The zeta potential measurements show that the flotation separation of diaspore from kaolinite, illite and pyrophyllite could be achieved in the range of pH 46.5 with cationic collectors. A special quaternary ammonium ...The zeta potential measurements show that the flotation separation of diaspore from kaolinite, illite and pyrophyllite could be achieved in the range of pH 46.5 with cationic collectors. A special quaternary ammonium salts(DTAL) shows better selectivity than that the dodecyl amine(DDA) does for the flotation of three silicates. The closed circuit flotation results show that the reverse flotation de silicate can be achieved with DTAL as collector, a new inorganic reagent(SFL) as depressant and MIBC as frother to obtain a bauxite concentrate m (Al 2O 3)/ m (SiO 2) >10, Al 2O 3 recovery>86%).展开更多
Using cetyl trimethylammonium bromide （CTAB） as collector, the flotation de-silicating from diasporic-bauxite was investigated. And the Zeta potentials and contact-angles of silicate minerals and diaspore were also ...Using cetyl trimethylammonium bromide （CTAB） as collector, the flotation de-silicating from diasporic-bauxite was investigated. And the Zeta potentials and contact-angles of silicate minerals and diaspore were also stu-（died.）The results show that in the presence of 2×10-4 mol·L-1CTAB, the surface charges of pyrophyllite, kaolinite and illite become more positive, and the contact angles of these three silicates also increase evidently in the pH range of 2-8, but the Zeta potentials and contact angles of diaspore change little. So, the floatability of the four minerals is in the following order: pyrophyllite>kaolinite≈illite>diaspore. The open-circuit flotation results also show that a bauxite concentrate with m（Al2O3）/m（SiO2） over 9.3 and Al2O3 recovery over 76% can be obtained from diasporic-bauxite ore. The result of XRD of the bauxite concentrate shows that pyrophyllite is easier to be removed from diasporic-bauxite than illite and kaolinite due to its better floatability.展开更多
The application of bauxite with low Al2O3 content has been studied in this paper and β-SiAlON has been obtained from two kinds of bauxites （Al2O3 content 68.08 mass% and 46.30 mass% respectively） by aluminum reduct...The application of bauxite with low Al2O3 content has been studied in this paper and β-SiAlON has been obtained from two kinds of bauxites （Al2O3 content 68.08 mass% and 46.30 mass% respectively） by aluminum reduction and nitridation method. The sequence of reactions has been studied using thermal analysis （TG-DTA）, X-ray diffraction （XRD） analysis and scanning electron microscopy （SEM） with EDS. Compared with carbon thermal reduction and nitridation of aluminosilicates employed presently, the reaction in the system of bauxite-Al-N2 occurs at lower temperature. β-SiAlON appears as one of the main products from 1573K and exists stably in the range of the present experimental temperature. The microstructure of β-SiAlON obtained at 1773 K is short column with 5-10μm observed by SEM.展开更多
文摘The zeta potential measurements show that the flotation separation of diaspore from kaolinite, illite and pyrophyllite could be achieved in the range of pH 46.5 with cationic collectors. A special quaternary ammonium salts(DTAL) shows better selectivity than that the dodecyl amine(DDA) does for the flotation of three silicates. The closed circuit flotation results show that the reverse flotation de silicate can be achieved with DTAL as collector, a new inorganic reagent(SFL) as depressant and MIBC as frother to obtain a bauxite concentrate m (Al 2O 3)/ m (SiO 2) >10, Al 2O 3 recovery>86%).
文摘Using cetyl trimethylammonium bromide （CTAB） as collector, the flotation de-silicating from diasporic-bauxite was investigated. And the Zeta potentials and contact-angles of silicate minerals and diaspore were also stu-（died.）The results show that in the presence of 2×10-4 mol·L-1CTAB, the surface charges of pyrophyllite, kaolinite and illite become more positive, and the contact angles of these three silicates also increase evidently in the pH range of 2-8, but the Zeta potentials and contact angles of diaspore change little. So, the floatability of the four minerals is in the following order: pyrophyllite>kaolinite≈illite>diaspore. The open-circuit flotation results also show that a bauxite concentrate with m（Al2O3）/m（SiO2） over 9.3 and Al2O3 recovery over 76% can be obtained from diasporic-bauxite ore. The result of XRD of the bauxite concentrate shows that pyrophyllite is easier to be removed from diasporic-bauxite than illite and kaolinite due to its better floatability.
文摘The application of bauxite with low Al2O3 content has been studied in this paper and β-SiAlON has been obtained from two kinds of bauxites （Al2O3 content 68.08 mass% and 46.30 mass% respectively） by aluminum reduction and nitridation method. The sequence of reactions has been studied using thermal analysis （TG-DTA）, X-ray diffraction （XRD） analysis and scanning electron microscopy （SEM） with EDS. Compared with carbon thermal reduction and nitridation of aluminosilicates employed presently, the reaction in the system of bauxite-Al-N2 occurs at lower temperature. β-SiAlON appears as one of the main products from 1573K and exists stably in the range of the present experimental temperature. The microstructure of β-SiAlON obtained at 1773 K is short column with 5-10μm observed by SEM.