Wood has no inherent natural resistance against agents of biodegradation. We evaluated the effects of metal bath heat treatment(MBHT) on decay resistance and dimensional stability of Chinese parasol(Firmiana simplex) ...Wood has no inherent natural resistance against agents of biodegradation. We evaluated the effects of metal bath heat treatment(MBHT) on decay resistance and dimensional stability of Chinese parasol(Firmiana simplex) and Chinese fir(Cunninghamia lanceolata) wood. A low melting point alloy was used as heating medium in the treatment of the wood samples at 150, 180, and 210 °C for2, 4, and 8 h. Heat-treated and control samples were exposed to brown rot fungus(Poria placenta) and white rot fungus(Coriolus versicolor) for decay resistance testing and anti-swelling efficiency(ASE). The improved decay resistance with increase temperatures with low mass losses of 7.3 and 7.3% for F. simplex, and 3.9 and 3.6% for C.lanceolata at 210 °C for 8 h against Coriolus versicolor and Poria placenta, respectively. ASE indicated that MBHT contributed to improved dimensional stability of both wood species after treatment. Scanning electron micrograph results indicate that metal bath-treated samples showed strong decay resistance. Therefore, our approach to thermally modify wood should be explored to overcome the energy utilization by using low melting point alloy for the heat treatment of wood.展开更多
以梧桐树粉尘为例,研究了可作为工业粉状炸药添加剂的木粉粉尘的爆炸特性。运用哈特曼管测试了粉尘云的最小点火能,得出样品1#、样品2#和样品3#的最小点火能分别为70、90 m J和150 m J。将响应面法中的Box-Behnken试验设计应用于粉尘爆...以梧桐树粉尘为例,研究了可作为工业粉状炸药添加剂的木粉粉尘的爆炸特性。运用哈特曼管测试了粉尘云的最小点火能,得出样品1#、样品2#和样品3#的最小点火能分别为70、90 m J和150 m J。将响应面法中的Box-Behnken试验设计应用于粉尘爆炸压力的测试,用20 L爆炸球进行试验,并从试验结果中拟合回归方程,由此判断出粉尘浓度对爆炸压力的影响最大,其次是点火能量,再次是粉尘粒径。对爆炸压力的试验条件进行优化,试验测得压力值为0.795 9 MPa,试验值与预测值之间的误差仅为1.28%,证明了该模型非常有效。展开更多
基金financially supported by the Special Scientific Research Fund for Public Service Sectors of Forestry(Grant No.201504603)Science and Technology Projects of Fujian Province(2014NZ003)the National Natural Science Foundation of China(Grant Nos.31370560,31170520)
文摘Wood has no inherent natural resistance against agents of biodegradation. We evaluated the effects of metal bath heat treatment(MBHT) on decay resistance and dimensional stability of Chinese parasol(Firmiana simplex) and Chinese fir(Cunninghamia lanceolata) wood. A low melting point alloy was used as heating medium in the treatment of the wood samples at 150, 180, and 210 °C for2, 4, and 8 h. Heat-treated and control samples were exposed to brown rot fungus(Poria placenta) and white rot fungus(Coriolus versicolor) for decay resistance testing and anti-swelling efficiency(ASE). The improved decay resistance with increase temperatures with low mass losses of 7.3 and 7.3% for F. simplex, and 3.9 and 3.6% for C.lanceolata at 210 °C for 8 h against Coriolus versicolor and Poria placenta, respectively. ASE indicated that MBHT contributed to improved dimensional stability of both wood species after treatment. Scanning electron micrograph results indicate that metal bath-treated samples showed strong decay resistance. Therefore, our approach to thermally modify wood should be explored to overcome the energy utilization by using low melting point alloy for the heat treatment of wood.
文摘以梧桐树粉尘为例,研究了可作为工业粉状炸药添加剂的木粉粉尘的爆炸特性。运用哈特曼管测试了粉尘云的最小点火能,得出样品1#、样品2#和样品3#的最小点火能分别为70、90 m J和150 m J。将响应面法中的Box-Behnken试验设计应用于粉尘爆炸压力的测试,用20 L爆炸球进行试验,并从试验结果中拟合回归方程,由此判断出粉尘浓度对爆炸压力的影响最大,其次是点火能量,再次是粉尘粒径。对爆炸压力的试验条件进行优化,试验测得压力值为0.795 9 MPa,试验值与预测值之间的误差仅为1.28%,证明了该模型非常有效。
