Ce0.67Zr0.33O2-Al2O3 solid solution was prepared by the co-precipitation method. Fe2O3-based catalysts supported on the solid solution were obtained by the impregnation method. The article revealed that the optimal lo...Ce0.67Zr0.33O2-Al2O3 solid solution was prepared by the co-precipitation method. Fe2O3-based catalysts supported on the solid solution were obtained by the impregnation method. The article revealed that the optimal loading amount of Fe2O3 on Ce0.67Zr0.33 O2-Al2O3 in our experimental condition for catalytic combustion of methane was 8% （ mass fraction）. The prepared catalysts were characterized by BET, TPR, XRD analyses, and their catalytic activity was investigated after being calcined at 873 K and after being aged in water gas at 1273 K. When the loading amount of Fe203 was 8% （ mass fraction）, the catalyst held the highest activity, and the best temperature speciality and thermal stability. The complete-conversion temperature of methane for fresh and aged sample was 788 and 838 K, respectively. The range between the light-off temperature and the complete-conversion temperature was only 15 K. The characterization results of XRD indicated that Fe2O3 was well dispersed on the Ce0.67Zr0.33O2-Al2O3 matrix. The results of BET and TPR were in good harmony with the catalytic activity results.展开更多
Monolithic catalysts of Pt/La-Al2O3 and Pt/Ce0.67Zr0.3302 were prepared to investigate methane selective catalytic reduction （SCR） of NO. The results indicate that Pt/Ce0.67Zr0.33O2 shows high activity and both NO a...Monolithic catalysts of Pt/La-Al2O3 and Pt/Ce0.67Zr0.3302 were prepared to investigate methane selective catalytic reduction （SCR） of NO. The results indicate that Pt/Ce0.67Zr0.33O2 shows high activity and both NO and CH4 can be converted completely at 450℃. Meanwhile, NO and CH4 can be converted completely when there exists excess oxygen. The Pt/Ce0.67Zr0.33O2 catalyst were further investigated by using methane as reducing agent to SCR NO in a novel equipment which combined the CH4 selective catalytic reduction of NO with methane combustion. The result shows that the catalyst is high active and the novel equipment is very effective. The conversion of NO is above 92% under the conditions used in this work. The prepared burner and catalysts have great potential for application.展开更多
Pd/Ce0.67Zr0.33O2 catalyst was pretreated in different atmosphere respectively, and characterized by CO chemical adsorption, XPS, HR-TEM, H2-TPR, Raman, OSC and in situ DRIFTS to investigate the effect of the structur...Pd/Ce0.67Zr0.33O2 catalyst was pretreated in different atmosphere respectively, and characterized by CO chemical adsorption, XPS, HR-TEM, H2-TPR, Raman, OSC and in situ DRIFTS to investigate the effect of the structure properties of PdOx species on the catalytic performance for CO, HC and NOx elimination. The results show that Pd/CZ catalyst pretreated in air atmosphere has higher oxidation activity of HC due to having high Pd dispersion and strong interaction between PdOx and CZ support. Pd/CZ-H catalyst pretreated in reducing atmosphere exhibits better catalytic performance of NOx elimination because of having relatively big Pd particle size, more Pd species in metallic state and higher concentration of oxygen vacancies. While for the Pd/CZ-RG catalyst pretreated in reactant atmosphere, strong adsorption of HC species on the surface of catalysts would lead to a part of active sites being covered, which inhibits HC and NO conversions.展开更多
Ceria-zirconia-alumina （CZA） solid solution was prepared by sol-gel method in the present study. 0.5 wt.% Pd supported on CZA was prepared by incipient wetness impregnation. The steam effects for CO and C3H8 oxidati...Ceria-zirconia-alumina （CZA） solid solution was prepared by sol-gel method in the present study. 0.5 wt.% Pd supported on CZA was prepared by incipient wetness impregnation. The steam effects for CO and C3H8 oxidation, three-way catalytic activity and stoichiometric window property were studied. The light-off temperature of the CO oxidation reaction shifted to a lower temperature due to the water-gas shift （WGS） reactions. The oxidation of C3H8 was enhanced due to the steam reforming （SR） reactions. The steam promoted the C3H8 oxidation and NO reduction in three-way catalytic reaction. The amplitude of stoichiometric window was amplified by the addition of water to the feed stream.展开更多
基金Project supported by the National Natural Science Key Foundation of China (20333030)
文摘Ce0.67Zr0.33O2-Al2O3 solid solution was prepared by the co-precipitation method. Fe2O3-based catalysts supported on the solid solution were obtained by the impregnation method. The article revealed that the optimal loading amount of Fe2O3 on Ce0.67Zr0.33 O2-Al2O3 in our experimental condition for catalytic combustion of methane was 8% （ mass fraction）. The prepared catalysts were characterized by BET, TPR, XRD analyses, and their catalytic activity was investigated after being calcined at 873 K and after being aged in water gas at 1273 K. When the loading amount of Fe203 was 8% （ mass fraction）, the catalyst held the highest activity, and the best temperature speciality and thermal stability. The complete-conversion temperature of methane for fresh and aged sample was 788 and 838 K, respectively. The range between the light-off temperature and the complete-conversion temperature was only 15 K. The characterization results of XRD indicated that Fe2O3 was well dispersed on the Ce0.67Zr0.33O2-Al2O3 matrix. The results of BET and TPR were in good harmony with the catalytic activity results.
基金Supported by the National High Technology Research and Development Program of China (863 Program, 2006AA06Z347)the NationalNatural Science Foundation of China (20773090).
文摘Monolithic catalysts of Pt/La-Al2O3 and Pt/Ce0.67Zr0.3302 were prepared to investigate methane selective catalytic reduction （SCR） of NO. The results indicate that Pt/Ce0.67Zr0.33O2 shows high activity and both NO and CH4 can be converted completely at 450℃. Meanwhile, NO and CH4 can be converted completely when there exists excess oxygen. The Pt/Ce0.67Zr0.33O2 catalyst were further investigated by using methane as reducing agent to SCR NO in a novel equipment which combined the CH4 selective catalytic reduction of NO with methane combustion. The result shows that the catalyst is high active and the novel equipment is very effective. The conversion of NO is above 92% under the conditions used in this work. The prepared burner and catalysts have great potential for application.
基金Project supported by the Key Program of Science Technology Department of Zhejiang Province(2018C03037)
文摘Pd/Ce0.67Zr0.33O2 catalyst was pretreated in different atmosphere respectively, and characterized by CO chemical adsorption, XPS, HR-TEM, H2-TPR, Raman, OSC and in situ DRIFTS to investigate the effect of the structure properties of PdOx species on the catalytic performance for CO, HC and NOx elimination. The results show that Pd/CZ catalyst pretreated in air atmosphere has higher oxidation activity of HC due to having high Pd dispersion and strong interaction between PdOx and CZ support. Pd/CZ-H catalyst pretreated in reducing atmosphere exhibits better catalytic performance of NOx elimination because of having relatively big Pd particle size, more Pd species in metallic state and higher concentration of oxygen vacancies. While for the Pd/CZ-RG catalyst pretreated in reactant atmosphere, strong adsorption of HC species on the surface of catalysts would lead to a part of active sites being covered, which inhibits HC and NO conversions.
基金Project supported by National High-Tech Research and Development Program of China(2011AA03A405)the Key Program of TianjinNatural Science Foundation(09JCZDJC26600)
文摘Ceria-zirconia-alumina （CZA） solid solution was prepared by sol-gel method in the present study. 0.5 wt.% Pd supported on CZA was prepared by incipient wetness impregnation. The steam effects for CO and C3H8 oxidation, three-way catalytic activity and stoichiometric window property were studied. The light-off temperature of the CO oxidation reaction shifted to a lower temperature due to the water-gas shift （WGS） reactions. The oxidation of C3H8 was enhanced due to the steam reforming （SR） reactions. The steam promoted the C3H8 oxidation and NO reduction in three-way catalytic reaction. The amplitude of stoichiometric window was amplified by the addition of water to the feed stream.