The superplastic forming potential of two fine-grained S083 aluminum alloys were studied under biaxial tension using a pneumatic bulge test. Experiments were performed at temperatures ranging from 475 to 525℃with thr...The superplastic forming potential of two fine-grained S083 aluminum alloys were studied under biaxial tension using a pneumatic bulge test. Experiments were performed at temperatures ranging from 475 to 525℃with three different strain paths ranging from equi-biaxial to approaching plane strain. The shape of the forming limited diagram(FLD) is found to be significantly different from FLDs commonly used in room temperature stamping. The effects of temperature on final thickness distribution, dome height and cavitation were investigated for the case of equi-biaxial stretching. Increasing temperature in free bulge forming can improve the thickness distribution of final parts but have no significant effect on dome height. The results indicate that determination of forming limits in SPF cannot be represented with a simple FLD and additional metrics such as external thinning and internal cavitation needed to determine the SPF potential of a material.展开更多
基金Project (50405014) supported by the National Natural Science Foundation of China
文摘The superplastic forming potential of two fine-grained S083 aluminum alloys were studied under biaxial tension using a pneumatic bulge test. Experiments were performed at temperatures ranging from 475 to 525℃with three different strain paths ranging from equi-biaxial to approaching plane strain. The shape of the forming limited diagram(FLD) is found to be significantly different from FLDs commonly used in room temperature stamping. The effects of temperature on final thickness distribution, dome height and cavitation were investigated for the case of equi-biaxial stretching. Increasing temperature in free bulge forming can improve the thickness distribution of final parts but have no significant effect on dome height. The results indicate that determination of forming limits in SPF cannot be represented with a simple FLD and additional metrics such as external thinning and internal cavitation needed to determine the SPF potential of a material.