To improve the cycle stability at high voltage and high charge/discharge rate, spherical LiNi1/3Co1/3Mn1/3O2 was coated with Al2O3 by using heterogeneous nucleation process, and the physical and electrochemical proper...To improve the cycle stability at high voltage and high charge/discharge rate, spherical LiNi1/3Co1/3Mn1/3O2 was coated with Al2O3 by using heterogeneous nucleation process, and the physical and electrochemical properties were studied. The SEM images show that there is a uniform coating on the modified spherical LiNi1/3Co1/3Mn1/3O2. The electrochemical tests indicate that the properties of LiNi1/3Co1/3Mn1/3O2 coated with 0.5% aluminum oxide are the best. The initial capacities are 150 and 173 mA·h/g at the rate of 1C in the voltage range of 2.7-4.3 V and 2.7-4.6 V, respectively, and the discharge capacities maintain about 99% and 85% after 30 cycles, respectively. While those of the bare LiNi1/3Co1/3Mn1/3O2 are only 90% and 75%, respectively. The CV tests of LiNi1/3Co1/3Mn1/3O2 show that Al2O3-coating can restrain the oxide-reduction peak currents fading during the charge/discharge course.展开更多
Several lithium-ion batteries of 18650-type were assembled with pristine or Al2O3-coated LiNi0.4Co0.2Mn0.4O2（NCM） as cathode material and mesocarbon microbeads（MCMB） as anode material.The cycling performance of th...Several lithium-ion batteries of 18650-type were assembled with pristine or Al2O3-coated LiNi0.4Co0.2Mn0.4O2（NCM） as cathode material and mesocarbon microbeads（MCMB） as anode material.The cycling performance of the batteries was examined under 25 °C at a 2C rate within a potential range of 2.75―4.20 V.The changes of the crystal structure,the lattice parameter,the mean crystallite size,and the mean micro-strain of pristine NCM and Al2O3-coated NCM during the charge-discharge cycling were determined by X-ray diffraction（XRD）.The results indicate that the bulk structure of Al2O3-coated NCM is more stable than that of pristine NCM,which leads to the better cycling performance of Al2O3-coated NCM compared to that of pristine NCM.展开更多
将耐热合金钢基体进行活化处理后,以Ni Co Cr Al Y为粘接过渡层,采用等离子喷涂法和喷枪快速喷涂工艺相结合制备包覆复合粉体Al_2O_3-Zr O_2/Y_2O_3和未包覆粉体Zr O_2/Y_2O_3的2种不同厚度的热障涂层材料样品,通过涂层的结合强度试验...将耐热合金钢基体进行活化处理后,以Ni Co Cr Al Y为粘接过渡层,采用等离子喷涂法和喷枪快速喷涂工艺相结合制备包覆复合粉体Al_2O_3-Zr O_2/Y_2O_3和未包覆粉体Zr O_2/Y_2O_3的2种不同厚度的热障涂层材料样品,通过涂层的结合强度试验、涂层微观结构和高温隔热试验比较相同厚度的2种陶瓷涂层的结合强度及隔热效果,并探讨涂层厚度与隔热效果的关系。结果表明:采用纳米Al_2O_3包覆Zr O_2/Y_2O_3粉体制备的热障涂层其结构和性能都优于未包覆粉体Zr O_2/Y_2O_3制备的热障涂层,且该热障涂层隔热性能随涂层厚度的增加而提高,温度越高性能优势越明显。展开更多
陶瓷颗粒增强型金属基复合涂层在诸多工业领域都有需求,其中包括炼钢工业。本文中,MCr Al Y-Al2O3复合粉末通过球磨法制备,并且通过等离子喷涂、超音速火焰喷涂和冷喷涂分别制备了MCr Al Y-Al2O3复合涂层。实验结果显示,可以选用不优先...陶瓷颗粒增强型金属基复合涂层在诸多工业领域都有需求,其中包括炼钢工业。本文中,MCr Al Y-Al2O3复合粉末通过球磨法制备,并且通过等离子喷涂、超音速火焰喷涂和冷喷涂分别制备了MCr Al Y-Al2O3复合涂层。实验结果显示,可以选用不优先使基体与Al2O3结合的复合粉末控制涂层中的Al2O3含量。涂层粉末的微结构在冷喷涂涂层和超音速火焰喷涂涂层中得到了良好的保留,这是因为喷涂粒子未熔化或部分熔化。然而,对于等离子喷涂的涂层,大多数Al2O3颗粒被隔离在层状界面,在条状界面上形成连续的氧化皮。经退火处理后,由元素扩散引起的条状界面的强化使得超音速火焰喷涂和大气等离子喷涂的涂层硬度增大。此外,冷喷涂涂层由于退火后加工硬化效果的消除,硬度增加不像超音速火焰喷涂和等离子喷涂涂层那样明显。展开更多
文摘To improve the cycle stability at high voltage and high charge/discharge rate, spherical LiNi1/3Co1/3Mn1/3O2 was coated with Al2O3 by using heterogeneous nucleation process, and the physical and electrochemical properties were studied. The SEM images show that there is a uniform coating on the modified spherical LiNi1/3Co1/3Mn1/3O2. The electrochemical tests indicate that the properties of LiNi1/3Co1/3Mn1/3O2 coated with 0.5% aluminum oxide are the best. The initial capacities are 150 and 173 mA·h/g at the rate of 1C in the voltage range of 2.7-4.3 V and 2.7-4.6 V, respectively, and the discharge capacities maintain about 99% and 85% after 30 cycles, respectively. While those of the bare LiNi1/3Co1/3Mn1/3O2 are only 90% and 75%, respectively. The CV tests of LiNi1/3Co1/3Mn1/3O2 show that Al2O3-coating can restrain the oxide-reduction peak currents fading during the charge/discharge course.
基金Supported by the Project of Shanghai Committee of Science and Technology,China(Nos.1052nm00100,09ZR1437600)
文摘Several lithium-ion batteries of 18650-type were assembled with pristine or Al2O3-coated LiNi0.4Co0.2Mn0.4O2（NCM） as cathode material and mesocarbon microbeads（MCMB） as anode material.The cycling performance of the batteries was examined under 25 °C at a 2C rate within a potential range of 2.75―4.20 V.The changes of the crystal structure,the lattice parameter,the mean crystallite size,and the mean micro-strain of pristine NCM and Al2O3-coated NCM during the charge-discharge cycling were determined by X-ray diffraction（XRD）.The results indicate that the bulk structure of Al2O3-coated NCM is more stable than that of pristine NCM,which leads to the better cycling performance of Al2O3-coated NCM compared to that of pristine NCM.
文摘将耐热合金钢基体进行活化处理后,以Ni Co Cr Al Y为粘接过渡层,采用等离子喷涂法和喷枪快速喷涂工艺相结合制备包覆复合粉体Al_2O_3-Zr O_2/Y_2O_3和未包覆粉体Zr O_2/Y_2O_3的2种不同厚度的热障涂层材料样品,通过涂层的结合强度试验、涂层微观结构和高温隔热试验比较相同厚度的2种陶瓷涂层的结合强度及隔热效果,并探讨涂层厚度与隔热效果的关系。结果表明:采用纳米Al_2O_3包覆Zr O_2/Y_2O_3粉体制备的热障涂层其结构和性能都优于未包覆粉体Zr O_2/Y_2O_3制备的热障涂层,且该热障涂层隔热性能随涂层厚度的增加而提高,温度越高性能优势越明显。
文摘陶瓷颗粒增强型金属基复合涂层在诸多工业领域都有需求,其中包括炼钢工业。本文中,MCr Al Y-Al2O3复合粉末通过球磨法制备,并且通过等离子喷涂、超音速火焰喷涂和冷喷涂分别制备了MCr Al Y-Al2O3复合涂层。实验结果显示,可以选用不优先使基体与Al2O3结合的复合粉末控制涂层中的Al2O3含量。涂层粉末的微结构在冷喷涂涂层和超音速火焰喷涂涂层中得到了良好的保留,这是因为喷涂粒子未熔化或部分熔化。然而,对于等离子喷涂的涂层,大多数Al2O3颗粒被隔离在层状界面,在条状界面上形成连续的氧化皮。经退火处理后,由元素扩散引起的条状界面的强化使得超音速火焰喷涂和大气等离子喷涂的涂层硬度增大。此外,冷喷涂涂层由于退火后加工硬化效果的消除,硬度增加不像超音速火焰喷涂和等离子喷涂涂层那样明显。