平纹编织SiC_(f)/SiC复合材料的中温蠕变断裂时间及损伤机制 被引量:3
1
作者 朱思雨 张巧君 +6 位作者 洪智亮 荆开开 管皞阳 程赞粼 刘永胜 王波 张程煜 《复合材料学报》 EI CAS CSCD 北大核心 2023年第1期464-471,共8页
碳化硅纤维增强碳化硅复合材料(SiC_(f)/SiC)是制造下一代航空发动机热结构件的关键材料,中等温度(~800℃)下,SiC_(f)/SiC的蠕变断裂时间t_(u)显著下降。为此,研究了平纹编织SiC_(f)/SiC(2D-SiC_(f)/SiC)在空气中500~1000℃的蠕变性能... 碳化硅纤维增强碳化硅复合材料(SiC_(f)/SiC)是制造下一代航空发动机热结构件的关键材料,中等温度(~800℃)下,SiC_(f)/SiC的蠕变断裂时间t_(u)显著下降。为此,研究了平纹编织SiC_(f)/SiC(2D-SiC_(f)/SiC)在空气中500~1000℃的蠕变性能及损伤机制,应力水平为100~160 MPa。利用SEM、TEM和EDS分析了断口形貌、微观组织和化学成分。结果表明:2D-SiC_(f)/SiC的t_(u)与温度和应力水平有关。相同温度下,2D-SiC_(f)/SiC的t_(u)随着应力增加而变短。当温度为800℃、蠕变应力大于基体开裂应力(PLS)时,2D-SiC_(f)/SiC发生中温脆化现象,其t_(u)下降。2D-SiC_(f)/SiC的中温脆化机制为基体开裂、BN界面氧化和SiO_(2)替代BN界面导致的强界面/基体结合。2D-SiC_(f)/SiC的t_(u)与应力在对数坐标下呈线性关系,且在过渡应力时发生线性转变,过渡应力与PLS一致。提高PLS能够有效提高SiC_(f)/SiC的t_(u)。 展开更多
关键词 SiC_(f)/SiC复合材料 蠕变断裂时间 bn界面 氧化 损伤机制
原文传递
SiC_f/SiC复合材料氮化硼(BN)界面层及其复合界面层研究进展 被引量:12
2
作者 吕晓旭 齐哲 +5 位作者 赵文青 姜卓钰 杨金华 周怡然 刘虎 焦健 《航空材料学报》 EI CAS CSCD 北大核心 2019年第5期13-23,共11页
SiC_f/SiC复合材料由SiC纤维、SiC基体和界面层组成。界面层可以传递载荷和偏转裂纹,同时防止SiC纤维受到材料制备和使用过程中的化学侵蚀,对于调节SiC_f/SiC复合材料的性能具有非常重要的作用。本文综述了氮化硼界面层的晶体结构、复... SiC_f/SiC复合材料由SiC纤维、SiC基体和界面层组成。界面层可以传递载荷和偏转裂纹,同时防止SiC纤维受到材料制备和使用过程中的化学侵蚀,对于调节SiC_f/SiC复合材料的性能具有非常重要的作用。本文综述了氮化硼界面层的晶体结构、复合界面层的种类,介绍了化学气相渗透法制备氮化硼(boron nitride,BN)及其复合界面层的工艺条件,总结了先驱体气体比例、载气、沉积压力及温度等工艺条件对界面层沉积速率、微观形貌结构的影响。选择合适的工艺条件,制备理想结构的BN及其复合界面层,将是SiC_f/SiC复合材料界面层研究领域的重点和难点。 展开更多
关键词 SICF/SIC复合材料 化学气相渗透 bn界面 复合界面
下载PDF
SiC晶须增强SiC_(f)/SiC复合材料的力学性能 被引量:5
3
作者 姜卓钰 束小文 +4 位作者 吕晓旭 高晔 周怡然 董禹飞 焦健 《材料工程》 EI CAS CSCD 北大核心 2021年第8期89-96,共8页
以连续SiC纤维为增强体,采用前驱体浸渍裂解工艺,在复合材料基体中引入SiC晶须制备出多级增强的SiC_(f)/SiC-SiC_(w)复合材料,并采用化学气相渗透工艺在SiC晶须表面制备BN界面层,研究了SiC晶须及其表面BN界面层对复合材料的性能影响。... 以连续SiC纤维为增强体,采用前驱体浸渍裂解工艺,在复合材料基体中引入SiC晶须制备出多级增强的SiC_(f)/SiC-SiC_(w)复合材料,并采用化学气相渗透工艺在SiC晶须表面制备BN界面层,研究了SiC晶须及其表面BN界面层对复合材料的性能影响。结果表明:在复合材料中引入SiC晶须后,由于晶须的拔出、桥连及裂纹偏转等作用增加了裂纹在基体中传递时的能量消耗,使SiC_(f)/SiC复合材料的压缩强度有明显提高,当引入体积分数为20%的SiC晶须时,复合材料压缩强度提高了22.6%,可达673.9 MPa。通过化学气相渗透工艺在SiC晶须表面制备BN界面层后,复合材料的拉伸强度、弯曲强度和断裂韧度分别为414.0,800.3 MPa和22.2 MPa·m^(1/2),较SiC晶须表面无界面层时分别提高了13.9%,8.8%和19.0%。 展开更多
关键词 陶瓷基复合材料 SIC晶须 力学性能 bn界面
下载PDF
不同界面层体系对SiC_f/SiC复合材料性能的影响 被引量:4
4
作者 庞宝琳 焦健 +5 位作者 王宇 邱海鹏 李秀倩 陈明伟 邹豪 高淑雅 《航空制造技术》 北大核心 2014年第6期79-82,85,共5页
主要研究无界面层、裂解碳和氮化硼3种界面层体系对SiCf/SiC复合材料力学性能的影响:首先,三维四向编织的SiC纤维预制体分别经过无界面层处理、裂解碳界面层制备(CVI工艺)和BN界面层制备(PIP工艺)3种不同工艺处理;以聚碳硅烷为原料,采用... 主要研究无界面层、裂解碳和氮化硼3种界面层体系对SiCf/SiC复合材料力学性能的影响:首先,三维四向编织的SiC纤维预制体分别经过无界面层处理、裂解碳界面层制备(CVI工艺)和BN界面层制备(PIP工艺)3种不同工艺处理;以聚碳硅烷为原料,采用PIP工艺制备出3种SiCf/SiC陶瓷基复合材料工艺试验件;对工艺试验件的基本力学性进行研究,评价不同纤维预制体处理工艺对材料性能的影响。研究结果表明,无涂层复合材料样品的弯曲强度最高;具有PyC涂层复合材料的弯曲强度略有下降,但断裂韧性较高;具有BN界面层的复合材料弯曲强度和断裂韧性均出现了较大程度的降低。3个样品力学性能的差别主要与纤维/界面层/基体之间作用力有关。本研究结果可以用于SiCf/SiC复合材料构件制造工作中,为制造工艺的初步筛选提供参考依据。 展开更多
关键词 SICF SIC复合材料 PIP工艺 PyC界面 bn界面
下载PDF
Effects of dip-coated BN interphase on mechanical properties of SiC_f/SiC composites prepared by CVI process 被引量:2
5
作者 周洋 周万城 +1 位作者 罗发 朱冬梅 《Transactions of Nonferrous Metals Society of China》 SCIE EI CAS CSCD 2014年第5期1400-1406,共7页
BN interphase was successfully synthesized on SiC fiber fabrics by dip-coating process using boric acid and urea as precursors under N2 atmosphere. The morphology of BN interphase was observed by SEM, and the structur... BN interphase was successfully synthesized on SiC fiber fabrics by dip-coating process using boric acid and urea as precursors under N2 atmosphere. The morphology of BN interphase was observed by SEM, and the structure was characterized by XRD and FT-IR spectra. The SiCf/SiC composites with dip-coated BN interphase were fabricated by chemical vapor infiltration (CVI) process, and the effects ofBN interphase on the mechanical properties of composites were investigated. The results show that the SiC fibers are fully covered by BN interphase with smooth surface and turbostratic structure (t-BN), and the thickness is about 0.4 μm. The flexural strengths of SiCf/SiC composites with and without BN interphase are about 180 and 95 MPa, respectively. Compared with the as-received SiCf/SiC composites, the composites with BN interphase exhibit an obvious toughened fracture behavior. From the microstructural analysis, it can be confirmed that the BN interphase plays a key part in protecting the fibers from chemical attack during matrix infiltration and weakening interfacial bonding, which can improve the mechanical properties of SiCf/SiC composites remarkably. 展开更多
关键词 SiCf/SiC composites bn interphase DIP-COATING CVI mechanical properties
下载PDF
热处理温度对BN界面涂层微观结构和相稳定性的影响 被引量:1
6
作者 戴建伟 刘德林 +3 位作者 牟仁德 何利民 王鑫 许振华 《失效分析与预防》 2021年第2期113-118,共6页
采用化学气相渗透工艺在SiC纤维表面制备BN界面涂层,在比沉积温度更高的温度下分别对涂层进行热处理。采用扫描电镜、透射电镜、拉曼光谱、X射线光电子能谱等技术,对BN界面涂层的微观结构和化学成分进行分析,并对涂层进行相稳定性能研... 采用化学气相渗透工艺在SiC纤维表面制备BN界面涂层,在比沉积温度更高的温度下分别对涂层进行热处理。采用扫描电镜、透射电镜、拉曼光谱、X射线光电子能谱等技术,对BN界面涂层的微观结构和化学成分进行分析,并对涂层进行相稳定性能研究。结果表明:在850℃沉积的BN界面涂层分别在1050、1150、1250℃下进行热处理,BN均发生有序化转变,非晶态的BN转变为六方相;并且随着热处理温度的增加,BN结晶度增加。未经高温热处理的非晶态BN涂层易氧化,部分BN和空气反应生成B2O3;并且,在室温至1200℃时相稳定性差;经过热处理的涂层中几乎全部为BN,在室温至1200℃时无相变。 展开更多
关键词 化学气相渗透 bn界面涂层 高温热处理 微观结构 相稳定性能
下载PDF
KD-S型SiC纤维表面BN界面层Raman光谱研究
7
作者 刘海山 谭瑞轩 +3 位作者 王洪磊 葛斌 周新贵 余金山 《光谱学与光谱分析》 SCIE EI CAS CSCD 北大核心 2018年第S1期215-216,共2页
由于SiC纤维具有高强度、高模量、强抗化学腐蚀性等优越性能,因此广泛用于陶瓷基复合材料的增强当中。但在高温下制备复合材料,容易使纤维与基体之间形成牢固的附着力,导致复合材料力学性能差,因此需要界面层使纤维与基体间的结合足够弱... 由于SiC纤维具有高强度、高模量、强抗化学腐蚀性等优越性能,因此广泛用于陶瓷基复合材料的增强当中。但在高温下制备复合材料,容易使纤维与基体之间形成牢固的附着力,导致复合材料力学性能差,因此需要界面层使纤维与基体间的结合足够弱。BN具有良好的耐热性、抗氧化性和微裂纹自愈合能力,可用于解决SiC纤维增强SiC基复合材料的界面问题。CVD法是常用的制备BN界面层的工艺方法。本文以BCl3-NH_3为原料,在较低温度下通过CVD工艺制备了BN界面层。 展开更多
关键词 SIC纤维 CVD bn界面
下载PDF
CVD BN界面层对Si_(3)N_(4)/SiBN复合材料弯曲性能的影响
8
作者 马新 邱海鹏 +5 位作者 梁艳媛 刘善华 王晓猛 赵禹良 陈明伟 谢巍杰 《材料导报》 EI CAS CSCD 北大核心 2021年第S02期86-89,共4页
连续Si_(3)N_(4)纤维以其优异的热稳定性、高温力学性能和介电性能,被认为是耐高温陶瓷基透波复合材料的候选材料之一。采用连续Si_(3)N_(4)纤维为增强体,以BCl_(3)+NH_(3)+H_(2)+Ar反应体系,利用化学气相沉积工艺在Si_(3)N_(4)纤维表... 连续Si_(3)N_(4)纤维以其优异的热稳定性、高温力学性能和介电性能,被认为是耐高温陶瓷基透波复合材料的候选材料之一。采用连续Si_(3)N_(4)纤维为增强体,以BCl_(3)+NH_(3)+H_(2)+Ar反应体系,利用化学气相沉积工艺在Si_(3)N_(4)纤维表面制备了BN界面层,并以聚硅硼氮烷为陶瓷先驱体,通过先驱体浸渍裂解工艺制备了Si_(3)N_(4)/SiBN复合材料。研究了CVD BN界面层的合成及其对Si_(3)N_(4)/SiBN复合材料弯曲性能的影响。结果表明:在Si_(3)N_(4)纤维表面获得了均匀致密的BN界面层,该界面层有效改善了复合材料中纤维/基体的界面结合力,复合材料显示出典型的韧性断裂特征。当界面层的厚度为200 nm时,Si_(3)N_(4)/SiBN的弯曲强度和断裂韧性分别为182.3 MPa和17.3 MPa·m^(1/2),比无涂层的复合材料分别提高了59.6%和94.4%。 展开更多
关键词 连续纤维增强陶瓷基复合材料 化学气相沉积 先驱体浸渍裂解 bn界面 力学性能
下载PDF
多层界面相对SiC_(f)/SiC复合材料综合性能的影响
9
作者 康治伟 李志伟 +3 位作者 彭雨晴 王梦千 张方舟 李艳 《现代技术陶瓷》 CAS 2022年第4期282-293,共12页
界面相的存在对于SiC_(f)/SiC复合材料的力学性能和抗氧化性能有重要影响,选择合适的界面相对于复合材料本身性能至关重要。本工作采用化学气相渗透工艺制备了具有三种不同界面的SiC_(f)/SiC复合材料,即:SiC/BN/SiC;SiC/(BN-SiC)/SiC和S... 界面相的存在对于SiC_(f)/SiC复合材料的力学性能和抗氧化性能有重要影响,选择合适的界面相对于复合材料本身性能至关重要。本工作采用化学气相渗透工艺制备了具有三种不同界面的SiC_(f)/SiC复合材料,即:SiC/BN/SiC;SiC/(BN-SiC)/SiC和SiC/(BN-SiC-BN)/SiC,研究了多层界面相对材料本身力学性能和抗氧化性能影响。结果表明,界面相的存在有利于维持并提高材料本身的力学性能和抗氧化性能,并且在三种复合材料中,SiC/(BN-SiC-BN)/SiC复合材料在1200℃高温有氧环境强度保有率最高约为95%,并且呈现出更好的自愈合能力。 展开更多
关键词 SiC_(f)/SiC bn-SiC-bn多层界面 力学性能 抗氧化性
原文传递