In order to meet the forming demands for low plasticity materials and large height-diameter ratio parts, a new process of hydrodynamic deep drawing （HDD） with independent radial hydraulic pressure is proposed. To in...In order to meet the forming demands for low plasticity materials and large height-diameter ratio parts, a new process of hydrodynamic deep drawing （HDD） with independent radial hydraulic pressure is proposed. To investigate the effects of loading paths on the HDD with independent radial hydraulic pressure, the forming process of 5A06 aluminum alloy cylindrical cup with a hemispherical bottom was studied by numerical simulation. By employing the dynamic explicit analytical software ETA/Dynaform based on LS-DYNA3D, the effects of loading paths on the sheet-thickness distribution and surface quality were analyzed. The corresponding relations of the radial hydraulic pressure loading paths and the part＇s strain status on the forming limit diagram （FLD） were also discussed. The results indicated that a sound match between liquid chamber pressure and independent radial hydraulic pressure could restrain the serious thinning at the hemisphere bottom and that through adjusting radial hydraulic pressure could reduce the radial tensile strain and change the strain paths. Therefore, the drawing limit of the aluminum cylindrical cup with a hemispherical bottom could be increased significantly.展开更多
The plasma-MIG welding torch was developed.5A06 aluminum alloys with V-grooves were welded in a single pass in the plasma-MIG welding process and the joints were examined by X-ray diffractometry analysis and mechanica...The plasma-MIG welding torch was developed.5A06 aluminum alloys with V-grooves were welded in a single pass in the plasma-MIG welding process and the joints were examined by X-ray diffractometry analysis and mechanical tests.The orthogonal experimental design was used to study the influence of plasma-MIG welding parameters on the aluminum weld porosity.The mixed orthogonal matrix L16(4 4×2 3) and analysis of variance (ANOVA)technique were employed to optimize the welding parameters.The experimental results indicate that the effect of plasma gas flow rate is dominant,the secondary factors are MIG welding voltage,welding speed,wire feed rate and plasma current in turn.Confirmation experiments were conducted under optimum conditions and there was almost no porosity in the welded joints,thus good mechanical performance joints were obtained.展开更多
The formability of light-weight alloy, such as aluminum alloy, magnesium alloy, can be improved significantly when formed at elevated temperature. Superplastic forming (SPF) is a well-known manufacturing method to for...The formability of light-weight alloy, such as aluminum alloy, magnesium alloy, can be improved significantly when formed at elevated temperature. Superplastic forming (SPF) is a well-known manufacturing method to form complex part of these materials. In order to realize mass production of SPF in industry, forming at high strain rate should be realized. In this study, the mechanical properties of 5A06 sheet were tested by uniaxial tensile test at high strain rate and elevated temperatures up to 550 ℃. Free bulging test and forming of round cup were carried out to evaluate the formability of the 5A06 sheet. Results show that the total elongation of the 5A06 sheet began to increase rapidly after 200 ℃, and reached the maximum value at 450 ℃. At higher temperature, early brittle fracture occurred. In free bulging test, the bulging height remained almost constant about 27.0 mm, which means the formability of the sheet is not sensitive to forming temperature at elevated temperature. In the forming of round cup part, temperature has direct effect on the corner filling ability of the sheet, especially at temperature lower than 400 ℃.展开更多
Aluminum alloy tubes were prepared by tube spinning.The intergranular and electrochemical corrosion tests were used to investigate the intergranular corrosion behavior of the 5A06 aluminum alloy blank sample and the s...Aluminum alloy tubes were prepared by tube spinning.The intergranular and electrochemical corrosion tests were used to investigate the intergranular corrosion behavior of the 5A06 aluminum alloy blank sample and the spinning sample.Results showed that the intergranular corrosion resistance of the spinning sample was higher than that of the blank sample.In addition,the electrochemical corrosion resistance of the spinning sample was higher than that of the blank sample.The EDS maps indicated a uniform element distribution pattern of aluminum and magnesium.Moreover,the phase composition and lattice constant of the samples were obtained by XRD analysis.The differences in microstructure between the aluminum alloy subjected to the spinning process and the untreated aluminum alloy were determined by EBSD.The differences were mainly attributed to the complex interactions among grain size,dislocations and grain boundaries.展开更多
In order to overcome the limitation of hydro-rim deep drawing, a new process of hydrodynamic deep drawing （HDD） with independent radial hydraulic pressure was proposed. By employing the dynamic explicit analytical s...In order to overcome the limitation of hydro-rim deep drawing, a new process of hydrodynamic deep drawing （HDD） with independent radial hydraulic pressure was proposed. By employing the dynamic explicit analytical software ETA/DynaformS.5 which is based on LS-DYNA3D, the effects of independent radia! hydraulic pressure on the stress, strain and the sheet-thickness of aluminum-magnesium cylindrical cup with a hemispherical bottom were analyzed by numerical simulation. The feature of stress distribution is that there exists a stress-dividing circle in the flange, and the radius of dividing circle was determined by theoretical analysis and stimulation. The experimental results indicate that the reasonable match of independent radial hydraulic pressure and liquid chamber pressure can effectively reduce the thinning at the bottom of hemisphere, decrease the radial stress-strain, and improve the drawing limit of aiuminum-magnesium alloy cylindrical cup.展开更多
In order to avoid the occurrence of fracture at room temperature in reverse deep drawing of aluminum alloy plate, the warm reverse deep drawing method was proposed. The experiments were conducted at room temperature,...In order to avoid the occurrence of fracture at room temperature in reverse deep drawing of aluminum alloy plate, the warm reverse deep drawing method was proposed. The experiments were conducted at room temperature, 280 and 360 ℃ with a 4.5 mm thick 5A06 aluminum alloy plate. The effect of temperature, blank-holding force and gap on the fracture and wrinkle of the reverse deep drawing process was investigated. A fully coupled thermal-mechanical simulation was carried out to obtain the stress distribution through the commercial software of Abaqus/Explicit. The results show that the fracture is avoided at 280 ℃ since the bending-induced stress gradient in the transient area between the inside corner and the straight wall decreases from 505 MPa at RT to 72 MPa at 280 ° C. Although the fracture is avoided as the temperature increases, the wrinkle occurs at the outside die corner at temperature over 280 ° C, where the circumferential compressive stress becomes larger than that at the inside. As the temperature increases to 360 ℃, the fracture occurs due to the excessive softening, the tensile stress in the straight wall reaches rapidly to the tensile strength at the beginning of reverse deep drawing. When 1.5t （t=4.5 mm） blank holding gap is applied at 280 ℃, both the fracture and wrinkle can be avoided, and 420 mm deep cups are drawn successfully.展开更多
文摘In order to meet the forming demands for low plasticity materials and large height-diameter ratio parts, a new process of hydrodynamic deep drawing （HDD） with independent radial hydraulic pressure is proposed. To investigate the effects of loading paths on the HDD with independent radial hydraulic pressure, the forming process of 5A06 aluminum alloy cylindrical cup with a hemispherical bottom was studied by numerical simulation. By employing the dynamic explicit analytical software ETA/Dynaform based on LS-DYNA3D, the effects of loading paths on the sheet-thickness distribution and surface quality were analyzed. The corresponding relations of the radial hydraulic pressure loading paths and the part＇s strain status on the forming limit diagram （FLD） were also discussed. The results indicated that a sound match between liquid chamber pressure and independent radial hydraulic pressure could restrain the serious thinning at the hemisphere bottom and that through adjusting radial hydraulic pressure could reduce the radial tensile strain and change the strain paths. Therefore, the drawing limit of the aluminum cylindrical cup with a hemispherical bottom could be increased significantly.
文摘The plasma-MIG welding torch was developed.5A06 aluminum alloys with V-grooves were welded in a single pass in the plasma-MIG welding process and the joints were examined by X-ray diffractometry analysis and mechanical tests.The orthogonal experimental design was used to study the influence of plasma-MIG welding parameters on the aluminum weld porosity.The mixed orthogonal matrix L16(4 4×2 3) and analysis of variance (ANOVA)technique were employed to optimize the welding parameters.The experimental results indicate that the effect of plasma gas flow rate is dominant,the secondary factors are MIG welding voltage,welding speed,wire feed rate and plasma current in turn.Confirmation experiments were conducted under optimum conditions and there was almost no porosity in the welded joints,thus good mechanical performance joints were obtained.
基金National Nature Science Foundation of China (50805033)Natural Science Foundation of Heilongjiang Province of China (E200804)
文摘The formability of light-weight alloy, such as aluminum alloy, magnesium alloy, can be improved significantly when formed at elevated temperature. Superplastic forming (SPF) is a well-known manufacturing method to form complex part of these materials. In order to realize mass production of SPF in industry, forming at high strain rate should be realized. In this study, the mechanical properties of 5A06 sheet were tested by uniaxial tensile test at high strain rate and elevated temperatures up to 550 ℃. Free bulging test and forming of round cup were carried out to evaluate the formability of the 5A06 sheet. Results show that the total elongation of the 5A06 sheet began to increase rapidly after 200 ℃, and reached the maximum value at 450 ℃. At higher temperature, early brittle fracture occurred. In free bulging test, the bulging height remained almost constant about 27.0 mm, which means the formability of the sheet is not sensitive to forming temperature at elevated temperature. In the forming of round cup part, temperature has direct effect on the corner filling ability of the sheet, especially at temperature lower than 400 ℃.
基金Funded by the National Natural Science Foundation of China(No.51802189)the Shanghai Lingang Innovation Program(No.SH-LG-GK-2020-28)。
文摘Aluminum alloy tubes were prepared by tube spinning.The intergranular and electrochemical corrosion tests were used to investigate the intergranular corrosion behavior of the 5A06 aluminum alloy blank sample and the spinning sample.Results showed that the intergranular corrosion resistance of the spinning sample was higher than that of the blank sample.In addition,the electrochemical corrosion resistance of the spinning sample was higher than that of the blank sample.The EDS maps indicated a uniform element distribution pattern of aluminum and magnesium.Moreover,the phase composition and lattice constant of the samples were obtained by XRD analysis.The differences in microstructure between the aluminum alloy subjected to the spinning process and the untreated aluminum alloy were determined by EBSD.The differences were mainly attributed to the complex interactions among grain size,dislocations and grain boundaries.
基金Funded by the National Natural Science Foundation of China(Nos.50525516, 50875062)
文摘In order to overcome the limitation of hydro-rim deep drawing, a new process of hydrodynamic deep drawing （HDD） with independent radial hydraulic pressure was proposed. By employing the dynamic explicit analytical software ETA/DynaformS.5 which is based on LS-DYNA3D, the effects of independent radia! hydraulic pressure on the stress, strain and the sheet-thickness of aluminum-magnesium cylindrical cup with a hemispherical bottom were analyzed by numerical simulation. The feature of stress distribution is that there exists a stress-dividing circle in the flange, and the radius of dividing circle was determined by theoretical analysis and stimulation. The experimental results indicate that the reasonable match of independent radial hydraulic pressure and liquid chamber pressure can effectively reduce the thinning at the bottom of hemisphere, decrease the radial stress-strain, and improve the drawing limit of aiuminum-magnesium alloy cylindrical cup.
基金Project(IRT1229)supported by the Program for Chang-jiang Scholars and Innovative Research Team in University,ChinaProject(51375114)supported by the National Natural Science Foundation of China
文摘In order to avoid the occurrence of fracture at room temperature in reverse deep drawing of aluminum alloy plate, the warm reverse deep drawing method was proposed. The experiments were conducted at room temperature, 280 and 360 ℃ with a 4.5 mm thick 5A06 aluminum alloy plate. The effect of temperature, blank-holding force and gap on the fracture and wrinkle of the reverse deep drawing process was investigated. A fully coupled thermal-mechanical simulation was carried out to obtain the stress distribution through the commercial software of Abaqus/Explicit. The results show that the fracture is avoided at 280 ℃ since the bending-induced stress gradient in the transient area between the inside corner and the straight wall decreases from 505 MPa at RT to 72 MPa at 280 ° C. Although the fracture is avoided as the temperature increases, the wrinkle occurs at the outside die corner at temperature over 280 ° C, where the circumferential compressive stress becomes larger than that at the inside. As the temperature increases to 360 ℃, the fracture occurs due to the excessive softening, the tensile stress in the straight wall reaches rapidly to the tensile strength at the beginning of reverse deep drawing. When 1.5t （t=4.5 mm） blank holding gap is applied at 280 ℃, both the fracture and wrinkle can be avoided, and 420 mm deep cups are drawn successfully.