclic voltammetry,is about 4.22×10^-6 cm^2/s.The characterization of the deposits obtained by potentiostatic electrolysis at different potentials was investigated by XRD,and the results were well consistent with the electrochemical reduction mechanism of Zr^4＋（complex） ions.展开更多
To acquire the synergy effects between Sn and Cu for the jointly high Faradaic efficiency and current density,we develop a novel strategy to design the Sn-Cu alloy catalyst via a decorated co-electrodeposition method ...To acquire the synergy effects between Sn and Cu for the jointly high Faradaic efficiency and current density,we develop a novel strategy to design the Sn-Cu alloy catalyst via a decorated co-electrodeposition method for CO2 electroreduction to formate.The Sn-Cu alloy shows high formate Faradaic efficiency of 82.3%±2.1% and total C1 products Faradaic efficiency of 90.0%±2.7% at^-1.14 V vs.reversible hydrogen electrode(RHE).The current density and mass activity of formate reach as high as(79.0±0.4)mA cm^-2 and(1490.6±7.5)m A mg^-1 at^-1.14 V vs.RHE.Theoretical calculations suggest that Sn-Cu alloy can obtain high Faradaic efficiency for CO2 electroreduction by suppressing the competitive hydrogen evolution reaction and that the formate formation follows the path of CO2→HCOO*→HCOOH.The stepped(211)surface of Sn-Cu alloy is beneficial towards selective formate production.展开更多
文摘The electrochemical reduction of Zr^4＋（complex） ions in NaCl-KCl-K2ZrF6 molten salt on Pt electrode was investigated using cyclic voltammetry and square wave voltammetry at 1023 K.Two cathodic reduction peaks related to Zr^4＋/Zr^2＋ and Zr^2＋/Zr steps were observed in the cyclic voltammograms.The result was also confirmed by square wave voltammetry.The diffusion coefficient of Zr^4＋（complex） ions at 1023 K in NaCl-KCl-K2ZrF6 melt,measured by cyclic voltammetry,is about 4.22×10^-6 cm^2/s.The characterization of the deposits obtained by potentiostatic electrolysis at different potentials was investigated by XRD,and the results were well consistent with the electrochemical reduction mechanism of Zr^4＋（complex） ions.
基金supported by the National Key R&D Program of China(2017YFA0700102)the National Natural Science Foundation of China(21573222,91545202,21802124,91945302 and 91845103)+6 种基金Dalian National Laboratory for Clean Energy(DNL180404)Dalian Institute of Chemical Physics(DICP DMTO201702)Dalian Outstanding Young Scientist Foundation(2017RJ03)Liaoning Revitalization Talents Program(XLYC1907099)the Strategic Priority Research Program of the Chinese Academy of Sciences(XDB17020200)the financial support from CAS Youth Innovation Promotion(2015145)the financial support from the China Postdoctoral Science Foundation(2018M630307 and 2019T120220)。
文摘To acquire the synergy effects between Sn and Cu for the jointly high Faradaic efficiency and current density,we develop a novel strategy to design the Sn-Cu alloy catalyst via a decorated co-electrodeposition method for CO2 electroreduction to formate.The Sn-Cu alloy shows high formate Faradaic efficiency of 82.3%±2.1% and total C1 products Faradaic efficiency of 90.0%±2.7% at^-1.14 V vs.reversible hydrogen electrode(RHE).The current density and mass activity of formate reach as high as(79.0±0.4)mA cm^-2 and(1490.6±7.5)m A mg^-1 at^-1.14 V vs.RHE.Theoretical calculations suggest that Sn-Cu alloy can obtain high Faradaic efficiency for CO2 electroreduction by suppressing the competitive hydrogen evolution reaction and that the formate formation follows the path of CO2→HCOO*→HCOOH.The stepped(211)surface of Sn-Cu alloy is beneficial towards selective formate production.