The fracture morphologies of several advanced high-strength steels （DP590, DP780, DP980, Ml180, and M1300） formed in uniaxial tension and piercing were observed by scanning electron microscope, and then quantitative...The fracture morphologies of several advanced high-strength steels （DP590, DP780, DP980, Ml180, and M1300） formed in uniaxial tension and piercing were observed by scanning electron microscope, and then quantitatively analyzed by image processing technique. The tension-induced fractographs are dominated by obvious uniform or bimodal size dimples, while shearing-induced fractographs have smooth surfaces and few dimples. The fracture zone of higher grade DP steels is smoother. As for M1180 and M1300, the fracture zones consist of very small dimples and smooth brittle surfaces. The dimple size of M1300（ ,- 1.2 tm） is smaller than that of M1180（ 1.6 tm）. Moreover, in the tensile fracture, the quantitative correlation between average dimple diameter （d） and tensile strength （a） can be represented by d = 10,502.32a-121. However, the relation between dimple density and tensile strength is not monotonic due to the appearance of bimodal size dimples with increase of tensile strength. For shearing-induced fracture during piercing, the fitted empirical model between the percentage of burnish zone （f） and tensile strength can be described asf --- 239.9a-＇36.展开更多
The fracture surface of the normalized steel 55SiMnMo was observed,under tensile device at- tached on the SEM,to be of ductile dimple feature on the bainite which is composed of lath ferrite and austenite platelet.The...The fracture surface of the normalized steel 55SiMnMo was observed,under tensile device at- tached on the SEM,to be of ductile dimple feature on the bainite which is composed of lath ferrite and austenite platelet.The dimple is essentially nucleated in the ferrite.Because the austenitic plastic deformation is remarkable during fracturing,the tear ridge of dimple is very sharp.展开更多
This study aims to discover the stress-state dependence of the dynamic strain aging(DSA)effect on the deformation and fracture behavior of high-strength dual-phase(DP)steel at different deformation temperatures(25-400...This study aims to discover the stress-state dependence of the dynamic strain aging(DSA)effect on the deformation and fracture behavior of high-strength dual-phase(DP)steel at different deformation temperatures(25-400°C)and reveal the damage mechanisms under these various configurations.To achieve different stress states,predesigned specimens with different geometric features were used.Scanning electron microscopy was applied to analyze the fracture modes(e.g.,dimple or shear mode)and underlying damage mechanism of the investigated material.DSA is present in this DP steel,showing the Portevin-Le Chatelier(PLC)effect with serrated flow behavior,thermal hardening,and blue brittleness phenomena.Results show that the stress state contributes distinctly to the DSA effect in terms of the magnitude of thermal hardening and the pattern of blue brittleness.Either low stress triaxiality or Lode angle parameter promotes DSA-induced blue brittleness.Accordingly,the damage mechanisms also show dependence on the stress states in conjunction with the DSA effect.展开更多
基金Project (51204124) supported by the National Natural Science Foundation of ChinaProject (2012M511610) supported by the China Postdoctoral Science FoundationProject (14125041) supported by the Scientific Research Foundation of Wuhan Institute of Technology
基金financially supported by the National Natural Science Foundation of China(No.51105246)
文摘The fracture morphologies of several advanced high-strength steels （DP590, DP780, DP980, Ml180, and M1300） formed in uniaxial tension and piercing were observed by scanning electron microscope, and then quantitatively analyzed by image processing technique. The tension-induced fractographs are dominated by obvious uniform or bimodal size dimples, while shearing-induced fractographs have smooth surfaces and few dimples. The fracture zone of higher grade DP steels is smoother. As for M1180 and M1300, the fracture zones consist of very small dimples and smooth brittle surfaces. The dimple size of M1300（ ,- 1.2 tm） is smaller than that of M1180（ 1.6 tm）. Moreover, in the tensile fracture, the quantitative correlation between average dimple diameter （d） and tensile strength （a） can be represented by d = 10,502.32a-121. However, the relation between dimple density and tensile strength is not monotonic due to the appearance of bimodal size dimples with increase of tensile strength. For shearing-induced fracture during piercing, the fitted empirical model between the percentage of burnish zone （f） and tensile strength can be described asf --- 239.9a-＇36.
文摘The fracture surface of the normalized steel 55SiMnMo was observed,under tensile device at- tached on the SEM,to be of ductile dimple feature on the bainite which is composed of lath ferrite and austenite platelet.The dimple is essentially nucleated in the ferrite.Because the austenitic plastic deformation is remarkable during fracturing,the tear ridge of dimple is very sharp.
基金The authors gratefully acknowledge the valuable comments by Prof.Sebastian Münstermann from Steel Institute(IEHK),RWTH Aachen University,Germany.The work has been supported by the European Commission Research Fund for Coal and Steel(No.709711).Wenqi Liu is grateful to Shujing Li and Guangming Zeng from IEHK for data processing.
文摘This study aims to discover the stress-state dependence of the dynamic strain aging(DSA)effect on the deformation and fracture behavior of high-strength dual-phase(DP)steel at different deformation temperatures(25-400°C)and reveal the damage mechanisms under these various configurations.To achieve different stress states,predesigned specimens with different geometric features were used.Scanning electron microscopy was applied to analyze the fracture modes(e.g.,dimple or shear mode)and underlying damage mechanism of the investigated material.DSA is present in this DP steel,showing the Portevin-Le Chatelier(PLC)effect with serrated flow behavior,thermal hardening,and blue brittleness phenomena.Results show that the stress state contributes distinctly to the DSA effect in terms of the magnitude of thermal hardening and the pattern of blue brittleness.Either low stress triaxiality or Lode angle parameter promotes DSA-induced blue brittleness.Accordingly,the damage mechanisms also show dependence on the stress states in conjunction with the DSA effect.