齿轮钢8620RH(K)(/%:0.18～0.22C,0.17～0.26Si,0.70～0.90Mn,≤0.025P,0.015～0.025S,0.4～0.6Cr,0.4～0.7Ni,0.15～0.25Mo,0.015～0.045Al,≤0.010 0N)的冶炼流程为60 t BOF-LF-VD-300 mm×360mm铸坯。分析了工艺改进前BOF终点残...齿轮钢8620RH(K)(/%:0.18～0.22C,0.17～0.26Si,0.70～0.90Mn,≤0.025P,0.015～0.025S,0.4～0.6Cr,0.4～0.7Ni,0.15～0.25Mo,0.015～0.045Al,≤0.010 0N)的冶炼流程为60 t BOF-LF-VD-300 mm×360mm铸坯。分析了工艺改进前BOF终点残余元素,出钢量,精炼合金调整量,VD增N方式和铸坯C偏析,得出BOF出钢量不稳定、中间包钢水过热度高、内控成分合格率低,铸坯C偏析指数高是导致末端淬火试验AHRC值4～5带宽符合率偏低的主要因素。通过稳定转炉装入量和出钢量,LF吹氮气增氮,空置红钢包加盖,控制中间包钢水过热度15～25℃,优化连铸电磁搅拌参数等工艺措施,使8620RH(K)钢末端淬火内控符合率由原<60%提高至82.93%。展开更多
文摘齿轮钢8620RH(K)(/%:0.18～0.22C,0.17～0.26Si,0.70～0.90Mn,≤0.025P,0.015～0.025S,0.4～0.6Cr,0.4～0.7Ni,0.15～0.25Mo,0.015～0.045Al,≤0.010 0N)的冶炼流程为60 t BOF-LF-VD-300 mm×360mm铸坯。分析了工艺改进前BOF终点残余元素,出钢量,精炼合金调整量,VD增N方式和铸坯C偏析,得出BOF出钢量不稳定、中间包钢水过热度高、内控成分合格率低,铸坯C偏析指数高是导致末端淬火试验AHRC值4～5带宽符合率偏低的主要因素。通过稳定转炉装入量和出钢量,LF吹氮气增氮,空置红钢包加盖,控制中间包钢水过热度15～25℃,优化连铸电磁搅拌参数等工艺措施,使8620RH(K)钢末端淬火内控符合率由原<60%提高至82.93%。