To study the influence of multi-wall carbon nanotubes （MWCNTs） on the mechanical and microstructural properties of cementitious composites, 0.00, 0.02, 0.08, 0.10, and 0.20 wt% of multi-wall carbon nanotubes were ad...To study the influence of multi-wall carbon nanotubes （MWCNTs） on the mechanical and microstructural properties of cementitious composites, 0.00, 0.02, 0.08, 0.10, and 0.20 wt% of multi-wall carbon nanotubes were added into cement mortar, in which the cement-sand ratio was 1：1.5. The flexural and compressive strengths of cement mortar at the age of 3, 7, 28 and 90 d and the fracture performance at the age of 28 d were determined, its 2D micrograph was tested by means of SEM, and the 3D defects distribution was firstly determined with or without CNTs by means of XCT （X-ray computerized tomography）. The results showed that 0.08 wt% of CNTs improved the compressive strength and flexural strength by 18% and 19~A, respectively, and a significant improvement of its fracture property was observed. Moreover lower addition of carbon nanotubes to cement mortars can improve its microstructure and decrease the defects significantly compared to the cement mortar without CNTs. With the increase of the content of CNTs, the mechanical properties of cement mortars presented to be declined largely due to the agglomeration of CNTs.展开更多
The surface of carbon nanotubes(CNTs)was modified by plasma to improve the dispersion,conductivity and adsorption properties of carbon nanotubes.Cement-based composites made with plasmatreated carbon nanotubes(P-CNTs)...The surface of carbon nanotubes(CNTs)was modified by plasma to improve the dispersion,conductivity and adsorption properties of carbon nanotubes.Cement-based composites made with plasmatreated carbon nanotubes(P-CNTs)at different perntages were tested under repeated cyclic axial compressive stress by four electrode methods to measure the electric resistance.Those made with CNTs without plasma treatment as controls were tested also.The results showed that electric resistance change values of the cement mortar with P-CNT and CNT were all monatomic corresponding to the cyclic loading.When the water-cement ratio of the mortar was fixed,increasing of the P-CNT/CNT content would increase the resistance change value of the mortars added with P-CNT/CNT,and the sensitivity performance.It has certain engineering application value.展开更多
基金Funded by the National Basic Research Program of China(No.2009CB623200)the Program for Changjiang Scholars and Innovative Research Team in University of China(No.IRT13075)
文摘To study the influence of multi-wall carbon nanotubes （MWCNTs） on the mechanical and microstructural properties of cementitious composites, 0.00, 0.02, 0.08, 0.10, and 0.20 wt% of multi-wall carbon nanotubes were added into cement mortar, in which the cement-sand ratio was 1：1.5. The flexural and compressive strengths of cement mortar at the age of 3, 7, 28 and 90 d and the fracture performance at the age of 28 d were determined, its 2D micrograph was tested by means of SEM, and the 3D defects distribution was firstly determined with or without CNTs by means of XCT （X-ray computerized tomography）. The results showed that 0.08 wt% of CNTs improved the compressive strength and flexural strength by 18% and 19~A, respectively, and a significant improvement of its fracture property was observed. Moreover lower addition of carbon nanotubes to cement mortars can improve its microstructure and decrease the defects significantly compared to the cement mortar without CNTs. With the increase of the content of CNTs, the mechanical properties of cement mortars presented to be declined largely due to the agglomeration of CNTs.
基金Funded by National Natural Science Foundation of China(No.52178149)。
文摘The surface of carbon nanotubes(CNTs)was modified by plasma to improve the dispersion,conductivity and adsorption properties of carbon nanotubes.Cement-based composites made with plasmatreated carbon nanotubes(P-CNTs)at different perntages were tested under repeated cyclic axial compressive stress by four electrode methods to measure the electric resistance.Those made with CNTs without plasma treatment as controls were tested also.The results showed that electric resistance change values of the cement mortar with P-CNT and CNT were all monatomic corresponding to the cyclic loading.When the water-cement ratio of the mortar was fixed,increasing of the P-CNT/CNT content would increase the resistance change value of the mortars added with P-CNT/CNT,and the sensitivity performance.It has certain engineering application value.