采用氢氧化钠-硫脲-尿素水溶液在中高温条件下处理稻草盘磨机械浆,通过用碱量、纤维浓度、处理温度和处理时间等参数的单因素试验探究该溶剂对稻草纤维成纸强度性能的影响。研究表明:在用碱量4%、处理时间40m i n、处理温度50℃、纤维浓...采用氢氧化钠-硫脲-尿素水溶液在中高温条件下处理稻草盘磨机械浆,通过用碱量、纤维浓度、处理温度和处理时间等参数的单因素试验探究该溶剂对稻草纤维成纸强度性能的影响。研究表明:在用碱量4%、处理时间40m i n、处理温度50℃、纤维浓度15%的条件下,稻草机械浆的强度性能最佳,以原浆强度为参比,经处理后纤维的抗张指数和耐破指数分别提高75.6%和80.9%,同时其成纸松厚度下降13.6%,但耐折度无明显变化。此外,处理前后浆料纤维无定形区和结晶区的整体结构不受影响,纤维中碳、氢、氧三种元素的质量比没有明显变化,但氮元素含量降低明显。展开更多
The aim of this work is optimizing the techniques to prepare pure cellulose microspheres, which are used as packing adsorbents for high-performance liquid chromatography. Thereupon, cellulose was dissolved in a pre-co...The aim of this work is optimizing the techniques to prepare pure cellulose microspheres, which are used as packing adsorbents for high-performance liquid chromatography. Thereupon, cellulose was dissolved in a pre-cooled NaOH/urea solution, from which various-size microspheres were prepared. The volume-average diameters were controlled approximately at 30 p,m, 8 ~tm and 4 pm grades when cyclohexane, liquid paraffin and pump oil were used as dispersants, respectively. The present investigations reveal that higher viscosity dispersant is suitable for the preparation of smaller-size microspheres, while larger size microspheres are prepared preferably using lower-viscosity dispersant. The chiral stationary phase derived from 8 μm grade microspheres can separate the enantiomers of efavirenz.展开更多
Hydroxypropyl celluloses(HPC) were homogenously synthesized by the reaction of cellulose with propylene oxide in NaOH/urea aqueous solution.Water-soluble HPC with molar degree of substitution(MSNMR) in the range of 0....Hydroxypropyl celluloses(HPC) were homogenously synthesized by the reaction of cellulose with propylene oxide in NaOH/urea aqueous solution.Water-soluble HPC with molar degree of substitution(MSNMR) in the range of 0.52~0.78 was prepared from microcrystalline cellulose,cotton linters,and spruce sulfite pulp.The structure of the HPC samples was characterized by means of FT-IR,NMR,gas chromatography(GC),and size exclusion chromatography(SEC) analyses.Three types of cellulose samples with different molecular weights were found to dissolve well in the NaOH/urea solvent with no obvious differences in reactivity and regioselectivity.The relative reactivity of hydroxyl groups in the glycosyl unit was in the following order:O-6>O-2>O-3.In addition,the results of the study indicated that the tandem reaction during hydroxypropylation could be ignored.展开更多
Quaternized cellulose( QC) derivatives were synthesized by reacting cellulose with 3-chloro-2-hydroxypropyl trimethyl ammonium chloride( CHPTAC) in an aqueous solution of Na OH-urea. The chemical structures and physic...Quaternized cellulose( QC) derivatives were synthesized by reacting cellulose with 3-chloro-2-hydroxypropyl trimethyl ammonium chloride( CHPTAC) in an aqueous solution of Na OH-urea. The chemical structures and physical properties of the obtained QC derivatives were characterized using nitrogen content analysis,Fourier transform infrared spectroscopy( FT-IR),~1H-nuclear magnetic resonance(1H-NMR),X-ray diffraction( XRD),and thermal gravity analysis( TGA). The FT-IR and ~1H-NMR results confirmed the successful introduction of cationic quaternary ammonium groups into the main chain of cellulose. A series of QC derivatives with the degree of substitution( DS) values ranging from 0. 33 to 0. 80 were derived by adjusting the molar ratio of CHPTAC to anhydroglucose unit( AGU) of cellulose,concentration of cellulose in the Na OH-urea solution,as well as reaction temperature and time. According to the DS values of the QC derivatives,the optimized synthetic conditions were as follows: 25℃ reaction temperature,3% cellulose in Na OH-urea solution,the molar ratio of etherification agent to glycosidic cellulose of 15∶ 1,and 12 h reaction time. The TGA and XRD results revealed that the crystalline structure was destroyed during etherification,and the thermal stability of the QC derivatives was lower than that of cellulose.展开更多
文摘采用氢氧化钠-硫脲-尿素水溶液在中高温条件下处理稻草盘磨机械浆,通过用碱量、纤维浓度、处理温度和处理时间等参数的单因素试验探究该溶剂对稻草纤维成纸强度性能的影响。研究表明:在用碱量4%、处理时间40m i n、处理温度50℃、纤维浓度15%的条件下,稻草机械浆的强度性能最佳,以原浆强度为参比,经处理后纤维的抗张指数和耐破指数分别提高75.6%和80.9%,同时其成纸松厚度下降13.6%,但耐折度无明显变化。此外,处理前后浆料纤维无定形区和结晶区的整体结构不受影响,纤维中碳、氢、氧三种元素的质量比没有明显变化,但氮元素含量降低明显。
基金Funded by National Natural Science Foundation of China(Nos.50973086 and 51273073)Hubei Provincial Department of Education of China(No.Z20081501)
文摘The aim of this work is optimizing the techniques to prepare pure cellulose microspheres, which are used as packing adsorbents for high-performance liquid chromatography. Thereupon, cellulose was dissolved in a pre-cooled NaOH/urea solution, from which various-size microspheres were prepared. The volume-average diameters were controlled approximately at 30 p,m, 8 ~tm and 4 pm grades when cyclohexane, liquid paraffin and pump oil were used as dispersants, respectively. The present investigations reveal that higher viscosity dispersant is suitable for the preparation of smaller-size microspheres, while larger size microspheres are prepared preferably using lower-viscosity dispersant. The chiral stationary phase derived from 8 μm grade microspheres can separate the enantiomers of efavirenz.
文摘Hydroxypropyl celluloses(HPC) were homogenously synthesized by the reaction of cellulose with propylene oxide in NaOH/urea aqueous solution.Water-soluble HPC with molar degree of substitution(MSNMR) in the range of 0.52~0.78 was prepared from microcrystalline cellulose,cotton linters,and spruce sulfite pulp.The structure of the HPC samples was characterized by means of FT-IR,NMR,gas chromatography(GC),and size exclusion chromatography(SEC) analyses.Three types of cellulose samples with different molecular weights were found to dissolve well in the NaOH/urea solvent with no obvious differences in reactivity and regioselectivity.The relative reactivity of hydroxyl groups in the glycosyl unit was in the following order:O-6>O-2>O-3.In addition,the results of the study indicated that the tandem reaction during hydroxypropylation could be ignored.
基金financially supported by grants from the National Natural Science Foundation of China(No.31500493)the Liaoning Educational Common Scientific Research Project(No.L2015044)+1 种基金the Liaoning Natural Science Foundation(No.2015020576)the Open Foundation of the Key Lab of Pulp and Paper Science & Technology,and Ministry of Education(Shandong Province),Qilu University of Technology(No.08031338)
文摘Quaternized cellulose( QC) derivatives were synthesized by reacting cellulose with 3-chloro-2-hydroxypropyl trimethyl ammonium chloride( CHPTAC) in an aqueous solution of Na OH-urea. The chemical structures and physical properties of the obtained QC derivatives were characterized using nitrogen content analysis,Fourier transform infrared spectroscopy( FT-IR),~1H-nuclear magnetic resonance(1H-NMR),X-ray diffraction( XRD),and thermal gravity analysis( TGA). The FT-IR and ~1H-NMR results confirmed the successful introduction of cationic quaternary ammonium groups into the main chain of cellulose. A series of QC derivatives with the degree of substitution( DS) values ranging from 0. 33 to 0. 80 were derived by adjusting the molar ratio of CHPTAC to anhydroglucose unit( AGU) of cellulose,concentration of cellulose in the Na OH-urea solution,as well as reaction temperature and time. According to the DS values of the QC derivatives,the optimized synthetic conditions were as follows: 25℃ reaction temperature,3% cellulose in Na OH-urea solution,the molar ratio of etherification agent to glycosidic cellulose of 15∶ 1,and 12 h reaction time. The TGA and XRD results revealed that the crystalline structure was destroyed during etherification,and the thermal stability of the QC derivatives was lower than that of cellulose.