Slurry processing experiments were performed with AlSi7Mg0.6 to identify the globularization mechanisms.The melt sample water quenched slightly above the liquidus point is predominantly dendritic while that cooled int...Slurry processing experiments were performed with AlSi7Mg0.6 to identify the globularization mechanisms.The melt sample water quenched slightly above the liquidus point is predominantly dendritic while that cooled into the semi-solid temperature range internally via stirring the melt with a rotating cylindrical block of the alloy itself becomes fully globular.The globules are much smaller when internal cooling and stirring are employed longer to achieve higher solid fractions before casting.Coarse dendrite fragments of various sizes are revealed,in the case of stirring after an initial fraction of solid is first formed without the benefit of additional internal cooling.展开更多
The isothermal oxidation behavior of the second generation single crystal superalloy DD6 was studied at 1050 ℃ and 1100 ℃ in ambient atmosphere.Morphology of oxides was examined by SEM and their composition was anal...The isothermal oxidation behavior of the second generation single crystal superalloy DD6 was studied at 1050 ℃ and 1100 ℃ in ambient atmosphere.Morphology of oxides was examined by SEM and their composition was analyzed by XRD and EDS.The experimental results show that DD6 alloy obeys subparabolic rate law during oxidation of 100 h at 1050 ℃ and 1100 ℃.The oxide scale exposed at 1050 ℃ is made up of an outer NiO layer with a small amount of Al2O3 and an inner Al2O3 layer.The oxide scale exposed at 1100 ℃ is made up of an outer Al2O3 layer with a small amount of NiO,an intermediate layer,mainly composed of Cr2O3 and TaO2,and an inner Al2O3 layer.The γ＇-free layer was formed under the oxide scale at two temperatures.展开更多
基金the State Planning Organization of Turkey for the financial support
文摘Slurry processing experiments were performed with AlSi7Mg0.6 to identify the globularization mechanisms.The melt sample water quenched slightly above the liquidus point is predominantly dendritic while that cooled into the semi-solid temperature range internally via stirring the melt with a rotating cylindrical block of the alloy itself becomes fully globular.The globules are much smaller when internal cooling and stirring are employed longer to achieve higher solid fractions before casting.Coarse dendrite fragments of various sizes are revealed,in the case of stirring after an initial fraction of solid is first formed without the benefit of additional internal cooling.
文摘The isothermal oxidation behavior of the second generation single crystal superalloy DD6 was studied at 1050 ℃ and 1100 ℃ in ambient atmosphere.Morphology of oxides was examined by SEM and their composition was analyzed by XRD and EDS.The experimental results show that DD6 alloy obeys subparabolic rate law during oxidation of 100 h at 1050 ℃ and 1100 ℃.The oxide scale exposed at 1050 ℃ is made up of an outer NiO layer with a small amount of Al2O3 and an inner Al2O3 layer.The oxide scale exposed at 1100 ℃ is made up of an outer Al2O3 layer with a small amount of NiO,an intermediate layer,mainly composed of Cr2O3 and TaO2,and an inner Al2O3 layer.The γ＇-free layer was formed under the oxide scale at two temperatures.