为了解杆式弹超高速撞击多层薄钢靶的破坏过程及毁伤机理,开展了克级93W杆式弹正撞击多层Q345钢靶实验及数值模拟研究,通过扫描电子显微镜(scanning electron microscope,SEM)及金相显微镜,分析了超高速撞击实验后靶板材料的微观组织及...为了解杆式弹超高速撞击多层薄钢靶的破坏过程及毁伤机理,开展了克级93W杆式弹正撞击多层Q345钢靶实验及数值模拟研究,通过扫描电子显微镜(scanning electron microscope,SEM)及金相显微镜,分析了超高速撞击实验后靶板材料的微观组织及成分。结果表明,超高速撞击作用下,靶板呈现出“翻唇”穿孔变形、花瓣状塑性变形、撕裂、撞击成坑及鼓包等破坏模式。靶板前3层毁伤以超高速穿孔为主,孔洞数目多但面积小,后几层靶板毁伤孔洞数目少且孔径呈先增大后减小趋势。微观分析表明靶材在强冲击压力下发生晶粒碎化、熔化及再结晶,撞击过程中会形成微孔聚集与微裂纹,可见靶板失效主要是熔融混合物冷却过程中产生的热应力与切应力下的剪切撕裂综合作用的结果。展开更多
The microstructure and properties of the 93W-4Ni-2Co-1Fe(mass fraction,%) tungsten heavy alloys prepared by mechanical alloying and electric current activated sintering from mixed elemental powders were investigated.A...The microstructure and properties of the 93W-4Ni-2Co-1Fe(mass fraction,%) tungsten heavy alloys prepared by mechanical alloying and electric current activated sintering from mixed elemental powders were investigated.After 15 h milling,the average W grain size in the powders is decreased to 120 nm.For the powders milled for 15 h,the density,hardness and transverse rupture strength of the alloys sintered only by an intensive pulse electric current are the maximum.When the total sintering time keeps constant,the properties of the sintered alloys can be obviously improved by optimizing the sintering time of pulse-and constant-currents.A bulk ultrafine alloy with an average W grain size of about 340 nm can be obtained by sintering 15 h-milled powders in a total sintering time of 6 min.The corresponding sintered density,hardness and transverse rupture strength reach 16.78 g /cm3,HRA84.3 and 968 MPa,respectively.展开更多
文摘为了解杆式弹超高速撞击多层薄钢靶的破坏过程及毁伤机理,开展了克级93W杆式弹正撞击多层Q345钢靶实验及数值模拟研究,通过扫描电子显微镜(scanning electron microscope,SEM)及金相显微镜,分析了超高速撞击实验后靶板材料的微观组织及成分。结果表明,超高速撞击作用下,靶板呈现出“翻唇”穿孔变形、花瓣状塑性变形、撕裂、撞击成坑及鼓包等破坏模式。靶板前3层毁伤以超高速穿孔为主,孔洞数目多但面积小,后几层靶板毁伤孔洞数目少且孔径呈先增大后减小趋势。微观分析表明靶材在强冲击压力下发生晶粒碎化、熔化及再结晶,撞击过程中会形成微孔聚集与微裂纹,可见靶板失效主要是熔融混合物冷却过程中产生的热应力与切应力下的剪切撕裂综合作用的结果。
基金Project(2007CB616905) supported by the National Basic Research Program of ChinaProject(2007AA03Z112) supported by the National High-tech Research and Development Program of China+1 种基金Project(x2jqB6080210) supported by the Natural Science Foundation of Guangdong Province,ChinaProject(9140A18040709JW1601) supported by the Advanced Research Fund of Department of Defense,China
文摘The microstructure and properties of the 93W-4Ni-2Co-1Fe(mass fraction,%) tungsten heavy alloys prepared by mechanical alloying and electric current activated sintering from mixed elemental powders were investigated.After 15 h milling,the average W grain size in the powders is decreased to 120 nm.For the powders milled for 15 h,the density,hardness and transverse rupture strength of the alloys sintered only by an intensive pulse electric current are the maximum.When the total sintering time keeps constant,the properties of the sintered alloys can be obviously improved by optimizing the sintering time of pulse-and constant-currents.A bulk ultrafine alloy with an average W grain size of about 340 nm can be obtained by sintering 15 h-milled powders in a total sintering time of 6 min.The corresponding sintered density,hardness and transverse rupture strength reach 16.78 g /cm3,HRA84.3 and 968 MPa,respectively.
基金National Nature Science Foundation of China (50674106)National Natural Science Funds for Distinguished Young Scholars (50925416)Creative Research Group of National Nature Science Foundation of China (50721003)