Novel 3D biogenic C-doped Bi_2 MoO_6/In_2O_3-ZnO Z-scheme heterojunctions were synthesized for the first time, using cotton fiber as template. The as-prepared samples showed excellent adsorption and photodegradation p...Novel 3D biogenic C-doped Bi_2 MoO_6/In_2O_3-ZnO Z-scheme heterojunctions were synthesized for the first time, using cotton fiber as template. The as-prepared samples showed excellent adsorption and photodegradation performance toward the hazardous antibiotic doxycycline under simulated sunlight irradiation. The morphology, phase composition and in situ carbon doping could be precisely controlled by adjusting processing parameters. The carbon doping in Bi_2 MoO_6/In_2O_3-ZnO was derived from the cotton template, and the carbon content could be varied in the range 0.9–4.4 wt.% via controlling the heat treatment temperature. The sample with Bi_2 MoO_6/In_2O_3-ZnO molar ratio of 1:2 and carbon content of1.1 wt.% exhibited the highest photocatalytic activity toward doxycycline degradation,which was 3.6 and 4.3 times higher than those of pure Bi_2 MoO_6 and Zn In Al-CLDH(calcined layered double hydroxides), respectively. It is believed that the Z-scheme heterojunction with C-doping, the 3D hierarchically micro–meso–macro porous structure, as well as the high adsorption capacity, contributed significantly to the enhanced photocatalytic activity.展开更多
Recently,sodium-ion batteries gradually become the promising alternative to lithium-ion batteries because of cost considerations.In this work,a kind of Bi2MoO6 nanosheets@N,S codoped graphene composite is designed and...Recently,sodium-ion batteries gradually become the promising alternative to lithium-ion batteries because of cost considerations.In this work,a kind of Bi2MoO6 nanosheets@N,S codoped graphene composite is designed and fabricated for sodium storage applications.Detailed characterizations are employed to investigate its morphology,structure and chemical compositions.When evaluated as an anode material for sodium-ion batteries,the as-prepared composite is able to display a specific capacity of 254 mA·h/g after 50 cycles at a current density of 0.2 A/g,and 186 mA·h/g at 1.6 A/g during the rate capability test.As a result,the further morphology and structure optimization is still required for high performance sodium-ion batteries.展开更多
Mesh-like Bi2MoO6 product was successfully synthesized by a hydrothermal method without using any surfactant or template. The pH value played an important role in the formation of this morphology. The as-prepared mesh...Mesh-like Bi2MoO6 product was successfully synthesized by a hydrothermal method without using any surfactant or template. The pH value played an important role in the formation of this morphology. The as-prepared mesh-like Bi2MoO6 sample exhibited excellent visible-light-driven photocatalytic e ciency. The photocatalytic activity of the mesh-like Bi2MoO6 sample was much higher than that of bulk Bi2MoO6 sample prepared by solid-state reac-tion. Di erence in the photocatalytic activities of the mesh-like Bi2MoO6 sample and bulk Bi2MoO6 sample was further investigated.展开更多
The fabrication of multicomponent composite systems may provide bene ts in terms of charge separation and the retardation of charge pair recombination. In this work, a ternary heterostructured Ag-Bi2MoO6/BiPO4 composi...The fabrication of multicomponent composite systems may provide bene ts in terms of charge separation and the retardation of charge pair recombination. In this work, a ternary heterostructured Ag-Bi2MoO6/BiPO4 composite was fabricated through a low-temperature solution-phase route for the rst time. The XRD, SEM, EDX and XPS results indicated the prepared sample is a three-phase composite of BiPO4, Bi2MoO6, and Ag. Ag nanopar-ticles were photodeposited on the surface of Bi2MoO6/BiPO4 nanosheets, which not only increase visible-light absorption via the surface plasmon resonance, but also serve as good electron acceptor for facilitating quick photoexcited electron transfer. The interface between Bi2MoO6 and BiPO4 facilitates the migration of photoinduced electrons from Bi2MoO6 to BiPO4, which is also conductive to reduce the recombination of electron-holes. Thus, the ternary heterostructured Ag-Bi2MoO6/BiPO4 composite showed signi cant photocatalytic activity, higher than pure Bi2MoO6, BiPO4, and Bi2MoO6/BiPO4. Moreover, the possible photocatalytic mechanism of the Ag-Bi2MoO6/BiPO4 heterostructure related to the band positions of the semiconductors was also discussed. In addition, the quenching effects of di erent scavengers revealed that the reactive ·OH and O2·- play a major role in the phenol red decolorization.展开更多
基金supported by the National Natural Science Foundation of China(No.51672110)HKSAR(Hong Kong Special Administrative Region)Government RGC-GRF(The Research Grants Council-General Research Fund)Grant(No.CUHK14303914)a Direct Grant(No.3132731)from the Faculty of Science,The Chinese University of Hong Kong
文摘Novel 3D biogenic C-doped Bi_2 MoO_6/In_2O_3-ZnO Z-scheme heterojunctions were synthesized for the first time, using cotton fiber as template. The as-prepared samples showed excellent adsorption and photodegradation performance toward the hazardous antibiotic doxycycline under simulated sunlight irradiation. The morphology, phase composition and in situ carbon doping could be precisely controlled by adjusting processing parameters. The carbon doping in Bi_2 MoO_6/In_2O_3-ZnO was derived from the cotton template, and the carbon content could be varied in the range 0.9–4.4 wt.% via controlling the heat treatment temperature. The sample with Bi_2 MoO_6/In_2O_3-ZnO molar ratio of 1:2 and carbon content of1.1 wt.% exhibited the highest photocatalytic activity toward doxycycline degradation,which was 3.6 and 4.3 times higher than those of pure Bi_2 MoO_6 and Zn In Al-CLDH(calcined layered double hydroxides), respectively. It is believed that the Z-scheme heterojunction with C-doping, the 3D hierarchically micro–meso–macro porous structure, as well as the high adsorption capacity, contributed significantly to the enhanced photocatalytic activity.
文摘Recently,sodium-ion batteries gradually become the promising alternative to lithium-ion batteries because of cost considerations.In this work,a kind of Bi2MoO6 nanosheets@N,S codoped graphene composite is designed and fabricated for sodium storage applications.Detailed characterizations are employed to investigate its morphology,structure and chemical compositions.When evaluated as an anode material for sodium-ion batteries,the as-prepared composite is able to display a specific capacity of 254 mA·h/g after 50 cycles at a current density of 0.2 A/g,and 186 mA·h/g at 1.6 A/g during the rate capability test.As a result,the further morphology and structure optimization is still required for high performance sodium-ion batteries.
文摘Mesh-like Bi2MoO6 product was successfully synthesized by a hydrothermal method without using any surfactant or template. The pH value played an important role in the formation of this morphology. The as-prepared mesh-like Bi2MoO6 sample exhibited excellent visible-light-driven photocatalytic e ciency. The photocatalytic activity of the mesh-like Bi2MoO6 sample was much higher than that of bulk Bi2MoO6 sample prepared by solid-state reac-tion. Di erence in the photocatalytic activities of the mesh-like Bi2MoO6 sample and bulk Bi2MoO6 sample was further investigated.
文摘The fabrication of multicomponent composite systems may provide bene ts in terms of charge separation and the retardation of charge pair recombination. In this work, a ternary heterostructured Ag-Bi2MoO6/BiPO4 composite was fabricated through a low-temperature solution-phase route for the rst time. The XRD, SEM, EDX and XPS results indicated the prepared sample is a three-phase composite of BiPO4, Bi2MoO6, and Ag. Ag nanopar-ticles were photodeposited on the surface of Bi2MoO6/BiPO4 nanosheets, which not only increase visible-light absorption via the surface plasmon resonance, but also serve as good electron acceptor for facilitating quick photoexcited electron transfer. The interface between Bi2MoO6 and BiPO4 facilitates the migration of photoinduced electrons from Bi2MoO6 to BiPO4, which is also conductive to reduce the recombination of electron-holes. Thus, the ternary heterostructured Ag-Bi2MoO6/BiPO4 composite showed signi cant photocatalytic activity, higher than pure Bi2MoO6, BiPO4, and Bi2MoO6/BiPO4. Moreover, the possible photocatalytic mechanism of the Ag-Bi2MoO6/BiPO4 heterostructure related to the band positions of the semiconductors was also discussed. In addition, the quenching effects of di erent scavengers revealed that the reactive ·OH and O2·- play a major role in the phenol red decolorization.