Direct phase transformation of flue gas desulfurization gypsum in hot salt solution at atmospheric pres-sure was investigated.The effects of temperature,salt species,salt concentration,solids content,pH and modifier w...Direct phase transformation of flue gas desulfurization gypsum in hot salt solution at atmospheric pres-sure was investigated.The effects of temperature,salt species,salt concentration,solids content,pH and modifier were examined.The crystals obtained under different conditions and solubility of calcium sulfate in contact with solid gypsum were also determined.α-Calcium sulfate hemihydrate crystals of stubby columnar shape and regular pentahedral sides were obtained under the following conditions：salt concentration 20%-30%,operation tempera-ture 95-100 °C,solids mass content in the slurry 10%-30% and neutral pH.Thermodynamic analysis revealed that phase transformation of calcium sulfate dihydrate to α-calcium sulfate hemihydrate occurs because of the difference in solubilities between the two solid gypsum phases in this system.展开更多
Solvent annealing is a facile method for changing the aggregated microstructure and physical properties of polymer materials. In this paper, we addressed the effects of solvent vapor annealing, including chloroform an...Solvent annealing is a facile method for changing the aggregated microstructure and physical properties of polymer materials. In this paper, we addressed the effects of solvent vapor annealing, including chloroform and water vapor, on the polymorphic transformation in both hot-pressed film and electrospun nonwoven of isotactic polybutene-1 （PB-1） by means of in situ Fourier transform infrared spectroscopy （FTIR）. The pretty rapid transition rate caused by the increased motion of molecular chains under chloroform vapor is associated with a lowest crystallinity. Also, a decreased crystallinity with the crystal transition occurred in electrospun nonwovens resulting from the relaxation of the stretched molecular chains into amorphous state rather than realignment into crystal form I predominating the crystal transition process.展开更多
Single-crystal Ni-rich cathode material LiNi0.88Co0.09Al0.03O2(SC) was synthesized by a high-temperature solid-state calcination method. Physicochemical properties of primary and delithiated SC samples were investigat...Single-crystal Ni-rich cathode material LiNi0.88Co0.09Al0.03O2(SC) was synthesized by a high-temperature solid-state calcination method. Physicochemical properties of primary and delithiated SC samples were investigated by X-ray diffractometry, X-ray photoelectron spectroscopy, and transmission electron microscopy. Electrochemical performance was characterized by long-term cycling, cyclic voltammetry, and in-situ impedance spectroscopy. The results indicated that high temperature rendered layered oxides to lose lithium/oxygen in the interior and exterior, and induced cationic disordering. Besides, the solid-phase synthesis process promoted phase transformation for electrode materials, causing the coexisting multi-phase in a single particle. High temperature can foster the growth of single particles, but it caused unstable structure of layered phase.展开更多
基金Supported by the National High Technology Research and Development Program of China（2006AA06Z385） the Science Foundation of Wuhan University of Science and Technology（2008RC06）
文摘Direct phase transformation of flue gas desulfurization gypsum in hot salt solution at atmospheric pres-sure was investigated.The effects of temperature,salt species,salt concentration,solids content,pH and modifier were examined.The crystals obtained under different conditions and solubility of calcium sulfate in contact with solid gypsum were also determined.α-Calcium sulfate hemihydrate crystals of stubby columnar shape and regular pentahedral sides were obtained under the following conditions：salt concentration 20%-30%,operation tempera-ture 95-100 °C,solids mass content in the slurry 10%-30% and neutral pH.Thermodynamic analysis revealed that phase transformation of calcium sulfate dihydrate to α-calcium sulfate hemihydrate occurs because of the difference in solubilities between the two solid gypsum phases in this system.
基金financially supported by the Special Foundation of Taishan Mountain Scholar Constructive Programthe National Natural Science Foundation of China(No.21174074)+3 种基金Shandong Provincical Key R&D Program(No.2015GGX102019)Shandong Provincial Natural Science Fund for Distinguished Young Scholars(No.JQ201213)the Nature Science Foundation of Shandong Province(No.ZR2013BM004)the Yellow River Delta Scholar program(Office of National University Science&Technology Park Administrative Committee(China University of Petroleum))
文摘Solvent annealing is a facile method for changing the aggregated microstructure and physical properties of polymer materials. In this paper, we addressed the effects of solvent vapor annealing, including chloroform and water vapor, on the polymorphic transformation in both hot-pressed film and electrospun nonwoven of isotactic polybutene-1 （PB-1） by means of in situ Fourier transform infrared spectroscopy （FTIR）. The pretty rapid transition rate caused by the increased motion of molecular chains under chloroform vapor is associated with a lowest crystallinity. Also, a decreased crystallinity with the crystal transition occurred in electrospun nonwovens resulting from the relaxation of the stretched molecular chains into amorphous state rather than realignment into crystal form I predominating the crystal transition process.
基金financial supports from the National Natural Science Foundation of China (51974368)the Fundamental Research Funds of the Central South University,China。
文摘Single-crystal Ni-rich cathode material LiNi0.88Co0.09Al0.03O2(SC) was synthesized by a high-temperature solid-state calcination method. Physicochemical properties of primary and delithiated SC samples were investigated by X-ray diffractometry, X-ray photoelectron spectroscopy, and transmission electron microscopy. Electrochemical performance was characterized by long-term cycling, cyclic voltammetry, and in-situ impedance spectroscopy. The results indicated that high temperature rendered layered oxides to lose lithium/oxygen in the interior and exterior, and induced cationic disordering. Besides, the solid-phase synthesis process promoted phase transformation for electrode materials, causing the coexisting multi-phase in a single particle. High temperature can foster the growth of single particles, but it caused unstable structure of layered phase.