In this paper, a comparative study of the maximum power on the shading rate on the maximum power of thin film PV modules. Thus two thin film PV modules of type Copper indium gallium selenide, CIGS, of 90W power and a ...In this paper, a comparative study of the maximum power on the shading rate on the maximum power of thin film PV modules. Thus two thin film PV modules of type Copper indium gallium selenide, CIGS, of 90W power and a CdTe (Cadmium telluride)/CdS (Cadmium sulfide) module, of maximum power 75 W. These modules, reference SN-CIGS90 and CX3 75 were tested under the conditions of the installation site to ensure their proper functioning and to determine the initial values of electrical parameters before shading. The results obtained are as follows: for the CIGS: Pm (80.717 W);Vco (23.06 V), Icc (3.5 A) and for the CdTe:Pm (54.914 W);Vco (35.52 V), Icc (1.546 A). After this characterization test, the modules are exposed to real operating conditions at the Center for Study and Research on the renewable energy (CERER), Cheikh Anta Diop University in Dakar. Four types of shading are performed on each module with the same mask: partial shading at 25%, 50%, 75% and complete shading at 100%. The comparison of the variation rates obtained on the experimental values of the 4 types of shading carried out on each module, shows that, the phenomenon of shading constitutes an environmental factor which influences negatively the maximum power of the thin film PV modules. But this reduction depends on the surface of the shaded module, the nature of the mask but also the technology used. Indeed, for a shading of 25% of the surface of the two modules, we note a reduction of 21.32% of power for the CIGS, against 40.53% for the CdTe/CdS, that is to say a difference which approaches 20%.展开更多
In the study, we observed the strong adsorption of CdTe/CdS QDs to antibodies and the formation of QDs-antibodies conjugates. Capillary electrophoresis with laser-induced fluorescence detection （CE-LIF）, fluorescenc...In the study, we observed the strong adsorption of CdTe/CdS QDs to antibodies and the formation of QDs-antibodies conjugates. Capillary electrophoresis with laser-induced fluorescence detection （CE-LIF）, fluorescence spectrometry and fluorescence correlation spectroscopy （FCS） were used to characterize the QDs conjugates with antibody. We found that the QDs-antibody conjugates possessed high fluorescence, small hydrodynamic radii and good stability in aqueous solution. 2009 Ji Cun Ren. Published by Elsevier B.V. on behalf of Chinese Chemical Society. All rights reserved.展开更多
Novel CdTe/CdS quantum dots(QDs)coated with a hybrid of SiO_2 and ZnS were fabricated through a simple two-step approach.The hybrid SiO_2/ZnS coated CdTe/CdS quantum dots was characterized by transmission electron mic...Novel CdTe/CdS quantum dots(QDs)coated with a hybrid of SiO_2 and ZnS were fabricated through a simple two-step approach.The hybrid SiO_2/ZnS coated CdTe/CdS quantum dots was characterized by transmission electron microscopy(TEM),UV and fluorescence spectrometer.Results indicated that the core-shell structure gave the QDs outstanding photoluminescence properties,includinganarrowphotoluminescencespectrum,high photoluminescence(PL)quantum yield and long emission lifetime(average PL lifetime of increased from 26.4 ns to 49.1 ns).Cellular studies showed the QDs had good cytocompatibility with Hela cells as determined by the 3-(4,5-dimethyl-2-thiazolyl)-2,5-diphenyl-2-H-tetrazolium bromide(MTT)assay after coating SiO_2/ZnS,and also proved the feasibility of using the hybrid SiO_2/ZnS coated QDs as optical probes for in vitro cell imaging.The synthesis method of QDs is highly promising for the production of robust and functional optical probes for bio-imaging and sensing applications.展开更多
目的制备毒性低,生物相容性好的新型半导体量子点。方法以还原型谷胱甘肽（GSH）为硫源和稳定剂,采用水热法合成Cd Te/Cd S QDs。结果制备的GSH包裹的Cd Te/Cd S QDs波长范围覆盖400~800 nm的区域,量子产率高达83.1%,平均粒径约为3 nm...目的制备毒性低,生物相容性好的新型半导体量子点。方法以还原型谷胱甘肽（GSH）为硫源和稳定剂,采用水热法合成Cd Te/Cd S QDs。结果制备的GSH包裹的Cd Te/Cd S QDs波长范围覆盖400~800 nm的区域,量子产率高达83.1%,平均粒径约为3 nm。结论该Cd Te/Cd S QDs制备方法简便,成本低,有效降低了量子点生物毒性。展开更多
Cadmium telluride thin films were prepared by vacuum evaporation of CdTe powder in an attempt to fabricate all thin film solar cells of the type CdTe/CdS.Characterization of CdTe has shown it to have a band gap of 1.5...Cadmium telluride thin films were prepared by vacuum evaporation of CdTe powder in an attempt to fabricate all thin film solar cells of the type CdTe/CdS.Characterization of CdTe has shown it to have a band gap of 1.522eV and a resistivity of 22Ω-cm.As prepared,solar cells exhibited low values of output parameters.Given quantity of copper was then deposited on top of the CdTe/CdS solar cells and the whole system was annealed at 350℃.This copper doping changed the output parameters favorably with a maximum efficiency of 1.9%.展开更多
We report high-efficiency CdTe/CdS core/shell nanocrystals synthesized in water by epitaxially growing CdS shells on aqueous CdTe cores at room temperature, enabled by the controlled release of S species under low-int...We report high-efficiency CdTe/CdS core/shell nanocrystals synthesized in water by epitaxially growing CdS shells on aqueous CdTe cores at room temperature, enabled by the controlled release of S species under low-intensity ultraviolet （UV） light illumination. The resulting photo-induced dissociation of S2O2- ions conveniently triggers the formation of critical two-dimensional CdS epitaxy on the CdTe surface at room temperature, as opposed to initiating the growth of individual CdS core-only nanocrystals. This controlled colloidal hetero-epitaxy leads to a substantial increase in the photoluminescence （PL） quantum yield （QY） of the shelled nanocrystals in water （reaching 64%）. With a systematic set of studies, the maximum PL QY is found to be almost independent of the illuminating UV intensity, while the shell formation kinetics required for reaching the maximum QY linearly depends on the illuminating UV intensity. A stability study of the QD films in air at various temperatures shows highly improved thermal stability of the shelled QDs （up to 120 ℃ in ambient air）. These results indicate that the proposed aqueous CdTe/CdS core/shell nanocrystals hold great promise for applications requiring efficiency and stability.展开更多
CdTe/CdS quantum dots（QDs） are fabricated on Si nanowires（NWs） substrates with and without Au nanoparticles（NPs）. The formation of Au NPs on Si NWs can be certified as shown in scanning electron microscopy image...CdTe/CdS quantum dots（QDs） are fabricated on Si nanowires（NWs） substrates with and without Au nanoparticles（NPs）. The formation of Au NPs on Si NWs can be certified as shown in scanning electron microscopy images. The optical properties of samples are also investigated. It is interesting to find that the photoluminescence（PL） intensity of Cd Te/Cd S QD films on Si nanowire substrates with Au NPs is significantly increased,which can reach 8-fold higher than that of samples on planar Si without Au NPs. The results of finite-difference time-domain simulation indicate that Au NPs induce stronger localization of electric field and then boost the PL intensity of QDs nearby. Furthermore, the time-resolved luminescence decay curve shows the PL lifetime, which is about 5.5 ns at the emission peaks of QD films on planar, increasing from 1.8 ns of QD films on Si NWs to4.7 ns after introducing Au NPs into Si NWs.展开更多
文摘In this paper, a comparative study of the maximum power on the shading rate on the maximum power of thin film PV modules. Thus two thin film PV modules of type Copper indium gallium selenide, CIGS, of 90W power and a CdTe (Cadmium telluride)/CdS (Cadmium sulfide) module, of maximum power 75 W. These modules, reference SN-CIGS90 and CX3 75 were tested under the conditions of the installation site to ensure their proper functioning and to determine the initial values of electrical parameters before shading. The results obtained are as follows: for the CIGS: Pm (80.717 W);Vco (23.06 V), Icc (3.5 A) and for the CdTe:Pm (54.914 W);Vco (35.52 V), Icc (1.546 A). After this characterization test, the modules are exposed to real operating conditions at the Center for Study and Research on the renewable energy (CERER), Cheikh Anta Diop University in Dakar. Four types of shading are performed on each module with the same mask: partial shading at 25%, 50%, 75% and complete shading at 100%. The comparison of the variation rates obtained on the experimental values of the 4 types of shading carried out on each module, shows that, the phenomenon of shading constitutes an environmental factor which influences negatively the maximum power of the thin film PV modules. But this reduction depends on the surface of the shaded module, the nature of the mask but also the technology used. Indeed, for a shading of 25% of the surface of the two modules, we note a reduction of 21.32% of power for the CIGS, against 40.53% for the CdTe/CdS, that is to say a difference which approaches 20%.
基金supported by the National Natural Science Foundation of China(No.20705019)National High-Tech R&D Program(No.2006AA03Z324)
文摘In the study, we observed the strong adsorption of CdTe/CdS QDs to antibodies and the formation of QDs-antibodies conjugates. Capillary electrophoresis with laser-induced fluorescence detection （CE-LIF）, fluorescence spectrometry and fluorescence correlation spectroscopy （FCS） were used to characterize the QDs conjugates with antibody. We found that the QDs-antibody conjugates possessed high fluorescence, small hydrodynamic radii and good stability in aqueous solution. 2009 Ji Cun Ren. Published by Elsevier B.V. on behalf of Chinese Chemical Society. All rights reserved.
基金The Fundamental Research Funds for the Central Universities,China(No.2232015D3-15)Shanghai Natural Science Foundation,China(No.14ZR1401300)“111 Project”Biomedical Textile Materials Science and Technology,China(No.B07024)
文摘Novel CdTe/CdS quantum dots(QDs)coated with a hybrid of SiO_2 and ZnS were fabricated through a simple two-step approach.The hybrid SiO_2/ZnS coated CdTe/CdS quantum dots was characterized by transmission electron microscopy(TEM),UV and fluorescence spectrometer.Results indicated that the core-shell structure gave the QDs outstanding photoluminescence properties,includinganarrowphotoluminescencespectrum,high photoluminescence(PL)quantum yield and long emission lifetime(average PL lifetime of increased from 26.4 ns to 49.1 ns).Cellular studies showed the QDs had good cytocompatibility with Hela cells as determined by the 3-(4,5-dimethyl-2-thiazolyl)-2,5-diphenyl-2-H-tetrazolium bromide(MTT)assay after coating SiO_2/ZnS,and also proved the feasibility of using the hybrid SiO_2/ZnS coated QDs as optical probes for in vitro cell imaging.The synthesis method of QDs is highly promising for the production of robust and functional optical probes for bio-imaging and sensing applications.
文摘目的制备毒性低,生物相容性好的新型半导体量子点。方法以还原型谷胱甘肽（GSH）为硫源和稳定剂,采用水热法合成Cd Te/Cd S QDs。结果制备的GSH包裹的Cd Te/Cd S QDs波长范围覆盖400~800 nm的区域,量子产率高达83.1%,平均粒径约为3 nm。结论该Cd Te/Cd S QDs制备方法简便,成本低,有效降低了量子点生物毒性。
文摘Cadmium telluride thin films were prepared by vacuum evaporation of CdTe powder in an attempt to fabricate all thin film solar cells of the type CdTe/CdS.Characterization of CdTe has shown it to have a band gap of 1.522eV and a resistivity of 22Ω-cm.As prepared,solar cells exhibited low values of output parameters.Given quantity of copper was then deposited on top of the CdTe/CdS solar cells and the whole system was annealed at 350℃.This copper doping changed the output parameters favorably with a maximum efficiency of 1.9%.
文摘We report high-efficiency CdTe/CdS core/shell nanocrystals synthesized in water by epitaxially growing CdS shells on aqueous CdTe cores at room temperature, enabled by the controlled release of S species under low-intensity ultraviolet （UV） light illumination. The resulting photo-induced dissociation of S2O2- ions conveniently triggers the formation of critical two-dimensional CdS epitaxy on the CdTe surface at room temperature, as opposed to initiating the growth of individual CdS core-only nanocrystals. This controlled colloidal hetero-epitaxy leads to a substantial increase in the photoluminescence （PL） quantum yield （QY） of the shelled nanocrystals in water （reaching 64%）. With a systematic set of studies, the maximum PL QY is found to be almost independent of the illuminating UV intensity, while the shell formation kinetics required for reaching the maximum QY linearly depends on the illuminating UV intensity. A stability study of the QD films in air at various temperatures shows highly improved thermal stability of the shelled QDs （up to 120 ℃ in ambient air）. These results indicate that the proposed aqueous CdTe/CdS core/shell nanocrystals hold great promise for applications requiring efficiency and stability.
基金Supported by the Qing Lan Project of the Higher Education Institutions of Jiangsu Province,Qing Lan Project of Yangzhou Polytechnic Institute,the Natural Science Foundation of Yangzhou City under Grant No YZ2016123the National Natural Science Foundation of China under Grant No 61376004
文摘CdTe/CdS quantum dots（QDs） are fabricated on Si nanowires（NWs） substrates with and without Au nanoparticles（NPs）. The formation of Au NPs on Si NWs can be certified as shown in scanning electron microscopy images. The optical properties of samples are also investigated. It is interesting to find that the photoluminescence（PL） intensity of Cd Te/Cd S QD films on Si nanowire substrates with Au NPs is significantly increased,which can reach 8-fold higher than that of samples on planar Si without Au NPs. The results of finite-difference time-domain simulation indicate that Au NPs induce stronger localization of electric field and then boost the PL intensity of QDs nearby. Furthermore, the time-resolved luminescence decay curve shows the PL lifetime, which is about 5.5 ns at the emission peaks of QD films on planar, increasing from 1.8 ns of QD films on Si NWs to4.7 ns after introducing Au NPs into Si NWs.