The Ce conversion films on 2195A1-Li alloy without and with post-treatment were studied and the corrosion resistance was evaluated as well. The surface morphology was observed by scanning electron microscopy （SEM）, ...The Ce conversion films on 2195A1-Li alloy without and with post-treatment were studied and the corrosion resistance was evaluated as well. The surface morphology was observed by scanning electron microscopy （SEM）, and the chemical composition was characterized by X-ray photoelectron spectroscopy （XPS）. The corrosion behaviors of 2195A1-Li alloy and conversion coating were assessed by means of potentiodynamic polarization curves. The experimental results indicated that after post-treatment the surface quality was improved significantly. According to XPS, the conversion coating after post-treatment was mainly composed of CeO2, Ce203, Ce-OH and a little MoO3 and MOO2. The results of potentiodynamic polarization curves revealed that the conversion coating with post-treatment possessed better corrosion resistance than bare alloy and Ce conversion coating without post-treatment.展开更多
基金Teacher’s Research Foundation of Central South University(2013JSJJ001)National High Technology Research and Development Program of China(2013AA032401)
文摘The Ce conversion films on 2195A1-Li alloy without and with post-treatment were studied and the corrosion resistance was evaluated as well. The surface morphology was observed by scanning electron microscopy （SEM）, and the chemical composition was characterized by X-ray photoelectron spectroscopy （XPS）. The corrosion behaviors of 2195A1-Li alloy and conversion coating were assessed by means of potentiodynamic polarization curves. The experimental results indicated that after post-treatment the surface quality was improved significantly. According to XPS, the conversion coating after post-treatment was mainly composed of CeO2, Ce203, Ce-OH and a little MoO3 and MOO2. The results of potentiodynamic polarization curves revealed that the conversion coating with post-treatment possessed better corrosion resistance than bare alloy and Ce conversion coating without post-treatment.