The selective catalytic reduction(SCR) of NOx using MnOx and CeO2 supported on viscose-based active carbon fibers(ACF) at 120 ℃～270 ℃ relatively lower than the temperature when using V2O5/TiO2-anatase catalyst was ...The selective catalytic reduction(SCR) of NOx using MnOx and CeO2 supported on viscose-based active carbon fibers(ACF) at 120 ℃～270 ℃ relatively lower than the temperature when using V2O5/TiO2-anatase catalyst was studied.As a result,CeO2/ACF shows a better catalysis than MNOx/ACF,which is not affected by the reaction temperature. NO conversion of 85% is reached with the 10%-CeO2/ACF catalyst at the whole temperature window.Furthermore,a series of MnOx-CeO2/ACF composite catalysts were studied.The results show that the loading method of catalyst affects its activity.展开更多
The effects of CeO2 on microstructure and corrosion resistance of TiC-VC reinforced Fe-based laser cladding layers were investigated. The results showed that carbides presented in cladding layers were TiVC2 and VC. A ...The effects of CeO2 on microstructure and corrosion resistance of TiC-VC reinforced Fe-based laser cladding layers were investigated. The results showed that carbides presented in cladding layers were TiVC2 and VC. A small quantity of CeC appeared with 2.0 wt.% CeO2 addition. The amount of lamellar pearlite increased while the amount of residual austenite decreased with increasing CeO2 addition. The corrosion resistance of cladding layers increased firstly and then decreased with the addition of CeO2 increasing. The EIS spectrum of the cladding layer without CeO2 was composed of an inductive arc at low frequency and a capacitive arc at high frequency. The cladding layer with 0.5 wt.% CeO2 addition showed the best corrosion resistance, and then the inductive arc at low frequency transformed into a capacitive arc.展开更多
The cationic polyurethane/CeO 2 nanocomposite dispersion has been synthesiz ed by adding ceria organosol to pre-polymer of polyurethane and then adding neutralization reagent and water to give an emulsion. FTIR analys...The cationic polyurethane/CeO 2 nanocomposite dispersion has been synthesiz ed by adding ceria organosol to pre-polymer of polyurethane and then adding neutralization reagent and water to give an emulsion. FTIR analysis shows blue shift of the absorpsion band of CeO 2 . TEM micrograph shows that CeO 2 nano- particles ar e uniformly dispersed in polyurethane. Polyurethane/CeO 2 nanocomposite has high absorption at the region lower 350 nm.展开更多
文摘The selective catalytic reduction(SCR) of NOx using MnOx and CeO2 supported on viscose-based active carbon fibers(ACF) at 120 ℃～270 ℃ relatively lower than the temperature when using V2O5/TiO2-anatase catalyst was studied.As a result,CeO2/ACF shows a better catalysis than MNOx/ACF,which is not affected by the reaction temperature. NO conversion of 85% is reached with the 10%-CeO2/ACF catalyst at the whole temperature window.Furthermore,a series of MnOx-CeO2/ACF composite catalysts were studied.The results show that the loading method of catalyst affects its activity.
基金Project supported by National Natural Science Foundation of China(51271099)
文摘The effects of CeO2 on microstructure and corrosion resistance of TiC-VC reinforced Fe-based laser cladding layers were investigated. The results showed that carbides presented in cladding layers were TiVC2 and VC. A small quantity of CeC appeared with 2.0 wt.% CeO2 addition. The amount of lamellar pearlite increased while the amount of residual austenite decreased with increasing CeO2 addition. The corrosion resistance of cladding layers increased firstly and then decreased with the addition of CeO2 increasing. The EIS spectrum of the cladding layer without CeO2 was composed of an inductive arc at low frequency and a capacitive arc at high frequency. The cladding layer with 0.5 wt.% CeO2 addition showed the best corrosion resistance, and then the inductive arc at low frequency transformed into a capacitive arc.
文摘The cationic polyurethane/CeO 2 nanocomposite dispersion has been synthesiz ed by adding ceria organosol to pre-polymer of polyurethane and then adding neutralization reagent and water to give an emulsion. FTIR analysis shows blue shift of the absorpsion band of CeO 2 . TEM micrograph shows that CeO 2 nano- particles ar e uniformly dispersed in polyurethane. Polyurethane/CeO 2 nanocomposite has high absorption at the region lower 350 nm.