The structure of [Cu2(Hdmg)4] (Hdmg=dimethylglyoxime anion) has been determined by X ray crystallography. It is monoclinic, space group P21/n, with Z=2. The lattice parameters: a=0.71601(14)nm; b=1.7044(3)nm; c=1.0126...The structure of [Cu2(Hdmg)4] (Hdmg=dimethylglyoxime anion) has been determined by X ray crystallography. It is monoclinic, space group P21/n, with Z=2. The lattice parameters: a=0.71601(14)nm; b=1.7044(3)nm; c=1.0126(4)nm; β =113.89(2)° ; Mr=587.52 (C16H28Cu2N8O8); V=1.1299(5)nm3. The copper atom lies in a distorted square pyramidal environment. The four equatorial donors are four nitrogen atoms from bidentate chelate dimethylglyoxime anion ligands. The oxygen atom from the dimethylglyoxime ligand acts as a bridging atom occupying the apical position of the symmetry related copper atom in the dimer structure. The two dimethylglyoximes bridge two copper atoms to form a six member Cu2O2N2 ring, respectively. The thermal gravity (TG) data indicate that the compound [Cu2(Hdmg)4] undergoes two exothermic reactions with loss of the organic ligand to give residue CuO. CCDC: 208729.展开更多
Copper nitride film （Cu3N） and La-doped copper nitride films （LaxCu3N） were prepared on glass substrates by reactive magnetron sputtering of a pure Cu and a pure La targets under N2 atmosphere. The results show th...Copper nitride film （Cu3N） and La-doped copper nitride films （LaxCu3N） were prepared on glass substrates by reactive magnetron sputtering of a pure Cu and a pure La targets under N2 atmosphere. The results show that La-free film was composed of Cu3N crystallites with anti-ReO3 structure with （111） texture. The formation of the LaxCu3N films is affected strongly by La, and the peak intensity of the preferred crystalline [111]-orientation decreases with increasing the concentration of La. High concentration of La may prevent the formation of the Cu3N from crystallization. Compared with the Cu3N films, the resistivity of the LaxCu3N films have been decreased.展开更多
文摘The structure of [Cu2(Hdmg)4] (Hdmg=dimethylglyoxime anion) has been determined by X ray crystallography. It is monoclinic, space group P21/n, with Z=2. The lattice parameters: a=0.71601(14)nm; b=1.7044(3)nm; c=1.0126(4)nm; β =113.89(2)° ; Mr=587.52 (C16H28Cu2N8O8); V=1.1299(5)nm3. The copper atom lies in a distorted square pyramidal environment. The four equatorial donors are four nitrogen atoms from bidentate chelate dimethylglyoxime anion ligands. The oxygen atom from the dimethylglyoxime ligand acts as a bridging atom occupying the apical position of the symmetry related copper atom in the dimer structure. The two dimethylglyoximes bridge two copper atoms to form a six member Cu2O2N2 ring, respectively. The thermal gravity (TG) data indicate that the compound [Cu2(Hdmg)4] undergoes two exothermic reactions with loss of the organic ligand to give residue CuO. CCDC: 208729.
基金supported by the National Natural Sci-ence Foundation of China under grant No. 10574047the Key Program of the Education Branch of Hubei Provinceof China under grant No. D200529002+1 种基金the Key Pro-gram of the Ethnic Affairs Committee of China undergrant No. 08HB05 the Scientific Research Foundation of Nanjing University of Post and Telecommunication un-der grant No. NY208025.
文摘Copper nitride film （Cu3N） and La-doped copper nitride films （LaxCu3N） were prepared on glass substrates by reactive magnetron sputtering of a pure Cu and a pure La targets under N2 atmosphere. The results show that La-free film was composed of Cu3N crystallites with anti-ReO3 structure with （111） texture. The formation of the LaxCu3N films is affected strongly by La, and the peak intensity of the preferred crystalline [111]-orientation decreases with increasing the concentration of La. High concentration of La may prevent the formation of the Cu3N from crystallization. Compared with the Cu3N films, the resistivity of the LaxCu3N films have been decreased.