Fe(83.2-x)CoxP(10)C6Cu(0.8)(x=0,4,6,8 and 10)alloys with a high amorphous-forming ability and good softmagnetic properties were successfully synthesized.Saturation magnetic flux density(Bs)is effectively enhanced from...Fe(83.2-x)CoxP(10)C6Cu(0.8)(x=0,4,6,8 and 10)alloys with a high amorphous-forming ability and good softmagnetic properties were successfully synthesized.Saturation magnetic flux density(Bs)is effectively enhanced from 1.53 T to 1.61 T for as-quenched alloy by minor Co addition,which is consistent well with the result of the linear relationship between average magnetic moment and magnetic valence.For Cocontained alloys,the value of corecivity(Hc)is mainly determined by magneto-crystalline anisotropy,while effective permeability(μe)is dominated by grain size and average saturation polarization.After proper heat treatment,the Fe(79.2)Co4P(10)C6Cu(0.8)nanocrystalline alloy exhibited excellent soft-magnetic properties including a high Bsof 1.8 T,a low Hcof 6.6 A/m and a highμeof 15,510,which is closely related to the high volume fraction of α-(Fe,Co)grains and refined uniform nanocrystalline microstructure.展开更多
基金supported by the National Key Research and Development Program of China (Grant No. 2016YFB0300502)the National Natural Science Foundation of China (Grant Nos. 51631003, 51401052, 51871237 and 51501037)
文摘Fe(83.2-x)CoxP(10)C6Cu(0.8)(x=0,4,6,8 and 10)alloys with a high amorphous-forming ability and good softmagnetic properties were successfully synthesized.Saturation magnetic flux density(Bs)is effectively enhanced from 1.53 T to 1.61 T for as-quenched alloy by minor Co addition,which is consistent well with the result of the linear relationship between average magnetic moment and magnetic valence.For Cocontained alloys,the value of corecivity(Hc)is mainly determined by magneto-crystalline anisotropy,while effective permeability(μe)is dominated by grain size and average saturation polarization.After proper heat treatment,the Fe(79.2)Co4P(10)C6Cu(0.8)nanocrystalline alloy exhibited excellent soft-magnetic properties including a high Bsof 1.8 T,a low Hcof 6.6 A/m and a highμeof 15,510,which is closely related to the high volume fraction of α-(Fe,Co)grains and refined uniform nanocrystalline microstructure.