Al/Co co-doped α-Ni（OH）2 samples were prepared by either ultrasonic co-precipitation method （Sample B） or co-precipitation method （Sample A）. The crystal structure and particle size distribution of the prepared...Al/Co co-doped α-Ni（OH）2 samples were prepared by either ultrasonic co-precipitation method （Sample B） or co-precipitation method （Sample A）. The crystal structure and particle size distribution of the prepared samples were examined by X-ray diffraction （XRD） and laser particle size analyzer, respectively. The results show that Sample B has more crystalline defects and smaller average diameter than Sample A. The cyclic voltammetry and electrochemical impedance spectroscopy measurements indicate that Sample B has better electrochemical performance than Sample A, such as better reaction reversibility, lower charge-transfer resistance and better cyclic stability. Proton diffusion coefficient of Sample B is 1.96×10-10cm2/s, which is two times as large as that （9.78×10-11cm2/s） of Sample A. The charge-discharge tests show that the discharge capacity （308 mA·h/g） of Sample B is 25 mA·h/g higher than that of Sample A （283 mA·h/g）.展开更多
The poor structural stability and capacity retention of the high-voltage spinel-type LiNi_(0.5)Mn_(1.5)O_(4)(LNMO)limits their further application.Herein,Al and Co were doped in LNMO materials for a more stable struct...The poor structural stability and capacity retention of the high-voltage spinel-type LiNi_(0.5)Mn_(1.5)O_(4)(LNMO)limits their further application.Herein,Al and Co were doped in LNMO materials for a more stable structure and capacity.The LNMO,LiNi_(0.45)Al_(0.05)Mn_(1.5)O_(4)(LNAMO)and LiNi_(0.45)Co_(0.05)Mn_(1.5)O_(4)(LNCMO)were synthesized by calcination at 900℃ for 8 h,which was called as solid-phase method and applied universally in industry.XRD,FT-IR and CV test results showed the synthesized samples have cation disordering Fd-3m space group structures.Moreover,the incorporation of Al and Co increased the cation disordering of LNMO,thereby increasing the transfer rate of Li+.The SEM results showed that the doped samples performed more regular and ortho-octahedral.The EDS elemental analysis confirmed the uniform distribution of each metal element in the samples.Moreover,the doped samples showed better electrochemical properties than undoped LNMO.The LNAMO and LNCMO samples were discharged with specific capacities of 116.3 mA·h·g^(-1)and 122.8 mA·h·g^(-1)at 1 C charge/discharge rate with good capacity retention of 95.8% and 94.8% after 200 cycles at room temperature,respectively.The capacity fading phenomenon of the doped samples at 50℃ and 1 C rate was significantly improved.Further,cations doping also enhanced the rate performance,especially for the LNCMO,the discharge specific capacity of 117.9 mA·h·g^(-1)can be obtained at a rate of 5 C.展开更多
： The structures of Mg-Al-CO3 and Zn-Al-CO3 hydrotalcites have been studied by means of XRD,IR and TG-DTA.Although both have the same crystal structures,their thermal stabilities are quite different.During the therma...： The structures of Mg-Al-CO3 and Zn-Al-CO3 hydrotalcites have been studied by means of XRD,IR and TG-DTA.Although both have the same crystal structures,their thermal stabilities are quite different.During the thermal decomposition process,Mg-Al-CO3 hydrotalcite exhibits two steps- desorption of interlayer water occurs at 200℃ ,followed by dehydroxylation of the brucite-like layers and loss of carbonate at 400℃ ,Zn-Al-CO3 hydrotalcite decomposes in one step-the desorption of interlayer water, structural water and carbon dioxide occurred at the same time at 200℃ . The results of a theoretical study indicate that the bond strengths of OH-CO3-OH and OH-H2O-CO3-OH in Mg-Al-CO3 hydrotalcite are stronger than those in Zn-Al-CO3 hydrotalcite.It has been shown that the thermal stability of Mg-Al-CO3 hydrotalcite is higher than that of Zn-Al-CO3 hydrotalcite.展开更多
A series of Er-Al-Co bulk metallic glasses (BMGs) have been prepared by the copper mold casting method. The glass forming ability and magnetocaloric effect (MCE) for these alloys have been investigated. The second-ord...A series of Er-Al-Co bulk metallic glasses (BMGs) have been prepared by the copper mold casting method. The glass forming ability and magnetocaloric effect (MCE) for these alloys have been investigated. The second-order magnetic transition from para-magnetic to ferromagnetic states takes place at about 9 K. These BMGs exhibit excellent MCE because of their large effective magneton number; Er56Al24Co20 BMG has a maximum entropy change and refrigeration capacity of 16.06 J kg-1 K-1 and 546 J kg-1,respectively,under the field of 50 kOe (10 kOe=795.775 kA/m) indicating that these BMGs are potential candidate magnetic materials for hydrogen liquefaction.展开更多
基金Project (10774030) supported by the National Natural Science Foundation of ChinaProject (2008J1-C161) supported by the Science and Technology Program of Guangzhou City of China
文摘Al/Co co-doped α-Ni（OH）2 samples were prepared by either ultrasonic co-precipitation method （Sample B） or co-precipitation method （Sample A）. The crystal structure and particle size distribution of the prepared samples were examined by X-ray diffraction （XRD） and laser particle size analyzer, respectively. The results show that Sample B has more crystalline defects and smaller average diameter than Sample A. The cyclic voltammetry and electrochemical impedance spectroscopy measurements indicate that Sample B has better electrochemical performance than Sample A, such as better reaction reversibility, lower charge-transfer resistance and better cyclic stability. Proton diffusion coefficient of Sample B is 1.96×10-10cm2/s, which is two times as large as that （9.78×10-11cm2/s） of Sample A. The charge-discharge tests show that the discharge capacity （308 mA·h/g） of Sample B is 25 mA·h/g higher than that of Sample A （283 mA·h/g）.
基金supported by the National Natural Science Foundation of China(52022109 and 51834008)Beijing Municipal Natural Science Foundation(2202047)+1 种基金National Key Research and Development Program of China(2021YFC2901100)Science Foundation of China University of Petroleum,Beijing(2462021QNX2010,2462020YXZZ019,2462020YXZZ016,and 2462022QZDX008)。
文摘The poor structural stability and capacity retention of the high-voltage spinel-type LiNi_(0.5)Mn_(1.5)O_(4)(LNMO)limits their further application.Herein,Al and Co were doped in LNMO materials for a more stable structure and capacity.The LNMO,LiNi_(0.45)Al_(0.05)Mn_(1.5)O_(4)(LNAMO)and LiNi_(0.45)Co_(0.05)Mn_(1.5)O_(4)(LNCMO)were synthesized by calcination at 900℃ for 8 h,which was called as solid-phase method and applied universally in industry.XRD,FT-IR and CV test results showed the synthesized samples have cation disordering Fd-3m space group structures.Moreover,the incorporation of Al and Co increased the cation disordering of LNMO,thereby increasing the transfer rate of Li+.The SEM results showed that the doped samples performed more regular and ortho-octahedral.The EDS elemental analysis confirmed the uniform distribution of each metal element in the samples.Moreover,the doped samples showed better electrochemical properties than undoped LNMO.The LNAMO and LNCMO samples were discharged with specific capacities of 116.3 mA·h·g^(-1)and 122.8 mA·h·g^(-1)at 1 C charge/discharge rate with good capacity retention of 95.8% and 94.8% after 200 cycles at room temperature,respectively.The capacity fading phenomenon of the doped samples at 50℃ and 1 C rate was significantly improved.Further,cations doping also enhanced the rate performance,especially for the LNCMO,the discharge specific capacity of 117.9 mA·h·g^(-1)can be obtained at a rate of 5 C.
文摘： The structures of Mg-Al-CO3 and Zn-Al-CO3 hydrotalcites have been studied by means of XRD,IR and TG-DTA.Although both have the same crystal structures,their thermal stabilities are quite different.During the thermal decomposition process,Mg-Al-CO3 hydrotalcite exhibits two steps- desorption of interlayer water occurs at 200℃ ,followed by dehydroxylation of the brucite-like layers and loss of carbonate at 400℃ ,Zn-Al-CO3 hydrotalcite decomposes in one step-the desorption of interlayer water, structural water and carbon dioxide occurred at the same time at 200℃ . The results of a theoretical study indicate that the bond strengths of OH-CO3-OH and OH-H2O-CO3-OH in Mg-Al-CO3 hydrotalcite are stronger than those in Zn-Al-CO3 hydrotalcite.It has been shown that the thermal stability of Mg-Al-CO3 hydrotalcite is higher than that of Zn-Al-CO3 hydrotalcite.
基金supported by the National Natural Science Foundation of China (50871013 and 51071018)the National Basic Research Program of China (2007CB613901)
文摘A series of Er-Al-Co bulk metallic glasses (BMGs) have been prepared by the copper mold casting method. The glass forming ability and magnetocaloric effect (MCE) for these alloys have been investigated. The second-order magnetic transition from para-magnetic to ferromagnetic states takes place at about 9 K. These BMGs exhibit excellent MCE because of their large effective magneton number; Er56Al24Co20 BMG has a maximum entropy change and refrigeration capacity of 16.06 J kg-1 K-1 and 546 J kg-1,respectively,under the field of 50 kOe (10 kOe=795.775 kA/m) indicating that these BMGs are potential candidate magnetic materials for hydrogen liquefaction.