The chemical short-range order of Al-Fe-Ce amorphous alloy was studied by means of X-ray diffraction (XRD) and differential scanning calorimetry (DSC). It is found that the prepeak position in X-ray diffraction intens...The chemical short-range order of Al-Fe-Ce amorphous alloy was studied by means of X-ray diffraction (XRD) and differential scanning calorimetry (DSC). It is found that the prepeak position in X-ray diffraction intensity curve shifts to higher angles as the content of Fe increases, but it shifts to smaller angles as the content of Ce increases. The crystallization character of the amorphous alloy changes with the variation of the content of Fe and Ce. Ce can improve the interaction between atoms and the capacity of compound formation, so it is favorable to Al-based glass formability.展开更多
Rapidly solidified Al 8Fe 4Ce alloy was prepared by melt spinning.As quenched and as annealed microstructures were studied by TEM and energy dispersive spectrum analysis.The microhardness of the alloy at different...Rapidly solidified Al 8Fe 4Ce alloy was prepared by melt spinning.As quenched and as annealed microstructures were studied by TEM and energy dispersive spectrum analysis.The microhardness of the alloy at different annealing temperature was measured.The results obtained indicated that as quenched microstructure varied with different cooling rates.The microstructure annealed at 300℃ was much the same as that of the as quenched.The dispersed phases at grain boundary of the microstructure annealed at 400℃ became coarsening.After annealing at 450℃ for 2 hours,the primary phase and the intercellular dispersed phases,metastable phase Al 6Fe and Al 20 Fe 5Ce respectively,coarsened further.The soften temperature was deduced at over 300℃ by measuring microhardness.展开更多
文摘The chemical short-range order of Al-Fe-Ce amorphous alloy was studied by means of X-ray diffraction (XRD) and differential scanning calorimetry (DSC). It is found that the prepeak position in X-ray diffraction intensity curve shifts to higher angles as the content of Fe increases, but it shifts to smaller angles as the content of Ce increases. The crystallization character of the amorphous alloy changes with the variation of the content of Fe and Ce. Ce can improve the interaction between atoms and the capacity of compound formation, so it is favorable to Al-based glass formability.
文摘Rapidly solidified Al 8Fe 4Ce alloy was prepared by melt spinning.As quenched and as annealed microstructures were studied by TEM and energy dispersive spectrum analysis.The microhardness of the alloy at different annealing temperature was measured.The results obtained indicated that as quenched microstructure varied with different cooling rates.The microstructure annealed at 300℃ was much the same as that of the as quenched.The dispersed phases at grain boundary of the microstructure annealed at 400℃ became coarsening.After annealing at 450℃ for 2 hours,the primary phase and the intercellular dispersed phases,metastable phase Al 6Fe and Al 20 Fe 5Ce respectively,coarsened further.The soften temperature was deduced at over 300℃ by measuring microhardness.