Electroactive shape memory composites were synthesized using polybutadiene epoxy （PBEP） and bisphenol A type cyanate ester （BACE） filled with different contents of carbon black （CB）. Dynamic mechanical analysis ...Electroactive shape memory composites were synthesized using polybutadiene epoxy （PBEP） and bisphenol A type cyanate ester （BACE） filled with different contents of carbon black （CB）. Dynamic mechanical analysis （DMA）, scanning electron microscopy （SEM）, electrical performance and electroactive shape memory behavior were systematically investigated. It is found that the volume resistivity decreased due to excellent electrical conductivity of CB, in turn resulting in good electroactive shape memory properties. The content of CB and applied voltage had significant influence on electroactive shape memory effect of developed BACE/PBEP/CB composites. Shape recovery can be observed within a few seconds with the CB content of 5 wt% and voltage of 60 V. Shape recovery time decreased with increasing content of CB and voltage. The infrared thermometer revealed that the temperature rises above the glass transition temperature faster with the increase of voltage and the decrease of resistance.展开更多
Inkjet 3D printing has potential in the additive manufacturing of electronic circuits and devices.However,inks that can be used for printing layers with T5%>300℃ or hardness>200 MPa have been rarely reported.Cy...Inkjet 3D printing has potential in the additive manufacturing of electronic circuits and devices.However,inks that can be used for printing layers with T5%>300℃ or hardness>200 MPa have been rarely reported.Cyanate ester(CE)polymers have excellent thermal stability,high strength,and low shrinkage compared to other common dielectric inks for inkjet 3D printing,but cannot be quickly shaped by ultraviolet(UV)irradiation or thermal treatment.Combining CEs with UV-curable monomers may be a possible way to accelerate crosslinking,but there are challenges from the adverse effects of the dilution of both monomers.In this study,dielectric inks with acrylate and cyanate moieties were developed.The low viscosity and surface tension of the CE precursor(Bisphenol E cyanate ester)were combined with photocurable acrylate diluent monomers and cross-linker to realize an ink suitable for inkjet 3D printing.An internal dual three-dimensional cross-linked network structure resin was prepared by a combination of photocuring and thermal curing with T5%up to 326.69℃,hardness up to 431.84 MPa,dielectric constant of 2.70 at 8 GHz,and shrinkage of 1.64%.The developed dielectric inks can be applied to the 3D printing of printed circuit boards and other electronic devices that require dielectric properties.展开更多
The properties of resin transfer molding(RTM)cyanate ester and its T800 grade carbon fiber composites were studied with the rheometer,differential scanning calorimetry(DSC),FT-IR,dynamic mechanical analyzer(DMA),therm...The properties of resin transfer molding(RTM)cyanate ester and its T800 grade carbon fiber composites were studied with the rheometer,differential scanning calorimetry(DSC),FT-IR,dynamic mechanical analyzer(DMA),thermal gravimetric analysis(TGA),mechanical property testing,and scanning electron microscopy(SEM).The results showed that the temperature of cyanate ester suitable for RTM process was 70℃.Curing process of the resin was 130℃/2 h+160℃/2 h+200℃/2 h+220℃/4 h.Glass transition temperature and heat decomposition temperature of the cured resin are 289℃and 415℃,respectively.Mechanical properties of T800/RTM cyanate composites are 13.5%higher than that of T700/RTM cyanate composites and equal to that of T800/Prepreg cyanate composites.Tg of T800/RTM cyanate composites was proved to be 291℃.Fracture pattern of the composites was flat,which proved excellent interface properties between fiber and resin in this composite.展开更多
This present study deals with the reinforcement of thermosetting resin blends composed of cyanate ester(CE) and benzoxazine(BOZ) resins with natural hemp fibers(NHFs). These NHFs were initially treated by using a sila...This present study deals with the reinforcement of thermosetting resin blends composed of cyanate ester(CE) and benzoxazine(BOZ) resins with natural hemp fibers(NHFs). These NHFs were initially treated by using a silane coupling agent(SCA) in order to chiefly enhance their distributions as well as adhesions within the CE/BOZ resin matrix,then incorporated with various weight amounts ranging from 5 wt% to 20 wt% with a regular interval of 5 wt%. The obtained results showed that at the maximum treated fiber loading(20 wt%), distinctive enhancements in the mechanical properties in terms of flexural strength and microhardness were obtained. Besides, the thermal stability and glass transition temperature(Tg) were appreciably enhanced and were higher than those of the pure CE/BOZ resin properties. With respect to the astonishing properties of the NHFs, these enhancements could be possibly due to the good dispersion and adhesion of the treated NHFs inside the CE/BOZ resin achieved upon using the SCA. Therefore,we believe herein that these renewable and cheap NHFs have considerable potential to be used as reinfocer materials for CE/BOZ resin composites to be used in various industrial sectors.展开更多
High-performance polymer friction materials with tunable tribological behavior to fit varied work conditions remain a challenge of widespread interest for a variety of applications.Shape memory polymer exhibits morphi...High-performance polymer friction materials with tunable tribological behavior to fit varied work conditions remain a challenge of widespread interest for a variety of applications.Shape memory polymer exhibits morphing and modulus changing over temperature changing provides a promising material to adjust the friction process.Herein,we investigated the tribological properties of shape memory cyanate ester(SMCE)under different conditions.The SMCE exhibits the tribological behavior of good friction material with stable high coefficient of friction(COF)and a low wear rate.Besides,the COF increases and wear rate decreases with the temperature increasing show the tunable friction property of the SMCE.We propose a new model of wear-compensation through shape recovery to explain the adjustable friction behavior of thermal-responsive polymer from the aspect of shape recovery and energy conversion.This study provides a high-performance friction material and paves the route for the application of shape memory polymer(SMP)in tribology field with tunable property.展开更多
文摘Electroactive shape memory composites were synthesized using polybutadiene epoxy （PBEP） and bisphenol A type cyanate ester （BACE） filled with different contents of carbon black （CB）. Dynamic mechanical analysis （DMA）, scanning electron microscopy （SEM）, electrical performance and electroactive shape memory behavior were systematically investigated. It is found that the volume resistivity decreased due to excellent electrical conductivity of CB, in turn resulting in good electroactive shape memory properties. The content of CB and applied voltage had significant influence on electroactive shape memory effect of developed BACE/PBEP/CB composites. Shape recovery can be observed within a few seconds with the CB content of 5 wt% and voltage of 60 V. Shape recovery time decreased with increasing content of CB and voltage. The infrared thermometer revealed that the temperature rises above the glass transition temperature faster with the increase of voltage and the decrease of resistance.
基金supported by the National Key Researchand Development Programof China(No.2022YFB4600101)the Strategic Priority Research Program of the Chinese Academy of Sciences(No.XDB 0470303)+2 种基金the National Natural Science Foundation of China(No.21974057)the Western Light Project of Chinese Academy of Sciences(No.xbzg-zdsy-202007)the Oasis Scholar of Shihezi University and the Central Government to Guide Local Technological Development(No.23ZYQA315).
文摘Inkjet 3D printing has potential in the additive manufacturing of electronic circuits and devices.However,inks that can be used for printing layers with T5%>300℃ or hardness>200 MPa have been rarely reported.Cyanate ester(CE)polymers have excellent thermal stability,high strength,and low shrinkage compared to other common dielectric inks for inkjet 3D printing,but cannot be quickly shaped by ultraviolet(UV)irradiation or thermal treatment.Combining CEs with UV-curable monomers may be a possible way to accelerate crosslinking,but there are challenges from the adverse effects of the dilution of both monomers.In this study,dielectric inks with acrylate and cyanate moieties were developed.The low viscosity and surface tension of the CE precursor(Bisphenol E cyanate ester)were combined with photocurable acrylate diluent monomers and cross-linker to realize an ink suitable for inkjet 3D printing.An internal dual three-dimensional cross-linked network structure resin was prepared by a combination of photocuring and thermal curing with T5%up to 326.69℃,hardness up to 431.84 MPa,dielectric constant of 2.70 at 8 GHz,and shrinkage of 1.64%.The developed dielectric inks can be applied to the 3D printing of printed circuit boards and other electronic devices that require dielectric properties.
文摘The properties of resin transfer molding(RTM)cyanate ester and its T800 grade carbon fiber composites were studied with the rheometer,differential scanning calorimetry(DSC),FT-IR,dynamic mechanical analyzer(DMA),thermal gravimetric analysis(TGA),mechanical property testing,and scanning electron microscopy(SEM).The results showed that the temperature of cyanate ester suitable for RTM process was 70℃.Curing process of the resin was 130℃/2 h+160℃/2 h+200℃/2 h+220℃/4 h.Glass transition temperature and heat decomposition temperature of the cured resin are 289℃and 415℃,respectively.Mechanical properties of T800/RTM cyanate composites are 13.5%higher than that of T700/RTM cyanate composites and equal to that of T800/Prepreg cyanate composites.Tg of T800/RTM cyanate composites was proved to be 291℃.Fracture pattern of the composites was flat,which proved excellent interface properties between fiber and resin in this composite.
基金Supported by the National Natural Science Foundation of China(51773048)the Natural Science Foundation of Heilongjiang Province(E2016025)Fundamental Research Funds for the Central Universities(HEUCFP201724,HEUCFP201791)
文摘This present study deals with the reinforcement of thermosetting resin blends composed of cyanate ester(CE) and benzoxazine(BOZ) resins with natural hemp fibers(NHFs). These NHFs were initially treated by using a silane coupling agent(SCA) in order to chiefly enhance their distributions as well as adhesions within the CE/BOZ resin matrix,then incorporated with various weight amounts ranging from 5 wt% to 20 wt% with a regular interval of 5 wt%. The obtained results showed that at the maximum treated fiber loading(20 wt%), distinctive enhancements in the mechanical properties in terms of flexural strength and microhardness were obtained. Besides, the thermal stability and glass transition temperature(Tg) were appreciably enhanced and were higher than those of the pure CE/BOZ resin properties. With respect to the astonishing properties of the NHFs, these enhancements could be possibly due to the good dispersion and adhesion of the treated NHFs inside the CE/BOZ resin achieved upon using the SCA. Therefore,we believe herein that these renewable and cheap NHFs have considerable potential to be used as reinfocer materials for CE/BOZ resin composites to be used in various industrial sectors.
基金The authors gratefully acknowledge financial support from the National Natural Science Foundation of China(51935012 and 52105223)Major Program of the Lanzhou Institute of Chemical Physics,CAS(No.ZYFZFX-7)Key Research Program of the Chinese Academy of Sciences(Grant No.XDPB24).
文摘High-performance polymer friction materials with tunable tribological behavior to fit varied work conditions remain a challenge of widespread interest for a variety of applications.Shape memory polymer exhibits morphing and modulus changing over temperature changing provides a promising material to adjust the friction process.Herein,we investigated the tribological properties of shape memory cyanate ester(SMCE)under different conditions.The SMCE exhibits the tribological behavior of good friction material with stable high coefficient of friction(COF)and a low wear rate.Besides,the COF increases and wear rate decreases with the temperature increasing show the tunable friction property of the SMCE.We propose a new model of wear-compensation through shape recovery to explain the adjustable friction behavior of thermal-responsive polymer from the aspect of shape recovery and energy conversion.This study provides a high-performance friction material and paves the route for the application of shape memory polymer(SMP)in tribology field with tunable property.