Nanocrystal of upconversion （UC） phosphor Ho^3＋, Tm^3＋ , and Yb^3＋ co-doped NaYF4 was prepared by the hydrothermal method in the presence of the complexing agent EDTA. Under 980 nm diode laser excitation, the imp...Nanocrystal of upconversion （UC） phosphor Ho^3＋, Tm^3＋ , and Yb^3＋ co-doped NaYF4 was prepared by the hydrothermal method in the presence of the complexing agent EDTA. Under 980 nm diode laser excitation, the impact of different concentrations of Ho^3＋ ion on the UC luminescence intensity was discussed. The law of luminescence intensity versus pump power shows that the 474 nm blue emission, 538 nm green emission, and 642 nm red emission are all due to the two-photon process, while the 450 nm blue emission is a three-photon process. The UC mechanism and processes were also analyzed. The sample was characterized by transmission electron microscopy （TEM） and X-ray diffraction （XRD）. The result shows that Ho^3＋ ,Tm^3＋ , and Yb^3＋ co-doped NaYF4 prepared by the hydrothermal method exhibits a hexagonal nanocrystal.展开更多
The core-shell 2,4,6,8,10,12-Hexanitro-2,4,6,8,10,12-hexaazaisowurtzitane/2,4,6-Trinitrotoluene(CL-20/TNT)composite was prepared by spray-drying method in which sensitive high energy explosive(CL-20)was coated with in...The core-shell 2,4,6,8,10,12-Hexanitro-2,4,6,8,10,12-hexaazaisowurtzitane/2,4,6-Trinitrotoluene(CL-20/TNT)composite was prepared by spray-drying method in which sensitive high energy explosive(CL-20)was coated with insensitive explosive(TNT).The structure and properties of different formulations of CL-20/TNT composite and CL-20/TNT mixture were characterized by scanning electron microscopy(SEM),Transmission electron microscopy(TEM),Laser particle size analyzer,X-ray photoelectron spectroscopy(XPS),X-ray diffraction(XRD),differential scanning calorimetry(DSC),impact sensitivity test and detonation performance.The results of SEM,TEM,XPS and XRD show that e-CL-20 particles are coated by TNT.When the ratio of CL-20/TNT is 75/25,core-shell structure is well formed,and thickness of the shell is about 20e30 nm.And the analysis of heat and impact show that with the increase of TNT content,the TNT coating on the core-shell composite material can not only catalyze the thermal decomposition of core material(CL-20),but also greatly reduce the impact sensitivity.Compared with the CL-20/TNT mixture(75/25)at the same ratio,the characteristic drop height of core-shell CL-20/TNT composite(75/25)increased by 47.6%and the TNT coating can accelerate the nuclear decomposition in the CL-20/TNT composites.Therefore,the preparation of the core-shell composites can be regarded as a unique means,by which the composites are characterized by controllable decomposition rate,high energy and excellent mechanical sensitivity and could be applied to propellants and other fields.展开更多
基金Project supported bythe Key Laboratory of Rare Earth Chemistry and Physics ,ChangchunInstitute of Applied Chemistry ,Chinese Academy of Sciences (R020202K)
文摘Nanocrystal of upconversion （UC） phosphor Ho^3＋, Tm^3＋ , and Yb^3＋ co-doped NaYF4 was prepared by the hydrothermal method in the presence of the complexing agent EDTA. Under 980 nm diode laser excitation, the impact of different concentrations of Ho^3＋ ion on the UC luminescence intensity was discussed. The law of luminescence intensity versus pump power shows that the 474 nm blue emission, 538 nm green emission, and 642 nm red emission are all due to the two-photon process, while the 450 nm blue emission is a three-photon process. The UC mechanism and processes were also analyzed. The sample was characterized by transmission electron microscopy （TEM） and X-ray diffraction （XRD）. The result shows that Ho^3＋ ,Tm^3＋ , and Yb^3＋ co-doped NaYF4 prepared by the hydrothermal method exhibits a hexagonal nanocrystal.
文摘The core-shell 2,4,6,8,10,12-Hexanitro-2,4,6,8,10,12-hexaazaisowurtzitane/2,4,6-Trinitrotoluene(CL-20/TNT)composite was prepared by spray-drying method in which sensitive high energy explosive(CL-20)was coated with insensitive explosive(TNT).The structure and properties of different formulations of CL-20/TNT composite and CL-20/TNT mixture were characterized by scanning electron microscopy(SEM),Transmission electron microscopy(TEM),Laser particle size analyzer,X-ray photoelectron spectroscopy(XPS),X-ray diffraction(XRD),differential scanning calorimetry(DSC),impact sensitivity test and detonation performance.The results of SEM,TEM,XPS and XRD show that e-CL-20 particles are coated by TNT.When the ratio of CL-20/TNT is 75/25,core-shell structure is well formed,and thickness of the shell is about 20e30 nm.And the analysis of heat and impact show that with the increase of TNT content,the TNT coating on the core-shell composite material can not only catalyze the thermal decomposition of core material(CL-20),but also greatly reduce the impact sensitivity.Compared with the CL-20/TNT mixture(75/25)at the same ratio,the characteristic drop height of core-shell CL-20/TNT composite(75/25)increased by 47.6%and the TNT coating can accelerate the nuclear decomposition in the CL-20/TNT composites.Therefore,the preparation of the core-shell composites can be regarded as a unique means,by which the composites are characterized by controllable decomposition rate,high energy and excellent mechanical sensitivity and could be applied to propellants and other fields.