Long alumina .fibers with 60 cm in length were pre- pared by sol - gel method. The spinning sol was ob- tained by mixing aluminum nitrate, oxalic acid, and polyvinylpyrrolidone with a mass ratio of 10： 3： 2. Fourier...Long alumina .fibers with 60 cm in length were pre- pared by sol - gel method. The spinning sol was ob- tained by mixing aluminum nitrate, oxalic acid, and polyvinylpyrrolidone with a mass ratio of 10： 3： 2. Fourier transform infrared （ FTIR ） spectra, X-ray diffraction （XRD） , and scanning electron microscopy （SEM） were used to characterize the properties of the gel and ce- ramic fibers. The fibers with uniform diameter and smooth surface were obtained by sintering at 1 200℃ for 1 h, and their main phase was indentified as α-Al2O3.展开更多
Long alumina fibers were prepared by sol-gel method.The spinning sol was obtained by mixing aluminum nitrate,tartaric acid,and polyvinylpyrrolidone with a mass ratio of 10∶3∶1.5.Thermogravimetry-differential scannin...Long alumina fibers were prepared by sol-gel method.The spinning sol was obtained by mixing aluminum nitrate,tartaric acid,and polyvinylpyrrolidone with a mass ratio of 10∶3∶1.5.Thermogravimetry-differential scanning calorimetry （TG-DSC）,Fourier transform infrared （FT-IR） spectra,X-ray diffraction （XRD）,and scanning electron microscopy （SEM） were used to characterize the properties of the gel and ceramic fibers.A little of α-Al2O3 phase is observed in the alumina precursor gel fibers sintered at 1273 K.The fibers with a uniform diameter can be obtained when sintered at 1473 K,and its main phase is also indentified as α-Al2O3.展开更多
基金supported by the Natural Science Foundation of Shaanxi in China ( No. 2010K10 - 21)
文摘Long alumina .fibers with 60 cm in length were pre- pared by sol - gel method. The spinning sol was ob- tained by mixing aluminum nitrate, oxalic acid, and polyvinylpyrrolidone with a mass ratio of 10： 3： 2. Fourier transform infrared （ FTIR ） spectra, X-ray diffraction （XRD） , and scanning electron microscopy （SEM） were used to characterize the properties of the gel and ce- ramic fibers. The fibers with uniform diameter and smooth surface were obtained by sintering at 1 200℃ for 1 h, and their main phase was indentified as α-Al2O3.
基金supported by the Natural Science Foundation of Shaanxi Province,China (No.2010K10-21)
文摘Long alumina fibers were prepared by sol-gel method.The spinning sol was obtained by mixing aluminum nitrate,tartaric acid,and polyvinylpyrrolidone with a mass ratio of 10∶3∶1.5.Thermogravimetry-differential scanning calorimetry （TG-DSC）,Fourier transform infrared （FT-IR） spectra,X-ray diffraction （XRD）,and scanning electron microscopy （SEM） were used to characterize the properties of the gel and ceramic fibers.A little of α-Al2O3 phase is observed in the alumina precursor gel fibers sintered at 1273 K.The fibers with a uniform diameter can be obtained when sintered at 1473 K,and its main phase is also indentified as α-Al2O3.